High heat load tolerant frictional material

A friction material and high heat technology, applied in the field of friction materials, can solve the problem of high thermal load resistance, and achieve the effects of stable friction coefficient, low wear rate, and excellent thermal recession resistance.

Inactive Publication Date: 2016-05-25
FOSHAN WASEDA INFORMATION CONSULTATION CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a friction material that can withstand high heat loads, aiming to solve the problem that the current friction plate materials are not resistant to high heat loads

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The high thermal load resistant friction material is composed of the following components in parts by weight:

[0035] 20 parts of resin;

[0036] 24 parts of composite fiber;

[0037] 15 parts of polyimide;

[0038] 10 parts of barium sulfate;

[0039] 1 part wollastonite;

[0040] Aluminum oxide 1 part.

[0041] Put the weighed above-mentioned materials into the mixer, stir them thoroughly, and put them into the mold for pressing after uniform mixing. Preheat the die to a temperature range of 200°C before being ready for pressing. The pressing process conditions are: pressing temperature 200°C, pressing pressure 50Mpa, degassing once after 10s, degassing twice depending on the situation, heat preservation and pressure holding time 60s / mm. The pressed product is put into the oven first, the temperature is raised to 150°C, and kept for 2 hours; the temperature is raised to 180°C, and kept for 1 hour; the temperature is raised to 200°C, and kept for 12 hours. Cool...

Embodiment 2

[0044] The high thermal load resistant friction material is composed of the following components in parts by weight:

[0045] 30 parts of resin;

[0046] 30 parts of composite fiber;

[0047] 5 parts of polyimide;

[0048] 15 parts of barium sulfate;

[0049] 1 part wollastonite;

[0050] Aluminum oxide 2 parts.

[0051] Put the weighed above-mentioned materials into the mixer, stir them thoroughly, and put them into the mold for pressing after uniform mixing. Preheat the die to a temperature range of 200°C before being ready for pressing. The pressing process conditions are: pressing temperature 200°C, pressing pressure 50Mpa, degassing once after 10s, degassing twice depending on the situation, heat preservation and pressure holding time 60s / mm. The pressed product is put into the oven first, the temperature is raised to 150°C, and kept for 2 hours; the temperature is raised to 180°C, and kept for 1 hour; the temperature is raised to 200°C, and kept for 12 hours. Cool...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
friction coefficientaaaaaaaaaa
friction coefficientaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high heat load tolerant frictional material. The frictional material is prepared from the following components in parts by weight: 15-35 parts of resin, 15-30 parts of composite fibers, 5-20 parts of polyimide, 5-15 parts of barium sulfate, 1-2 parts of wollastonite and 1-2 parts of aluminum oxide. The frictional material can bear a high heat load and is stable in frictional coefficient in a high-temperature environment and relatively low in wear rate, thereby having excellent heat attenuation resistance.

Description

technical field [0001] The invention relates to the field of special materials, in particular to a friction material withstanding high heat load. Background technique [0002] People have higher and higher requirements for the performance of friction materials used in brakes and clutches such as disc brakes and drum brakes. Existing friction materials generally have good friction performance at room temperature, but in high temperature environments Or under continuous working conditions, the coefficient of friction cannot be kept constant, which will cause problems such as slipping. [0003] Therefore, prior art also needs further development and improvement. Contents of the invention [0004] The purpose of the present invention is to provide a high thermal load-resistant friction material, aiming to solve the problem that the current friction plate materials are not resistant to high thermal load. [0005] Technical scheme of the present invention is as follows: [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09K3/14
CPCC09K3/14
Inventor 林慈生
Owner FOSHAN WASEDA INFORMATION CONSULTATION CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap