Modified cement brick

A cement brick and modification technology, applied in the field of cement bricks, can solve the problems of large difference in drying shrinkage rate and easy cracks in finished products, and achieve the effects of low cost, low probability of cracks, and good water and acid resistance.

Inactive Publication Date: 2017-01-25
北海金匠水泥制品有限责任公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Patent CN101126271A discloses a cement decorative board including a surface layer and a bottom layer; however, the dry shrinkage rate gap between the surface layer and the bottom layer of the cement decorative board is relatively large, and cracks are prone to appear in the finished product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified cement brick

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] A modified cement brick is composed of the following components in parts by weight: 25 parts by weight of cement, 12 parts of magnesium chloride, 7 parts of calcium sulfate, 50 parts of fly ash, 30 parts of yellow sand, 20 parts of cinder and 13 parts of plant fiber.

Embodiment 2

[0012] A modified cement brick is composed of the following ingredients in parts by weight: 20 parts by weight of cement, 16 parts of magnesium chloride, 5 parts of calcium sulfate, 60 parts of fly ash, 20 parts of yellow sand, 30 parts of cinder and 10 parts of plant fiber.

Embodiment 3

[0014] A modified cement brick is composed of the following components in parts by weight: 30 parts by weight of cement, 8 parts of magnesium chloride, 9 parts of calcium sulfate, 40 parts of fly ash, 40 parts of yellow sand, 10 parts of cinder and 16 parts of plant fiber.

[0015] The production method of the above product is as follows: stirring and mixing each component according to the proportion, adding an appropriate amount of water to make a slurry, injecting into a mold to vibrate, condensing and curing for 3 days, demoulding, and drying.

[0016]

[0017] The cement brick prepared by the invention has the functions of high wear resistance and high anti-skid, which reduces the risk of easily slipping and falling when the floor brick is wet. After testing, the product's technical standards meet the requirements.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a modified cement brick, made from, by weight, 20-30 parts of cement, 8-16 parts of magnesium chloride, 5-9 parts of calcium sulfate, 40-60 parts of flyash, 20-40 parts of yellow sand, 10-30 parts of coal residue, and 10-16 parts of plant fibers. The modified cement brick has the advantages that the finished brick has low chances for cracking owing to tight adhesion; the brick has good water resistance and acid resistance, high cracking strength and high breaking strength and is free of deforming or shading; the color, shape and material of the brick may be designed as required, and the brick features low cost, environmental friendliness and meeting the industrial policy of sustainable development; the brick is widely applicable to decorations for walls, grounds, furniture surface and the like.

Description

technical field [0001] The invention relates to the technical field of cement bricks, in particular to a modified cement brick. Background technique [0002] With the development of the country's economic life, the materials used in interior and exterior design have involved various industries such as steel, non-ferrous metals, chemicals, textiles, wood, ceramics, plastics, and glass. People's emphasis and emphasis on the spirit of the theme of interior and exterior design also requires new materials with great personality and moderate cost to realize. As far as wall and floor decoration is concerned, there are many types of materials that can be used, such as ceramic glazed tiles, marble, and granite facing tiles. However, the above-mentioned materials are difficult to make new breakthroughs in decorative effects, and the cost is high. It is quite necessary to develop decorative bricks with low cost, good performance, environmental protection, and in line with national dev...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/14
CPCC04B28/14C04B2201/50C04B7/00C04B22/124C04B18/08C04B14/068C04B18/10C04B16/02
Inventor 刘兴汉
Owner 北海金匠水泥制品有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com