Method for electrophoresis of dual-color patterns on metal surface

A metal surface and electrophoresis technology, applied in the direction of electrophoretic plating, electrolytic coating, adhesive type, etc., can solve the problems of troublesome screen switching and cleaning and maintenance, great influence on performance and appearance, and damage to the electrophoretic film layer at one time. Achieve the effect of clear pattern boundary, good boiling test effect and long appearance life

Active Publication Date: 2016-11-02
JOMOO KITCHEN & BATHROOM
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When cleaning the ink, strong alkali or other corrosive substances must be used as cleaning agents, which will cause damage to the primary electrophoretic film layer, thus greatly affecting its performance and appearance, and easily causing environmental pollution
In addition, to form the pattern of the preset shape, the ink needs to use screen printing and other methods to achieve different patterns by designing different screens. Switching between screens and cleaning and maintenance are troublesome, costly, screen life is short, and the process is relatively slow. complex, which limits its application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for electrophoresis of dual-color patterns on metal surface

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] A two-color pattern electrophoresis method on a metal surface. A masking film made of hot melt adhesive is adhered to the surface of a metal product, and electrophoretic paint of different colors is deposited on the covered area and the uncovered area of ​​the masking film through secondary electrophoresis, thereby forming a predetermined pattern. Two-tone pattern.

[0034] The masking film is a preset pattern formed by cutting a hot-melt adhesive film, with a thickness of 20-150 μm and a softening point of the hot-melt adhesive in the range of 80-180°C. In one embodiment, during production, the materials forming the hot-melt adhesive are uniformly mixed according to the proportion, and after being melted and blended by an internal mixer or an extruder at 120-210°C, they are then rolled into a predetermined thickness by a calender. Film, the film is rewound after cooling. When in use, the hot melt adhesive film is cut, specifically through water cutting, punching or la...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for electrophoresis of dual-color patterns on the metal surface. A masking film of a preset shape is manufactured with hot melt adhesive, and the masking film adheres to the metal surface; a first paint layer is formed in an uncovering area of the masking film through primary electrophoresis; and a second paint layer different from the first paint layer in color is deposited in a covering area of the masking film through secondary electrophoresis after the masking film is removed, and accordingly the patterns of the masking film are transferred to the metal surface. The masking film made of the hot melt adhesive can be removed easily by being dissolved and cleaned with hot water or an organic solvent, strong base or other corrosive matter is not needed, and the film structure cannot be affected; and meanwhile, various dual-color electrophoresis patterns can be formed as needed, the manufacturing process is simple, the appearance life is long, and the application range is enlarged.

Description

technical field [0001] The invention relates to a metal surface treatment method, in particular to a two-color pattern electrophoresis method on the metal surface. Background technique [0002] The monotonous metallic or single-color paint surface of metal products can no longer meet people's needs for diversified product appearance. Therefore, while protecting the surface of metal products, a colorful decorative pattern appearance is formed to manufacture decorative products and unify the style with other parts High-quality products or novel and beautiful products are gradually being valued, and their production processes are also developing day by day. [0003] The existing pattern appearance production methods include surface spray coating, heat transfer pattern, printing, etc. The ink layer of these methods is separated from the primer, and only exists on the surface of the product without penetrating the primer, which is easily damaged by wear and corrosion. etc., espe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25D13/20C25D13/22C09J129/04C09J123/08C09J175/04C09J133/08C09J177/00C09J167/00
CPCC08L2201/06C08L2205/03C08L2205/035C09J129/04C25D13/20C25D13/22C08L23/0853C08L75/04C08L23/0861C08L23/0869C08L33/08C08L77/00C08L67/00
Inventor 林孝发林孝山李伟宇唐海舟王汉春
Owner JOMOO KITCHEN & BATHROOM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com