Metal part shot blasting counterforce pad

A technology for metal parts and metal fixing, applied in the field of metal parts processing, to achieve the effects of reducing energy consumption, long service life and simple structure

Inactive Publication Date: 2016-06-29
刁丽媚
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The object of the present invention is to provide a metal piece shot blasting reaction pad, which solves the problem of completing the front and back side shot blasting of the metal piece at one time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal part shot blasting counterforce pad
  • Metal part shot blasting counterforce pad
  • Metal part shot blasting counterforce pad

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Example 1, such as figure 1 As shown, a metal shot blasting reaction pad is characterized in that: the shot blasting reaction pad is composed of an outer layer, a middle layer, and a bottom layer, and the combined shape is a circle, rectangle, diamond, or trapezoid. The outer layer is made of a mixture of elastic colloids; it bounces high-speed shot blasting to the back of the metal part. The middle layer is made up of the outer metal fixing plate 1, the inner metal fixing plate 3 and the metal fixing on the outer layer. The damping spring 2 between the plate and the inner metal fixed plate, the bottom layer is set on the fixed object,

[0020] The outer layer is composed of the following raw materials in weight percentage:

[0021] Nitrile rubber 290740-50, 4-polybutadiene rubber 10-15, graphite 20-30, PVC resin 10-15, di-tert-butylperoxycumene 0.5-1, aluminum dihydrogen phosphate 5-6 , Tire waste powder 15-20, iron tailings powder 5-10, antioxidant 8-12, rhine wax 2-3, pe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a metal part shot blasting counterforce pad. The metal part shot blasting counterforce pad is characterized by being composed of an outer layer, a middle layer and a bottom layer, wherein the outer layer is used for enabling high-speed shots to bounce back to the back side of a metal part, the middle layer is composed of an outer-layer metal fixing plate, an inner-layer metal fixing plate and damping springs arranged between the outer-layer metal fixing plate and the inner-layer metal fixing plate, and the bottom layer is arranged on a fixture. The metal part shot blasting counterforce pad has the advantages of being simple in structure, good in elasticity, long in service life and especially suitable for shot blasting operation of automobile hubs; shot blasting operation can be completed at a time, so that energy consumption is reduced, and production efficiency is improved.

Description

Technical field [0001] The invention relates to the field of metal parts processing, in particular to a metal part shot blasting reaction pad. Background technique [0002] At present, in the process of shot blasting of metal parts, especially a series of large parts such as automobile wheels, in the process of water shot blasting, because the shot blasting space is all front shot blasting, the back side of the shot blasting part cannot be shot blasting. Therefore, the workpiece needs to be turned over and shot blasting again. This wastes time, processes, and resources. Summary of the invention [0003] The purpose of the present invention is to provide a metal part shot blasting reaction pad, which solves the problem of completing the front and back shot blasting of the metal part at one time. [0004] The technical solution adopted by the present invention to solve its technical problem is: a metal shot blasting reaction pad, characterized in that: the shot blasting reaction pad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B15/06B32B15/09B32B7/12B32B3/18B32B25/16C08L9/02C08L9/00C08L27/06C08L19/00C08L91/06C08K13/02C08K3/04C08K5/14C08K3/32C08K3/36
CPCB32B3/18B32B7/12B32B15/06B32B15/09B32B25/16B32B2307/51C08K2201/014C08L9/02C08L2205/02C08L2205/025C08L2205/035C08L9/00C08L27/06C08L19/003C08L91/06C08K13/02C08K3/04C08K5/14C08K2003/327C08K3/36
Inventor 刘超
Owner 刁丽媚