Polymer-modified glass fiber and preparation method thereof

A glass fiber and polymer technology, applied in the field of polymer modified glass fiber and its preparation, can solve the problems of poor wear resistance, poor toughness of glass fiber, etc.

Inactive Publication Date: 2016-12-07
安徽金生金世电子科技有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the poor toughness and wear resistance of glass fiber, its popularization is limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] (1) Place 1 glass fiber with a volume length of 15 μm in 1.1 volume concentration of 0.05 mol / L hypochlorous acid solution, and heat at 65°C for 20 minutes to carry out oxidation treatment;

[0020] (2) Place 1 volume of oxidized glass fibers in 2 volumes of titanate coupling agent with a temperature of 40°C and a volume concentration of 25% for 1 hour, then filter, wash, and dry to obtain pretreated glass fibers ;

[0021] (3) 2 parts by weight of pretreated glass fiber and 1 part by weight of epoxy resin were mixed and heated at 155° C. for 35 minutes to prepare polymer modified glass fiber A1.

Embodiment 2

[0023] (1) Place a glass fiber with a volume length of 28 μm in a hypochlorous acid solution with a volume concentration of 0.05 mol / L, and heat it at 83° C. for 28 minutes to perform oxidation treatment;

[0024] (2) Soak 1 volume of the glass fiber after oxidation treatment in 5 volumes of titanate coupling agent with a volume concentration of 43% at a temperature of 65°C for 1.8 hours, then filter, wash, and dry to obtain pretreated glass fiber;

[0025] (3) 5 parts by weight of pretreated glass fiber and 1 part by weight of epoxy resin were mixed and heated at 170° C. for 55 minutes to prepare polymer modified glass fiber A2.

Embodiment 3

[0027] (1) Put a glass fiber with a volume length of 20 μm in a hypochlorous acid solution with a volume concentration of 0.1mol / L, and heat it at 70°C for 25 minutes to perform oxidation treatment;

[0028] (2) Place 1 volume of the glass fiber after oxidation treatment in 3 volumes of titanate coupling agent with a temperature of 55°C and a volume concentration of 35% for 1.5 hours, then filter, wash, and dry to obtain pretreated glass fiber;

[0029] (3) Mix 2 parts by weight of pretreated glass fiber with 1 part by weight of epoxy resin and heat at 160° C. for 45 minutes to prepare polymer modified glass fiber A3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a polymer-modified glass fiber. The preparation method comprises the following steps: putting a glass fiber into a hypochlorous acid solution, and heating for oxidization treatment; soaking the glass fiber subjected to oxidization treatment into a titanate coupling agent to obtain a pretreated glass fiber; mixing the pretreated glass fiber with epoxy resin, and heating to obtain the polymer-modified glass fiber, wherein the length of the glass fiber is 15 to 30 [mu]m, and the volume concentration of the titanate coupling agent is 25 to 45 percent. The polymer-modified glass fiber prepared by the method has the characteristics of high toughness and wear resistance.

Description

technical field [0001] The invention relates to glass fibers, in particular to polymer modified glass fibers and a preparation method thereof. Background technique [0002] Glass fiber is an inorganic non-metallic material with excellent performance. There are many kinds of it. It has good insulation, strong heat resistance, good corrosion resistance and high mechanical strength. Glass fiber is made of glass balls or waste glass through high-temperature melting, wire drawing, winding, weaving and other processes. The diameter of its single filament is several microns to more than 20 microns. All are composed of hundreds or even thousands of monofilaments. The glass fiber is often used as reinforcing material of composite material, electrical insulation and heat insulation materials, substrate and other national economy fields. However, due to the poor toughness and wear resistance of glass fiber, its popularization is limited. Contents of the invention [0003] One of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/00C08K9/04C08K9/02C08K7/14
CPCC08K9/04C08K7/14C08K9/02C08K2201/004C08K2201/014C08L63/00
Inventor 倪伟
Owner 安徽金生金世电子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com