A kind of pure cotton label tape and its manufacturing method

A production method and technology of trademark tape, which are applied in the directions of textile, fabric, fiber type, etc., can solve the problems of improving the process of trademark tape, and achieve the effects of strong adhesion, not easy to fall off, and improved effect.

Active Publication Date: 2018-07-06
湖州倍亨纺织有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Our company discloses a manufacturing method of an environmentally friendly non-scattering printed trademark tape in CN102031701A, but the process of the trademark tape needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of pure cotton label tape and its manufacturing method
  • A kind of pure cotton label tape and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] Such as figure 1 and figure 2 Shown, a kind of manufacture method of pure cotton trademark band, comprises the following steps successively:

[0061] (1) Base fabric pre-treatment: The base fabric layer is made of polyester warp and weft yarns, with a warp density of 20 threads / cm and a weft density of 20 threads / cm. Pass the base fabric layer through the cold pad-batch working fluid at 45m / min at 25°C to make the excess rate 100%-120%. The composition of cold pad batch working fluid is: NaOH 40 g / L, H 2o 2 10g / L, water glass 10g / L, refining agent 20g / L, penetrant 5g / L. After the base cloth is cold-rolled, at 60°C, the composition is: NaOH 30g / L, refining agent 5g / L, NaOH 2 SO 3 1 g / L deboiled one-bath working solution. After the first two steps are completed, the base cloth is washed in a water tank at 98°C until the pH is neutral, and the pretreatment is completed.

[0062] (2) Pre-calendering treatment: In order to better complete the coating finishing, pr...

Embodiment 2

[0071] Such as figure 1 and figure 2 Shown, a kind of manufacture method of pure cotton trademark band, comprises the following steps successively:

[0072] (1) Base fabric pre-treatment: The base fabric layer is made of polyester warp and weft yarns, the warp and weft counts are 32 yarns, the warp yarn density is 25 yarns / cm, and the weft yarn density is 25 yarns / cm . Pass the base fabric layer through the cold pad-batch working fluid at 45m / min at 25°C to make the excess rate 100%-120%. The composition of cold pad batch working fluid is: NaOH 45 g / L, H 2 o 2 11 g / L, water glass 10g / L, refining agent 25 g / L, penetrant 7 g / L. After the base cloth is cold-rolled, at 60°C, the composition is: NaOH 35g / L, refining agent 7g / L, NaOH 2 SO 3 3g / L deboiled one-bath working solution. After the first two steps are completed, the base cloth is washed in a water tank at 98°C until the pH is neutral, and the pretreatment is completed.

[0073] (2) Pre-calendering treatment: In ...

Embodiment 3

[0082] Such as figure 1 and figure 2 Shown, a kind of manufacture method of pure cotton trademark band, comprises the following steps successively:

[0083] (1) Base fabric pretreatment: The base fabric layer is made of polyester warp and weft yarns, the warp and weft counts are 32 yarns, the warp yarn density is 25 yarns / cm, and the weft yarn density is 30 yarns / cm . Pass the base fabric layer through the cold pad-batch working fluid at 45m / min at 25°C to make the excess rate 100%-120%. The composition of cold pad batch working fluid is: NaOH 50 g / L, H 2 o 2 12 g / L, water glass 12g / L, refining agent 30 g / L, penetrant 10 g / L. After the base cloth is cold-rolled, at 60°C, the composition is: NaOH 40g / L, refining agent 10g / L, NaOH 2 SO 3 5g / L deboiled one-bath working solution. After the first two steps are completed, the base cloth is washed in a water tank at 98°C until the pH is neutral, and the pretreatment is completed.

[0084] (2) Pre-calendering treatment: In...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a trademark tape and a manufacturing method thereof, in particular to a pure cotton trademark tape and a manufacturing method thereof. It includes a base cloth layer and a paint layer coated on the upper and lower sides of the base cloth layer, the base cloth layer is flat-woven from pure cotton warp yarns and weft yarns, and the paint layer is a coating containing oily polyurethane. The production method includes: (1) Pretreatment of the base fabric: the pretreatment includes the base fabric layer passing through the cold pad-batch working fluid and deboiling one bath of the working fluid in turn, and the base fabric layer is heated at 25°C at a rate of 45m / min Immerse the cold pad-batch working solution at the speed of the vehicle, and the base cloth layer is deboiled through the one-bath working solution at 60-70°C; (2) Pre-calendering treatment: After the pre-treatment of the base cloth layer, at room temperature, under pressure 6MPa, pre-calendering treatment at a vehicle speed of 18-20m / min; (3) Coating treatment: coating the upper and lower sides of the pre-calendered base fabric layer with a coating layer, the coating layer is a coating containing oily polyurethane ; (4) Slitting treatment: the base cloth layer after coating treatment is cut into different specifications of trademark tapes. The pure cotton label tape of the invention has the characteristics of being able to be cold-cut without fraying and being resistant to stone washing.

Description

technical field [0001] The invention relates to a trademark tape and a manufacturing method thereof, in particular to a pure cotton trademark tape and a manufacturing method thereof. Background technique [0002] As one of the necessities of people's life, clothing is inseparable from the relationship between people. With the improvement of people's living standards, consumers' requirements for clothing have not only stopped at the requirements of clothing style and beauty, but also the safety and wearing of clothing. Comfort has also gradually gained widespread attention. As a very important auxiliary material, the trademark belt is an indispensable part of clothing, so people have also put forward new requirements for the trademark belt. According to incomplete statistics, most of the trademark belts on the market are mainly synthetic fibers, while pure cotton trademark belts only account for less than 10% of the market, but pure cotton trademark belts are woven from pure...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/564D06M11/38D06M11/50D06M11/79D06M11/54D03D15/00D06N3/14D06C15/00D06M101/06D06M101/32D03D15/217
CPCD03D15/00D06C15/00D06M11/38D06M11/50D06M11/54D06M11/79D06M15/564D06N3/14D06M2101/06D06M2101/32
Inventor 李红艳吴耀东
Owner 湖州倍亨纺织有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com