Preparing method for polymeric ferric chlorosulfate water purifying agent

A technology of ferric sulfate chloride and water purifying agent, applied in the field of water treatment, which can solve the problems of low cost, fast purification speed, and difficult treatment of pyrite slag, and achieve low cost, fast water purification speed, and reduction of harmful substances The effect of content

Inactive Publication Date: 2016-08-31
JIANGMEN JIANGHAI WEI CLEAN WATER MATERIALS CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to make up for the deficiencies in the prior art, the present invention provides a polymeric ferric chloride sulfate water purifying agent and its preparation method. The water purifying agent solves the problem that pyrite slag is difficult to handle, and it can effectively remove the polluting components, and the purification speed is fast and the cost is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The polymeric ferric sulfate chloride water purifying agent is configured according to the following parts by weight: 50 parts of pyrite slag, 15 parts of diatomaceous earth, 200 parts of sulfuric acid, 150 parts of hydrochloric acid, 10 parts of sodium chlorate, and 30 parts of nitric acid.

[0018] The preparation method of above-mentioned polymeric ferric sulfate chloride water purifier comprises the following steps:

[0019] (1) Grinding the pyrite slag and diatomite to 200 mesh, set aside;

[0020] (2) Add sulfuric acid and hydrochloric acid into a reaction kettle with a pressure of 0.3Mpa, and heat to 50°C;

[0021] (3) Add the powder obtained in step (1) into the reaction kettle and stir for 2 hours;

[0022] (4) Add sodium chlorate and nitric acid into the reaction kettle, heat to 60°C, and stir for 5 hours;

[0023] (5) After the solution in the reaction kettle in step (4) is left to cool, the polymeric ferric sulfate chloride water purifying agent can be obt...

Embodiment 2

[0025] The polymeric ferric sulfate chloride water purifying agent is configured according to the following parts by weight: 100 parts of pyrite slag, 25 parts of diatomaceous earth, 350 parts of sulfuric acid, 250 parts of hydrochloric acid, 20 parts of sodium chlorate, and 50 parts of nitric acid.

[0026] The preparation method of above-mentioned polymeric ferric sulfate chloride water purifier comprises the following steps:

[0027] (1) Grinding pyrite slag and diatomite to 300 mesh, set aside;

[0028] (2) Add sulfuric acid and hydrochloric acid into a reaction kettle with a pressure of 0.3Mpa, and heat to 50°C;

[0029] (3) Add the powder obtained in step (1) into the reaction kettle and stir for 2 hours;

[0030] (4) Add sodium chlorate and nitric acid into the reaction kettle, heat to 60°C, and stir for 6 hours;

[0031] (5) After the solution in the reaction kettle in step (4) is left to cool, the polymeric ferric sulfate chloride water purifying agent can be obtain...

Embodiment 3

[0033] The polymeric ferric sulfate chloride water purifying agent is configured according to the following parts by weight: 80 parts of pyrite slag, 20 parts of diatomaceous earth, 300 parts of sulfuric acid, 200 parts of hydrochloric acid, 15 parts of sodium chlorate, and 45 parts of nitric acid.

[0034] The preparation method of above-mentioned polymeric ferric sulfate chloride water purifier comprises the following steps:

[0035] (1) Grinding the pyrite slag and diatomite to 400 mesh, set aside;

[0036] (2) Add sulfuric acid and hydrochloric acid into a reaction kettle with a pressure of 0.3Mpa, and heat to 60°C;

[0037] (3) Add the powder obtained in step (1) into the reaction kettle and stir for 2 hours;

[0038] (4) Add sodium chlorate and nitric acid into the reaction kettle, heat to 60°C, and stir for 4 hours;

[0039] (5) After the solution in the reaction kettle in step (4) is left to cool, the polymeric ferric sulfate chloride water purifying agent can be obt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparing method for a polymeric ferric chlorosulfate water purifying agent. Raw materials include pyrite cinder, kieselguhr, sulfuric acid, hydrochloric acid, an oxidizing agent and a catalyst. Pyrite cinder is effectively used, waste is turned into wealth, and the problem that pyrite cinder is difficult to dispose is solved; when the water purifying agent is used for purifying a water body, alumen ustum is large in the coagulation process, and the water purifying agent is high in settling speed and free of secondary pollution and has a good purifying effect.

Description

technical field [0001] The invention belongs to the field of water treatment, and in particular relates to a preparation method of a polymeric ferric sulfate chloride water purifying agent. Background technique [0002] At present, my country's industrial sulfuric acid production is mainly obtained by roasting pyrite ore into sulfur dioxide, followed by purification, catalytic oxidation, and absorption. During the roasting process, a large amount of pyrite slag is produced, the main components of which are iron oxide, aluminum oxide, silicon dioxide, calcium oxide, magnesium oxide, lead, zinc, selenium, arsenic, phosphorus, etc. , not only occupies land, pollutes the environment, but also causes groundwater pollution, which has always been one of the difficult problems for sulfuric acid enterprises. And iron oxide in pyrite slag is one of the raw materials for preparing polyferric chloride water purifying agent, therefore, how to use pyrite slag to prepare polymeric ferric ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C02F1/52C02F1/28
CPCC02F1/5236C02F1/281
Inventor 杨炯辉
Owner JIANGMEN JIANGHAI WEI CLEAN WATER MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap