Induction heating method for preparing tungsten carbide wear-resistant coating required for swing head of swing mill

An induction heating and wear-resistant coating technology, which is applied in the field of wear-resistant coating preparation in material processing engineering, can solve problems such as the decrease in the hardness of the brazing substrate, achieve a large coating thickness, be easy to implement, and improve wear resistance Effect

Active Publication Date: 2018-10-23
NANCHANG INST OF TECH
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] Due to the use of induction local heating, this technology brazes to prepare 0.5-3.0mm thick tungsten carbide composite coating, which solves the shortcoming of the overall heating and brazing matrix hardness in the furnace, and can obtain a good metallurgical bonding interface, and the coating and the matrix are combined. Good, can meet the use requirements of the hemisphere, the key component of the swing rolling machine

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Induction heating method for preparing tungsten carbide wear-resistant coating required for swing head of swing mill
  • Induction heating method for preparing tungsten carbide wear-resistant coating required for swing head of swing mill

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] The method for preparing the tungsten carbide wear-resistant coating required for the swing head of the pendulum mill according to the argon protection induction heating described in this embodiment includes the following steps:

[0048] (1) Stick the paste prefabricated layer containing tungsten carbide WC or tungsten carbide-cobalt WC-Co, self-fluxing alloy powder on the metal substrate with epoxy resin adhesive; the paste prefabricated layer can be two layers Above, the content of tungsten carbide WC or tungsten carbide-cobalt WC-Co in different layers is different, from the surface layer to the paste precoat close to the steel substrate, the content of tungsten carbide WC or tungsten carbide-cobalt WC-Co gradually Reduced to form a tungsten carbide-cobalt content gradient to reduce welding stress;

[0049] The formula of described pasty prefabricated layer is:

[0050] (A) Tungsten carbide WC or tungsten carbide-cobalt WC-Co, and mechanically alloyed self-fluxing a...

Embodiment 2

[0062] The method for preparing the tungsten carbide wear-resistant coating required for the swing head of the pendulum mill according to the argon protection induction heating described in this embodiment includes the following steps:

[0063] (1) Stick the paste prefabricated layer containing tungsten carbide WC or tungsten carbide-cobalt WC-Co, self-fluxing alloy powder on the metal substrate with epoxy resin adhesive; the paste prefabricated layer can be two layers Above, the content of tungsten carbide WC or tungsten carbide-cobalt WC-Co in different layers is different, from the surface layer to the paste precoat close to the steel substrate, the content of tungsten carbide WC or tungsten carbide-cobalt WC-Co gradually Reduced to form a tungsten carbide-cobalt content gradient to reduce welding stress;

[0064] The formula of described pasty prefabricated layer is:

[0065] (A) Tungsten carbide WC or tungsten carbide-cobalt WC-Co, and mechanically alloyed self-fluxing a...

Embodiment 3

[0077] The method for preparing the tungsten carbide wear-resistant coating required for the swing head of the pendulum mill according to the argon protection induction heating described in this embodiment includes the following steps:

[0078] (1) Stick the paste prefabricated layer containing tungsten carbide WC or tungsten carbide-cobalt WC-Co, self-fluxing alloy powder on the metal substrate with epoxy resin adhesive; the paste prefabricated layer can be two layers Above, the content of tungsten carbide WC or tungsten carbide-cobalt WC-Co in different layers is different, from the surface layer to the paste precoat close to the steel substrate, the content of tungsten carbide WC or tungsten carbide-cobalt WC-Co gradually Reduced to form a tungsten carbide-cobalt content gradient to reduce welding stress;

[0079] The formula of described pasty prefabricated layer is:

[0080] (A) Tungsten carbide WC or tungsten carbide-cobalt WC-Co, and mechanically alloyed self-fluxing all...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

A method for preparing the tungsten carbide wear-resistant coating required for the swing head of the pendulum mill by induction heating. on the metal substrate; then paste the BNi2 brazing material on the tungsten carbide composite powder paste prefabricated layer by the same means; put the above metal prefabricated parts into the argon protection induction device for induction heating. The experimental method adopted by the invention is simple and easy to implement, and the developed wear-resistant tungsten carbide coating is low in cost, simple and easy to implement, and has high matrix strength, and the wear resistance of the coating is significantly improved due to the holes for oil storage.

Description

technical field [0001] The invention relates to a method for preparing a tungsten carbide wear-resistant coating required for the swing head of a swing mill by an argon-protected induction heating infiltration brazing method, which belongs to the field of wear-resistant coating preparation in material processing engineering. Background technique [0002] Oscillating rolling is a forging technology, which is a rotary forming process that realizes integral forming of the workpiece through successive and continuous partial forming. Oscillating rolling can realize net-shape or near-net-shape processing, which has the advantages of labor saving, small impact, small vibration, low noise, easy filling of metal cavity, low investment, long mold life, high product precision, etc., and saves energy, materials, and Investment has expanded the scope of plastic processing and has been widely used in many industrial sectors such as machinery, automobiles, electrical appliances, instrument...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B23K1/002B23K1/20B23K3/04B23K3/08
CPCB23K1/002B23K1/20B23K3/04B23K3/08
Inventor 晏建武祝志芳
Owner NANCHANG INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products