Aluminum alloy fishing barrel

A technology of aluminum alloy and salvage barrel, which is applied in ship salvage, ship, transportation and packaging, etc. It can solve problems such as stress corrosion and achieve good stress corrosion resistance, high hardness and smooth surface

Inactive Publication Date: 2016-06-01
QINGDAO YUANZHILIN AGRI SCI & TECH DEV
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to reduce the weight of the salvage barrel, the barrel body of the salvage barrel can be made of aluminum alloy, but the barrel body is often used for ups and downs on the sea surface, and is often located at the seawater-air interface, which is prone to stress corrosion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum alloy fishing barrel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The weight percentages of the components in the aluminum alloy in this example are as follows: Si: 0.40%, Mg: 0.64%, Cu: 0.02%, Fe: 0.23%, Sr: 0.03%, La: 0.14%, Nd: 0.18%, Zn : 0.03%, Ti: 0.05%, and the rest is Al.

[0016] The above components are used to prepare aluminum alloy profile products. The specific preparation method is: after mixing the components evenly, they are homogenized in the aluminum rod furnace to improve the uniformity of the overall performance, so that the material has both appropriate hardness and toughness. Then it is cooled by air, and the ingot is heated at 450-500°C, and then sent to the extruder for extrusion. The temperature of the extrusion barrel is 400°C±10°C, and the extrusion speed is 3-6m / min. After mist quenching, after cutting, cooling bed cooling, stretching and straightening, artificial aging is carried out. The holding temperature is 250°C±10°C, and the time is 180min, to obtain the finished aluminum alloy. After testing, the h...

Embodiment 2

[0018] The weight percentages of the components in the aluminum alloy in this example are as follows: Si: 0.44%, Mg: 0.66%, Cu: 0.02%, Fe: 0.25%, Sr: 0.02%, La: 0.14%, Nd: 0.18%, Zn : 0.05%, Ti: 0.02%, and the rest is Al.

[0019] The above components are used to prepare aluminum alloy profile products. The specific preparation method is: after mixing the components evenly, they are homogenized in the aluminum rod furnace to improve the uniformity of the overall performance, so that the material has both appropriate hardness and toughness. Then it is cooled by air, and the ingot is heated at 450-500°C, and then sent to the extruder for extrusion. The temperature of the extrusion barrel is 400°C±10°C, and the extrusion speed is 3-6m / min. After mist quenching, after cutting, cooling bed cooling, stretching and straightening, artificial aging is carried out. The holding temperature is 250°C±10°C, and the time is 180min, to obtain the finished aluminum alloy. After testing, the h...

Embodiment 3

[0021] The weight percentages of the components in the aluminum alloy in this example are as follows: Si: 0.42%, Mg: 0.65%, Cu: 0.02%, Fe: 0.24%, Sr: 0.03%, La: 0.14%, Nd: 0.18%, Zn : 0.05%, Ti: 0.04%, and the rest is Al.

[0022] The above components are used to prepare aluminum alloy profile products. The specific preparation method is: after mixing the components evenly, they are homogenized in the aluminum rod furnace to improve the uniformity of the overall performance, so that the material has both appropriate hardness and toughness. Then it is cooled by air, and the ingot is heated at 450-500°C, and then sent to the extruder for extrusion. The temperature of the extrusion barrel is 400°C±10°C, and the extrusion speed is 3-6m / min. After mist quenching, after cutting, cooling bed cooling, stretching and straightening, artificial aging is carried out. The holding temperature is 250°C±10°C, and the time is 180min, to obtain the finished aluminum alloy. After testing, the h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an aluminum alloy fishing barrel. The aluminum alloy fishing barrel comprises a barrel body and a lifting handle arranged at the upper part of the barrel body, wherein the barrel body is made of aluminum alloy; the aluminum alloy is prepared from the following components in percentage by weight: 0.40 to 0.44 percent of Si, 0.64 to 0.66 percent of Mg, 0.02 percent of Cu, 0.23 to 0.25 percent of Fe, 0.02 to 0.03 percent of Sr, 0.14 percent of La, 0.18 percent of Nd, 0.03 to 0.05 percent of Zn, 0.02 to 0.05 percent of Ti and the balance being Al. The aluminum alloy fishing barrel has the advantages of smooth surface, wider hardness range and good stress corrosion resistance.

Description

technical field [0001] The invention relates to the field of material engineering, in particular to an aluminum alloy salvage barrel. Background technique [0002] Aluminum alloy has the advantages of light weight and easy availability of raw materials, and has been gradually used in marine operation equipment. Although aluminum alloys used in marine operation equipment have certain corrosion resistance, in the process of measuring the corrosion resistance of aluminum alloys, the aluminum alloys are often completely submerged in seawater as a prerequisite or evaluated under salt spray conditions. In fact, the aluminum alloy of marine operation equipment is often on the seawater-air interface, and the corrosion at this two-phase interface is more serious than that completely submerged in seawater. At present, few aluminum alloys can cope with this situation. In addition, aluminum alloys for marine operation equipment are often subjected to various stress loads, so stress cor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/08C22F1/047B63C7/04
CPCC22C21/08B63C7/04C22F1/047
Inventor 刘书元
Owner QINGDAO YUANZHILIN AGRI SCI & TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap