Wear-resistant hollow plate and production method thereof

A plate and hollow technology is applied in the field of wear-resistant hollow plates and their preparation, which can solve the problems of lack of wear resistance, and achieve the effects of good wear resistance, simple process and low cost.

Inactive Publication Date: 2016-08-24
SUZHOU DINGLI PACKAGING
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Also, the packaging does not have the necessary abrasion resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wear-resistant hollow plate and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A wear-resistant hollow plate, which is composed of the following components in proportion by weight: 18 parts of polycaprolactone, 18 parts of polyethylene, 9 parts of polypropylene, 8 parts of acrylic resin, 18 parts of dialdehyde starch, silicon dioxide 7 parts, glass fiber 9 parts, glycerin 9 parts, sodium chloride 7 parts, sodium hydroxide 3 parts, isopropanol 7 parts, water 19 parts.

[0021] A method for preparing a wear-resistant hollow plate, comprising the following steps:

[0022] (1) Add dialdehyde starch, silicon dioxide, glass fiber, and sodium hydroxide into water, and stir evenly at a temperature of 55°C and a pH value of 8.7 to make a paste; add the paste mixture into the autoclave , reacted for 35 minutes under the condition of 3.2MPa;

[0023] (2) Add polycaprolactone, polyethylene, polypropylene, and acrylic resin to isopropanol, place in a high-pressure reactor, and react under sealed conditions at 278°C for 30 minutes;

[0024] (3) Dissolve glyce...

Embodiment 2

[0027] A wear-resistant hollow plate, which is composed of the following components in proportion by weight: 33 parts of polycaprolactone, 27 parts of polyethylene, 16 parts of polypropylene, 13 parts of acrylic resin, 28 parts of dialdehyde starch, silicon dioxide 17 parts, glass fiber 19 parts, glycerin 15 parts, sodium chloride 14 parts, sodium hydroxide 8 parts, isopropanol 22 parts, water 35 parts.

[0028] A method for preparing a wear-resistant hollow plate, comprising the following steps:

[0029] (1) Add dialdehyde starch, silicon dioxide, glass fiber, and sodium hydroxide into water, and stir evenly at a temperature of 68°C and a pH value of 10.8 to make a paste; add the paste mixture into a high-pressure reactor , reacted for 44 minutes under the condition of 4.2MPa;

[0030] (2) Add polycaprolactone, polyethylene, polypropylene, and acrylic resin to isopropanol, place in a high-pressure reactor, and react at 368°C for 54 minutes under sealed conditions;

[0031] ...

Embodiment 3

[0034] A wear-resistant hollow plate, which is composed of the following components in proportion by weight: 38 parts of polycaprolactone, 32 parts of polyethylene, 22 parts of polypropylene, 17 parts of acrylic resin, 34 parts of dialdehyde starch, silicon dioxide 23 parts, glass fiber 24 parts, glycerin 21 parts, sodium chloride 18 parts, sodium hydroxide 11 parts, isopropanol 25 parts, water 39 parts.

[0035] A method for preparing a wear-resistant hollow plate, comprising the following steps:

[0036] (1) Add dialdehyde starch, silicon dioxide, glass fiber, and sodium hydroxide into water, and stir evenly at a temperature of 85°C and a pH value of 11.3 to make a paste; add the paste mixture into a high-pressure reactor , reacted for 50 minutes under the condition of 4.8MPa;

[0037] (2) Add polycaprolactone, polyethylene, polypropylene, and acrylic resin to isopropanol, place in a high-pressure reactor, and react under sealed conditions at 395°C for 65 minutes;

[0038]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a wear-resistant hollow plate and a production method thereof. The wear-resistant hollow plate is made from the following components according to parts by weight: 18-38 parts of polycaprolactone, 18-32 parts of polyethylene, 9-22 parts of polypropylene, 8-17 parts of acrylic resin, 18-34 parts of dialdehyde starch, 7-23 parts of silicon dioxide, 9-24 parts of glass fiber, 9-21 parts of glycerol, 7-18 parts of sodium chloride, 3-11 parts of sodium hydroxide, 7-25 parts of silicon dioxide, and 19-39 parts of water. The hollow plate produced herein is good in wear resistance and is waterproof, damp-proof and oil-proof; the production method described herein has simple process and low cost.

Description

technical field [0001] The invention belongs to the field of packaging materials, and relates to a hollow plate packaging material, in particular to a wear-resistant hollow plate and a preparation method thereof. Background technique [0002] Currently, there are many kinds of packaging materials used in packaging products made of glass, steel, metal and aluminum materials, and the packaging materials can be used during transportation, preservation and storage until delivered to users. During transportation and storage, products are exposed to many external factors, these are moisture, humidity, oil, dust and impacts. Therefore, in order to protect products from being damaged by these external factors, highly resistant packaging materials are required. [0003] Because glass, steel, metal and aluminum are hard and heavy, they can be difficult to pack. The materials used to package these products should be resistant to water, moisture or oil, scratches and dust, and not to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/04C08L23/06C08L23/12C08L3/10C08K13/04C08K7/14C08K5/053C08K3/22C08K3/36
CPCC08L67/04C08L3/10C08L23/06C08L2205/035C08L23/12C08K13/04C08K7/14C08K5/053C08K3/22C08K3/36
Inventor 顾建芳
Owner SUZHOU DINGLI PACKAGING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap