Tire burst-proof rubber

An explosion-proof rubber and tire technology, applied in the direction of adhesives, adhesive types, mineral oil hydrocarbon copolymer adhesives, etc., can solve the problems of throwing on the axis, short service life of explosion-proof glue, and failure to achieve explosion-proof effect. , to achieve high-efficiency fit performance, improve the effect of cold and heat resistance

Inactive Publication Date: 2016-11-09
东莞市成铭胶粘剂有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The service life of traditional explosion-proof rubber is extremely short. After a period of use, it is easy to be thrown to the axis by the centripetal force of the tire, and due to factors such as high temperature on the road surface, it will flow and accumulate on the inner wall of the tire, not only failing to achieve the explosion-proof effect, but also is an additional risk factor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A tire explosion-proof rubber, including a main polymer, a tackifying resin, a diluent and an additive, and the components are set according to the following parts by mass:

[0032] Host polymer 20 - 35%

[0033] Tackifying resin 30 - 60%

[0034] Thinner 10 - 25%

[0035] Additives 0.2 - 0.5%.

[0036] in:

[0037] The host polymer is SIS synthetic rubber. The tackifying resin is high temperature petroleum resin. The diluent is naphthenic oil. The additive is an antioxidant.

Embodiment 2

[0039] A tire explosion-proof rubber, including a main polymer, a tackifying resin, a diluent and an additive, and the components are set according to the following parts by mass:

[0040] Host polymer 21 - 35%

[0041] Tackifying resin 30 - 55%

[0042] Thinner 15 - 23%

[0043] Additives 0.2 - 0.4%.

[0044] in:

[0045] The host polymer is SIS synthetic rubber. The tackifying resin is high temperature petroleum resin. The diluent is naphthenic oil. The additive is an antioxidant.

Embodiment 3

[0047] A tire explosion-proof rubber, including a main polymer, a tackifying resin, a diluent and an additive, and the components are set according to the following parts by mass:

[0048] Host polymer 21 - 34%

[0049] Tackifying resin 33 - 55%

[0050] Thinner 15 - 22%

[0051] Additives 0.2 - 0.4%.

[0052] in:

[0053] The host polymer is SIS synthetic rubber. The tackifying resin is high temperature petroleum resin. The diluent is naphthenic oil. The additive is an antioxidant.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses tire burst-proof rubber. The tire burst-proof rubber comprises the following components in percentage by mass: 20-35% of a main polymer, 30-60% of tackifying resin, 10-25% of a diluting agent and 0.2-0.5% of an additive, and a special polystyrene-isoprene-styrene block copolymer is used as a main raw material. Through grafting modification, the rubber has 10 or more branched chains, and has efficient attaching performance, and through a special tackifier, cold resistance and heat resistance are improved, and a burst-proof function is effectively realized.

Description

technical field [0001] The invention relates to a tire explosion-proof rubber. Background technique [0002] Now the pneumatic tires of automobiles and electric bicycles will quickly leak and decompress after being punctured by sharp substances, which will cause great harm to people's safety. According to the statistics of the traffic management department, more than 70% of the highway traffic accidents in my country are caused by caused by a blowout. [0003] Based on the above reasons, there are currently many run-flat tires on the market, the principle of which is mostly to coat the inside of the tire with various adhesives to prevent sharp objects from piercing the tire and causing a blowout. The service life of traditional explosion-proof rubber is extremely short. After a period of use, it is easy to be thrown to the axis by the centripetal force of the tire, and due to factors such as high temperature on the road surface, it will flow and accumulate on the inner wall ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J157/02C09J153/02C09J191/00C09J11/00
CPCC09J157/02C08L2205/03C09J11/00C08L53/02C08L91/00
Inventor 邓小华韦杰陈铭
Owner 东莞市成铭胶粘剂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap