A technology of blended fabrics and blended yarns, applied in the field of textile materials, can solve the problems of not meeting the requirements of use, poor shear resistance between fabrics and fabrics, etc., and achieve the effect of improving shear resistance.
Active Publication Date: 2019-02-12
ZHENSHI GRP HUAMEI NEW MATERIALS
View PDF6 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
This patent is used for clothing, and this application is mainly used in the field of composite materials. Although the blended fabric has comfort, excellent radiation resistance and softness, the shear resistance between the fabric and the fabric is relatively poor. Can not meet people's use requirements, so it still has the above-mentioned defects
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0020] The present invention will be further described in detail below in conjunction with the accompanying drawings and examples. The following examples are explanations of the present invention and the present invention is not limited to the following examples.
[0021] Example.
[0022] see Figure 1 to Figure 3 , present implementation comprises chemical fiber blended fabric layer 4 and chemical fiber and glass fiber blended yarn 1, blended tow fabric is made up of multilayer chemical fiber blended fabric layer 4 and chemical fiber and glass fiber blended yarn 1 pierced therein, as figure 2 shown.
[0023] see figure 1 , the chemical fiber and glass fiber blended yarn 1 in the present embodiment includes chemical fiber filament 2 and glass fiber filament 3, and the chemical fiber filament 2 and glass fiber filament 3 are mixed and wound together during the production process of glass fiber filament 3; Chemical fiber and glass fiber blended yarn 1 On the one hand, becau...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention relates to a novel chemical fiber-and-glass fiber blended yarn fabric and a method for bonding fabric layers, and belongs to the technical field of textile materials. The novel chemical fiber and glass fiber blended yarn fabric comprises chemical fiber-blended fabric layers and chemical fiber-and-glass fiber blended yarns. The blended yarn fabric comprises two layers or more layers of the chemical fiber-blended fabric layers, and the chemical fiber-and-glass fiber blended yarns woven among the chemical fiber-blended fabric layers. The method for bonding the novel chemical fiber and glass fiber blended yarn fabric layers is further disclosed. According to the novel chemical fiber and glass fiber blended yarn fabric, the structure is simple and reasonable, the shearing resistance performance of a multi-layer blended fabric after mould pressing and rolling depression can be effectively improved, the tensile property and the bending performance are excellent.
Description
technical field [0001] The invention relates to a blended tow fabric and a method thereof, in particular to a chemical fiber and glass fiber blended tow fabric and a method for combining fabric layers, belonging to the technical field of textile materials. Background technique [0002] Chemical fiber and glass fiber blended fabrics are generally used in molding or continuous rolling production processes. When using them, the weight, fabric structure, and number of layers of the blended fabrics should be selected according to the requirements of the final product. However, due to the characteristics of the blended fabric itself, when the multi-layer blended fabric is used together, the combination of two adjacent layers of the blended fabric only depends on the melting of chemical fibers to form the interaction between the melts, so the interfacial bonding of two adjacent blended fabrics after forming The force is relatively weak, and interlaminar failure is prone to occur un...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): B32B5/08B32B27/02B32B27/12B32B17/02B32B17/12B32B5/26B32B37/02B32B38/18B32B37/10
CPCB32B5/08B32B5/26B32B17/067B32B27/12B32B37/02B32B37/10B32B38/18B32B2250/20B32B2262/0253B32B2262/0276B32B2262/101B32B2262/14B32B2307/546B32B2307/581
Inventor 周杰张健侃张海旭王敢维胡文武盛江峰杨国刚
Owner ZHENSHI GRP HUAMEI NEW MATERIALS