Glaze of brunet ceramic and preparation method of glaze

A technology of glaze and ceramics, applied in the field of ceramics, can solve the problems of low quality rate of ceramic products, influence of product quality, increase of production cost, etc., achieve the effect of controlling white spots and improving the rate of excellence

Active Publication Date: 2016-02-17
GUANGDONG JIA MEI CERAMIC
View PDF3 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] For some dark ceramic products, defects such as white spots and pinholes often appear due to glazes in the early production process, which affects the quality of the entire product, and the excellent rate of ceramic products is low, which increases the production of enterprises. cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glaze of brunet ceramic and preparation method of glaze

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Embodiment one, the ratio of bottom glaze and transparent glaze is respectively 90% and 10%.

[0021] The bottom glaze is composed of the following raw materials in parts by weight: 3 parts of ultra-white zirconium silicate, 20 parts of ordinary potassium feldspar powder, 25 parts of albite feldspar, 4 parts of alumina, 9 parts of kaolin and 6 parts of calcined kaolin. The transparent glaze is composed of the following raw materials in parts by weight: 3 parts of calcined zinc oxide, 9 parts of barium carbonate, 30 parts of albite, 0 part of calcined alumina, 13 parts of calcite, 9 parts of calcite, 5 parts of quartz, and 9 parts of kaolin Composed of 12 parts of calcined kaolin.

[0022] Carry out the weighing ratio mixing of raw materials according to the above ratio.

Embodiment 2

[0024] The bottom glaze is composed of the following raw materials in parts by weight: 3 parts of ultra-white zirconium silicate, 20 parts of ordinary potassium feldspar powder, 25 parts of albite feldspar, 4 parts of alumina, 9 parts of kaolin and 6 parts of calcined kaolin. The transparent glaze is composed of the following raw materials in parts by weight: 5 parts of calcined zinc oxide, 7 parts of barium carbonate, 30 parts of potassium feldspar powder, 0.5 parts of calcined alumina, 12 parts of calcite, 10 parts of calcite, 5 parts of quartz, and 9 parts of kaolin Composed of 7 parts of calcined kaolin. The quartz is finely ground quartz after being screened with 325 meshes.

[0025] Carry out the weighing ratio mixing of raw materials according to the above ratio.

Embodiment 3

[0027] The bottom glaze is composed of the following raw materials in parts by weight: 3 parts of ultra-white zirconium silicate, 20 parts of ordinary potassium feldspar powder, 25 parts of albite feldspar, 4 parts of alumina, 9 parts of kaolin and 6 parts of calcined kaolin. The transparent glaze is composed of the following raw materials in parts by weight: 5 parts of burnt zinc oxide, 7 parts of barium carbonate, 30 parts of potassium feldspar powder, 2 parts of calcined alumina, 12 parts of burnt talc, 10 parts of calcite, 5 parts of quartz, and 9 parts of kaolin Composed of 14 parts of calcined kaolin. The quartz is finely ground quartz after being screened with 325 meshes.

[0028] Carry out the weighing ratio mixing of raw materials according to the above ratio.

[0029] In addition, the present invention also discloses a preparation method of a dark ceramic glaze, comprising the following steps:

[0030] 1) Weigh the raw materials according to the weight components o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses glaze of brunet ceramic. The glaze is prepared from, by weight, 88-92% of ground glaze and 8-12% of transparent glaze; the ground glaze is prepared from, by weight, 2-5 parts of super white zirconium silicate, 18-22 parts of feldspar powder, 23-27 parts of albite, 3-5 parts of aluminum oxide, 8-10 parts of kaolin and 5-7 parts of calcined kaolin; the transparent glaze is prepared from, by weight, 3-7 parts of burned zinc oxide, 6-10 parts of barium carbonate, 28-32 parts of feldspar powder or 28-32 parts of albite, 0-3 parts of calcined alumina, 11-14 parts of calcinedtalc, 8-12 parts of calcite, 4-6 parts of quartz, 8-10 parts of kaolin and 7-14 parts of calcined kaolin. By means of the method, a product is rich in texture design and pattern, good in texture and soft, vivid, stable in performance, free of corrosion and free of crack.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a glaze for dark ceramic products and a preparation method for the glaze. Background technique [0002] As ceramic products enter millions of households, ceramic glazes are indispensable decorative materials for ceramic products. The existing ceramic glazes can be roughly classified according to their categories and uses as follows: 1. Lead glaze and lead-free glaze; 2. Raw glaze and frit glaze; 3. Glaze for primary firing or secondary firing; 4. Glaze for ceramic tiles, tableware, sanitary ceramics and electric porcelain; 5. Dip glaze, spray glaze, pouring glaze according to the glaze method; Glaze and low temperature glaze; 7. High expansion glaze and low expansion glaze; 8. Firing atmosphere oxidation flame, neutral flame and reducing flame; 9. Color glaze and colorless glaze; 10. Transparent glaze and opacity glaze; 11. Gloss glaze, matt glaze, semi-matt glaze or pattern gl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/02C03C8/04
Inventor 黄春保马占领韩军刘肖黄裕富
Owner GUANGDONG JIA MEI CERAMIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com