Process for producing high-perception Guangdong decoration

A kind of technology, Guangcai technology, applied in the field of Guangcai technology, can solve the problems of ice color, production time-consuming and so on

Active Publication Date: 2017-01-11
区冠舟
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The glaze of the porcelain pieces provided by this document is bright and smooth, bright in color and does not change color and fade, but when the pigment is thickly applied, ice color phenomenon is easy to occur, and there is an additional high-temperature roasting process compared with the traditional process, and the production is more time-consuming

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for producing high-perception Guangdong decoration
  • Process for producing high-perception Guangdong decoration

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Get 200g of quartz, 300g of red lead, 320g of zirconia and 150g of lanthanum oxide, mix and grind until the average particle size is about 20 μm, and obtain the anti-icing material; add a mass ratio of 20% of the anti-icing material to the color porcelain pigment; Draw the drawing on the porcelain piece; take an appropriate amount of the above-mentioned colored porcelain pigment that has been added with anti-icing material and fill it into the drawing. The thickness of the coloring pigment is 8mm; Firing, the temperature is set at 800°C.

Embodiment 2

[0033] Get 180g of quartz, 400g of red lead, 300g of zirconia and 100g of praseodymium oxide, mix and grind until the average particle size is about 20 μm, and obtain the anti-icing material; add a mass ratio of 10% of the anti-icing material to the color porcelain pigment; Draw the draft on the porcelain piece; take an appropriate amount of the above-mentioned colored porcelain pigment that has been added with anti-icing material and fill it into the artwork. The thickness of the coloring pigment is 10mm; Firing, the temperature is set at 800°C.

Embodiment 3

[0035] Take 180g of quartz, 400g of red lead, 300g of zirconia, 500g of lanthanum oxide, and 50g of scandium oxide, mix and grind until the average particle size is about 20 μm, and obtain an anti-icing material; add a mass ratio of 15% anti-icing material to the color porcelain pigment ; use ink to trace the drawing on the porcelain piece; take an appropriate amount of the above-mentioned colored porcelain pigment that has been added with anti-icing material and fill it into the artwork, the thickness of the coloring pigment is 10mm; after filling the color, carve a three-dimensional image with a carving knife; The pieces were fired in an electric furnace at a temperature of 800°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a process for producing high-perception Guangdong decoration, and provides an anti-icing material applied to the process. The anti-icing material is prepared from one or more of quartz, minium, zirconia and rare-earth in a mass ratio of (18-30):(30-55):(20-40):(10-25), preferably 20:30:32:15. The anti-icing material can be used for overcoming cracking and falling between pigment and body glaze, and decorative porcelain pigment containing 10-20 percent of the anti-icing material is glazed and has a thickness of 100mm. The process can be widely applied to glazing of Guangdong decorative porcelain and porcelain painting.

Description

technical field [0001] The invention belongs to the technical field of decoration, and in particular relates to a wide-color process for producing high three-dimensional effect. Background technique [0002] Guangcai porcelain is a handicraft made by painting and firing on various white porcelain vessels. In Guangcai technology, the thickness of coloring pigments generally cannot exceed 2mm. Porcelain pieces exceeding this thickness are easy to crack and fall off after the porcelain pieces are fired in the furnace and cooled. This phenomenon is called ice color in the industry. [0003] CN1165122 discloses a glaze for high-temperature jilan glaze in-glaze ceramics and a manufacturing method thereof. The document adopts a specific glaze formula, and the finished product is decorated and fired twice. The specific method is to paste the prefabricated flower paper made of high-temperature Jilan ceramic pigment on the white body porcelain made of glaze and fire it at high temper...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/85C09C1/00B44C1/22
CPCB44C1/225C04B41/5072C04B41/85C09C1/0009C04B41/5045C04B41/5035C04B41/5042
Inventor 区冠舟
Owner 区冠舟