Semi-high-speed steel

A semi-high-speed steel, weight percentage technology, applied in the field of semi-high-speed steel, can solve the problems of low sharpness, poor sharpening performance, etc., and achieve the effect of improving the finish, low cost, and high secondary hardening and tempering hardness

Inactive Publication Date: 2016-07-06
CHONGQING LINGYUN TOOLS CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the deficiencies of low sharpness and poor sharpening performance of high-speed steel inlaid paper cutting blades in the prior art, and provide a semi-high-speed steel blade steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The present invention will be further described below in conjunction with embodiment:

[0020] A semi-high-speed steel composed of the following chemical elements in weight percentage: C: 0.56-0.65%, Si: 0.40-0.60%, Mn: 0.25-0.40%, Cr: 6.0-6.8%, W: 1.6-2.5% %, Mo: 4.2-5.2%, V: 0.7-0.9%, Nb: 0.1-0.2%, Co0.3-0.4%, S≤0.02%, P≤0.025%, and the rest is Fe.

[0021] Further, it is composed of the following chemical elements in weight percentage: C: 0.58-0.62%, Si: 0.48-0.52%, Mn: 0.28-0.38%, Cr: 6.12-6.60%, W: 1.82-2.28%, Mo: 4.45~4.94%, V: 0.76~0.81%, Nb: 0.13~0.16%, Co or Ni: 0.32~0.38%, S≤0.02%, P≤0.025%, and the rest is Fe.

[0022] The preparation steps of a semi-high-speed steel copper brazing inlaid steel paper cutting blade are as follows:

[0023] (1) Production of semi-high-speed steel blade steel: use induction furnace or induction furnace to produce semi-high-speed steel blade steel through electroslag remelting. The semi-high-speed steel blade steel is composed ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses semi-high-speed steel. The semi-high-speed steel is composed of, by weight, 0.56%-0.65% of C, 0.40%-0.60% of Si, 0.25%-0.40% of Mn, 6.0%-6.8% of Cr, 1.6%-2.5% of W, 4.2%-5.2% of Mo, 0.7%-0.9% of V, 0.1%-0.2% of Nb, 0.3%-0.4% of Co, 0-0.02% of S, 0-0.025% of P, and the balance Fe. The strength of a paper cutting blade made from the semi-high-speed steel is identical with that of an original high-speed steel copper brazing steel plated paper cutting blade, but the paper cutting blade made from the semi-high-speed steel is higher in sharpness and easy to sharpen, and the material cost and process cost are reduced.

Description

technical field [0001] The invention relates to the technical field of mechanical blades, more specifically, to a semi-high-speed steel. Background technique [0002] The use performance of the paper cutting blade should not only have high sharpness and wear resistance, but also have good impact resistance and certain thermal hardness. [0003] It is very important to maintain the sharpness and sharpness of the cutting edge when the paper cutting blade is cutting. The carbides in the mouth are easy to fall off, which will not only reduce the sharpness, but also easily cause chipping during shearing. In recent years, we have researched, investigated, analyzed and demonstrated that if a suitable semi-high-speed steel blade steel is used, the number of carbides in the blade steel is reduced to between 3% and 8%, and the hardness of the matrix is ​​quenched and tempered while maintaining the level of high-speed steel, it will It is beneficial to improve the sharpness, durabili...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/30
Inventor 喻富春
Owner CHONGQING LINGYUN TOOLS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com