A kind of method of nano cobalt interlayer solid phase diffusion bonding cemented carbide

A cemented carbide, diffusion joining technology, applied in welding equipment, metal processing equipment, non-electric welding equipment, etc., to achieve the effect of increasing flexibility and improving mechanical properties

Active Publication Date: 2017-10-17
HARBIN INST OF TECH AT WEIHAI
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There is no relevant report in China on the solid-state diffusion connection of cemented carbide itself with a nano-scale interlayer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment 1: a kind of method that nanometer Co interlayer solid phase diffusion connects cemented carbide, it comprises the following steps:

[0022] (1) Wire-cut the cemented carbide YG8 to obtain (10mm×10mm×5mm) cemented carbide YG8 samples to be connected;

[0023] (2) Polish the surface to be welded of the cemented carbide YG8 sample to be joined obtained in step (1) with sandpaper, and then put it into acetone solution for ultrasonic cleaning for 15 minutes;

[0024] (3) Mix nano-Co into a paste with absolute ethanol, apply it on the surface of the cemented carbide to be welded, and assemble it into a hard alloy / nano-Co / hard alloy assembly, wherein the particle size of the nano-Co powder is 20nm , coating thickness is 50μm;

[0025] (4) Place the assembly obtained in step (3) in a vacuum heating furnace and apply a pressure of 10 MPa. When the vacuum degree of the vacuum heating furnace reaches 2.0×10 -3 Pa, start heating, control the heating rate in the furnac...

Embodiment 2

[0027] Embodiment 2: The difference between this embodiment and the specific embodiment 1 is that: the selected cemented carbide is YG4C, and the particle size of nano-Co in step (3) is 40nm. Others are identical with specific embodiment 1.

Embodiment 3

[0028] Embodiment 3: The difference between this embodiment and the specific embodiment 1 or 2 is that: the selected cemented carbide is YW1, and the particle size of nano-Co in step (3) is 50nm~100nm. Others are identical with specific embodiment 1 or 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
shear strengthaaaaaaaaaa
shear strengthaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for bonding hard alloy by solid-phase diffusion of a nano-Co intermediate layer. The surface of the hard alloy sample to be welded is polished and polished with sandpaper, and ultrasonically cleaned in acetone solution; the nano-Co is mixed with absolute ethanol to form a paste. Shape, coated on the surface of cemented carbide to be welded, assembled into cemented carbide / nano-Co / hard alloy assembly; place the assembly in a vacuum heating furnace, apply a pressure of 10MPa~20MPa, when vacuum heating When the vacuum degree of the furnace reaches (1.5~2.0)×10-3Pa, start heating, control the heating rate in the furnace to 10℃ / min~20℃ / min, raise the temperature to 1100℃~1300℃, then keep it warm for 20min~40min, and then Control the cooling rate at 5°C / min~10°C / min, cool to 400°C, and then cool with the furnace. The invention has the advantages of simple process, low cost, simple operation and high efficiency, and can realize reliable connection of cemented carbide.

Description

technical field [0001] The invention relates to a solid-phase diffusion bonding method of hard alloy cutters, in particular to a method for solid-phase diffusion bonding of hard alloys with a nano-cobalt intermediate layer. Background technique [0002] We know that cemented carbide tools are made of tungsten-cobalt materials, which are composed of refractory metal carbides and bonding metals using powder metallurgy. The presence of metal carbides ensures that cemented carbides have high hardness and durability. abrasiveness, while the binder phase endows the alloy with a certain strength and toughness, making it have good wear resistance, strength and impact toughness, which makes cemented carbide widely used in cutting tools, molds, geological mining tools and wear-resistant parts etc. [0003] Cemented carbide has a variety of grades according to its composition, such as YG8, YG4C, YW1, YW2, GE1, YT30 and so on. Cemented carbide has high hardness and high brittleness, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K20/00B23K20/24B23K20/227
CPCB23K20/001B23K20/227B23K20/24
Inventor 宋晓国赵一璇付伟刘多韩林峰冯吉才
Owner HARBIN INST OF TECH AT WEIHAI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com