Preparation method and system of niobium-aluminium alloy

A preparation system and aluminum alloy technology, which is applied in the field of non-ferrous alloys, can solve the problems of increasing preparation costs and achieve the effects of low production costs, accelerated diffusion, and reduced impurity content

Inactive Publication Date: 2016-03-09
GANZHOU NONFERROUS METALLURGICAL RES INST
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

This patented technology helps create pure metal alloys with fewer harmful substances from traditional methods like melting or casting processes without losing their quality. It also improves the efficiency at producing these materials while reducing costs associated therewith.

Problems solved by technology

This patented technical problem addressed in this patents relates to improving the properties of certain types of metals such as tantalum or zirconia during their production processes without causing them from separating out into different phases when they are mixed together due to differences between crystal structures caused by changes made over time (cold work).

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and system of niobium-aluminium alloy
  • Preparation method and system of niobium-aluminium alloy
  • Preparation method and system of niobium-aluminium alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] Such as figure 1 As shown, the preparation method of the niobium aluminum alloy of the present invention at least includes the following steps: mixing niobium pentoxide, aluminum and a small amount of slag remover to form a mixed material; melting the remaining aluminum to form aluminum liquid; The material is added into the aluminum liquid, so that it can generate niobium through the aluminothermic reduction reaction, and evenly distribute in the aluminum liquid, and react with excess aluminum to form a uniform niobium aluminum alloy.

[0029] Such as figure 2 As shown, according to an embodiment of the present invention, the niobium-aluminum alloy preparation system includes a ball mill pressing granulation device 1, a smelting device 2, a vacuum and / or an inert gas input device 3, a stirring device 4, a temperature control device 5, and a weight Proportioning device6.

[0030] In one embodiment of the present invention, the niobium-aluminum alloy comprises the fol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a niobium-aluminium alloy. The preparation method is characterized in that the preparation method comprises the following steps that niobium pentoxide is mixed with aluminum and a small quantity of fluxing agent and deslagging agent to form a mixed material; surplus aluminum is smelted to form molten aluminum; and the mixture is added to the molten aluminum, and niobium is produced through an aluminothermic reduction reaction, is uniformly distributed in the molten aluminum, and reacts with surplus aluminum to form the niobium-aluminium alloy which is uniform in component. According to the niobium-aluminium alloy prepared by the method, niobium is distributed uniformly, the segregation degree of niobium is low, aluminum ignition loss is little, and the alloy eutectic point temperature is low, and the components are stable.

Description

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Owner GANZHOU NONFERROUS METALLURGICAL RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap