Wear-resisting cable for ship and manufacturing method thereof

A technology for ships and cables, which is applied in the field of wear-resistant cables for ships and its manufacturing, can solve the problems of short service life, backward manufacturing technology, expensive manufacturing materials, etc., and achieve the effects of protecting the national environment, increasing economic benefits, and cheap prices

Inactive Publication Date: 2016-03-23
ANHUI TENGYUE ALUMINUM PLASTIC
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the relatively expensive manufacturing materials and backward manufacturing process of the existing ship cables, the market price of the ship cables is expensive and the service life is short, especially in terms of wear resistance, they are subject to seawater impact, erosion, sun weathering and friction with the surface of the ship. , many cables are quickly worn out and can no longer be used, and frequent replacement requires higher costs. Therefore, a low-cost, cheap, and more wear-resistant ship cable is urgently needed by the ship industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A wear-resistant rope for ships, characterized in that the rope is made of the following formula proportions by weight:

[0025] PP: 80%

[0026] PE: 15%

[0027] Oily materials: 1%

[0028] Plasticizer: 3%

[0029] Additives: 1%.

[0030] The PP and PE are produced by recycling and extracting plastic shells of waste motorcycles, airplanes, and household appliances, and waste tires of automobiles and motorcycles.

[0031] The oily materials mainly refer to acrylic copolymers.

[0032] The plasticizer is a polyester plasticizer.

[0033] The auxiliary agent is one or more of light stabilizers and antioxidants.

[0034] A method for manufacturing a wear-resistant cable for ships, which is characterized by the following steps:

[0035] According to the above parts by weight:

[0036] 1) Put the oily materials and additives into the mixer and mix at a speed of 1200 rpm to prepare the mixture for use;

[0037] 2) Through a single-screw extruder, using a quantitative feeding method, the PP and...

Embodiment 2

[0041] A wear-resistant rope for ships, characterized in that the rope is made of the following formula proportions by weight:

[0042] PP: 83%

[0043] PE: 12.5%

[0044] Oily materials: 2%

[0045] Plasticizer: 2%

[0046] Additives: 0.5%.

[0047] The PP and PE are produced by recycling and extracting plastic shells of waste motorcycles, airplanes, and household appliances, and waste tires of automobiles and motorcycles.

[0048] The oily materials mainly refer to acrylic copolymers.

[0049] The plasticizer is a polyester plasticizer.

[0050] The auxiliary agent is one or more of light stabilizers and antioxidants.

[0051] A method for manufacturing a wear-resistant cable for ships, which is characterized by the following steps:

[0052] According to the above parts by weight:

[0053] 1) Put the oily materials and additives into the mixer and mix at a speed of 1200 rpm to prepare the mixture for use;

[0054] 2) Through a single-screw extruder, using a quantitative feeding method, the PP...

Embodiment 3

[0058] A wear-resistant rope for ships, characterized in that the rope is made of the following formula proportions by weight:

[0059] PP: 85%

[0060] PE: 9.5%

[0061] Oily materials: 4%

[0062] Plasticizer: 1.4%

[0063] Additives: 0.1%.

[0064] The PP and PE are produced by recycling and extracting plastic shells of waste motorcycles, airplanes, and household appliances, and waste tires of automobiles and motorcycles.

[0065] The oily materials mainly refer to acrylic copolymers.

[0066] The plasticizer is a polyester plasticizer.

[0067] The auxiliary agent is one or more of light stabilizers and antioxidants.

[0068] A method for manufacturing a wear-resistant cable for ships, which is characterized by the following steps:

[0069] According to the above parts by weight:

[0070] 1) Put the oily materials and additives into the mixer and mix at a speed of 1200 rpm to prepare the mixture for use;

[0071] 2) Through a single-screw extruder, using a quantitative feeding method, the P...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a wear-resisting cable for a ship and a manufacturing method thereof, and relates to the field of ship equipment manufacturing. Plastic shells of waste motorcycles, waste planes and waste household appliances, and waste tires of automobiles and motorcycles are used as main raw materials, and mixed with other auxiliary material ingredients. The wear-resisting cable is prepared from 80-85% of PP, 10-15% of PE, 1-5% of an oily material, 1-3% of plasticizer and 0.1-1% of an auxiliary. By means of the unique process, the high-strength and wear-resistant ship cable is manufactured, the service life is 2-3 times that of a common ship cable, as the waste plastic and rubber products are adopted as the raw materials of the cable mostly, the raw materials are low in price and easy to obtain, the price of finished products is low, the wear-resisting cable saves energy and is environmentally friendly, waste and rubbish are recycled, the policy of environmental protection of the nation is met, economic benefits are increased, national environment is protected, and the effect of turning waste into wealth is achieved.

Description

Technical field: [0001] The invention relates to the field of ship equipment manufacturing, in particular to a wear-resistant cable for ships and a manufacturing method thereof. Background technique: [0002] Ship ropes are multi-strand ropes used to tie ships, which require tensile, impact, abrasion resistance, flexibility, lightness and softness. Existing ship ropes are expensive in manufacturing materials and backward in manufacturing processes, resulting in expensive ship ropes in the market and short service life, especially in terms of wear resistance, such as seawater impact, erosion, sun weathering, and friction with the ship’s surface Many cables are quickly worn out and cannot be used continuously. Frequent replacement requires higher costs. Therefore, a low-cost, inexpensive, and more wear-resistant ship cable is urgently needed by the shipbuilding industry. Summary of the invention: [0003] In order to solve the above problems, the present invention provides a wear-r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D07B1/02D01D5/08D01F1/10D01F8/06
CPCD07B1/02D01D5/08D01F1/10D01F8/06D07B2205/2003D07B2501/2061
Inventor 马学东
Owner ANHUI TENGYUE ALUMINUM PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products