Scrubbing-resistant high-adhesion metal flashing coating for photo frame

A technology of metallic flash paint and scrub resistance, applied in polyester coatings, coatings and other directions, can solve the problem that the scrub resistance and high adhesion performance of metallic flash paint cannot be satisfied, and achieve excellent scrub resistance, small steric hindrance, and improved performance. Effect

Inactive Publication Date: 2016-11-09
蚌埠市禹会区贵宾装饰材料商行
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Then the scrub resistance and high adhesion performance of the metal flash coating in the prior art can not meet the needs during actual use, so it is urgent to design a metal flash coating with excellent scrub resistance and high adhesion performance to meet the actual use requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A scrub-resistant high-adhesion metal glitter coating for photo frames proposed by the present invention, its raw materials include by weight: 40 parts of hydroxyl-containing acrylic resin, 10 parts of water-based polyester resin, 4 parts of ternary vinyl chloride resin, 4.5 parts of amino resin , 2.5 parts of dimethylethanolamine, 6 parts of water-based polyurethane, 4 parts of polyurethane dispersant, 2.5 parts of ethylene glycol butyl ether, 5 parts of modified cellulose acetate butyrate, 6 parts of aluminum powder, 2.5 parts of antimony trioxide, titanium 6 parts of white powder, 6.5 parts of superfine heavy calcium carbonate, 3.5 parts of superfine kaolin, 2.5 parts of microplastic crystal particles, 4.5 parts of curing agent, 2.5 parts of leveling agent, 3.5 parts of wetting agent, 3 parts of defoaming agent, Thickener 4 parts.

[0017] Among them, the neutralization degree of the hydroxyl-containing acrylic resin is 85%, the hydroxyl content is 3.9%, the viscosit...

Embodiment 2

[0020] A scrub-resistant high-adhesion metal glitter coating for photo frames proposed by the present invention, its raw materials include by weight: 35 parts of hydroxyl-containing acrylic resin, 15 parts of water-based polyester resin, 2 parts of ternary vinyl chloride resin, 6 parts of amino resin , 1 part of dimethylethanolamine, 9 parts of water-based polyurethane, 2 parts of polyurethane dispersant, 4 parts of ethylene glycol butyl ether, 2 parts of modified cellulose acetate butyrate, 9 parts of aluminum powder, 1 part of antimony trioxide, titanium 9 parts of white powder, 4 parts of superfine heavy calcium carbonate, 5 parts of superfine kaolin, 1 part of microplastic crystal particles, 6 parts of curing agent, 1 part of leveling agent, 5 parts of wetting agent, 1 part of defoamer, Thickener 6 parts.

[0021] Among them, the neutralization degree of the hydroxyl-containing acrylic resin is 84%, the hydroxyl content is 4.2%, the viscosity is 1800mpa·s, the glass transi...

Embodiment 3

[0024] A scrub-resistant high-adhesion metal glitter coating for photo frames proposed by the present invention, its raw materials include by weight: 45 parts of hydroxyl-containing acrylic resin, 5 parts of water-based polyester resin, 6 parts of ternary vinyl chloride resin, and 3 parts of amino resin , 4 parts of dimethylethanolamine, 3 parts of water-based polyurethane, 6 parts of polyurethane dispersant, 1 part of butyl glycol ether, 8 parts of modified cellulose acetate butyrate, 3 parts of aluminum powder, 4 parts of antimony trioxide, titanium 3 parts of white powder, 9 parts of superfine heavy calcium carbonate, 2 parts of superfine kaolin, 4 parts of microplastic crystal particles, 3 parts of curing agent, 4 parts of leveling agent, 2 parts of wetting agent, 5 parts of defoaming agent, Thickener 2 parts.

[0025] Among them, the neutralization degree of the hydroxyl-containing acrylic resin is 86%, the hydroxyl content is 3.6%, the viscosity is 2200mpa·s, the glass t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Glass transition temperatureaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a scrubbing-resistant high-adhesion metal flashing coating for a photo frame. The scrubbing-resistant high-adhesion metal flashing coating is prepared from 35-45 parts by weight of hydroxy acrylic resin, 5-15 parts by weight of aqueous polyester resin, 2-6 parts by weight of ternary vinyl chloride-vinyl acetate resin, 3-6 parts by weight of amino resin, 1-4 parts by weight of dimethyl ethanolamine, 3-9 parts by weight of aqueous polyurethane, 2-6 parts by weight of a polyurethane dispersant, 1-4 parts by weight of ethylene glycol monobutyl ether, 2-8 parts by weight of modified cellulose acetate butyrate, 3-9 parts by weight of aluminum powder, 1-4 parts by weight of antimony oxide, 3-9 parts by weight of titanium dioxide, 4-9 parts by weight of ultrafine heavy calcium carbonate, 2-5 parts by weight of ultrafine kaolin, 1-4 parts by weight of micro-plastic-crystal grains, 3-6 parts by weight of a curing agent, 1-4 parts by weight of a levelling agent, 2-5 parts by weight of a wetting agent, 1-5 parts by weight of an antifoaming agent and 2-6 parts by weight of a thickening agent. The metal flashing coating has excellent scrubbing resistance and high adhesion performances.

Description

technical field [0001] The invention relates to a flash paint, in particular to a metal flash paint with scrubbing resistance and high adhesion for photo frames. Background technique [0002] At present, the scaly aluminum powder in the metallic flash paint forms a multi-layer parallel arrangement in the coating film, which can effectively reflect ultraviolet rays, infrared rays and visible light, delay its aging damage to the coating film, and can also effectively prevent water, air, etc. And the penetration of ions, because of its unique decorative and anti-corrosion effects, it is more and more used in the surface coating of photo frames. [0003] Then the scrub resistance and high adhesion performance of the metal glitter coating in the prior art cannot meet the needs during actual use, so it is urgent to design a metal glitter coating with excellent scrub resistance and high adhesion performance to meet the actual use requirements. Contents of the invention [0004] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/14C09D167/00C09D127/06C09D161/20C09D7/12
CPCC09D133/14C08L2205/035C09D7/61C09D7/63C09D7/65C08L67/00C08L27/06C08L61/20C08L75/04C08L1/14C08K13/02C08K5/06C08K2003/0812C08K3/2279C08K2003/2241C08K2003/265C08K3/346
Inventor 刘贵斌刘阳
Owner 蚌埠市禹会区贵宾装饰材料商行
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com