Method for synthesizing ers-7 zeolite molecular sieve with linear polyquaternium organic template
A technology of ERS-7, zeolite molecular sieve, applied in the direction of crystalline aluminosilicate zeolite, etc., can solve the problems of easy to have miscellaneous crystals, narrow zeolite phase region, complex template synthesis process, etc., to simplify synthesis, reduce difficulty, and improve The effect of catalytic activity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0019] Embodiment 1: the synthesis of linear polyquaternium organic template
[0020] According to the molar ratio of 1,4-dibromobutane and N,N,N,N-tetramethyl-1,4-butanediamine is 1:1, weigh 10g 1,4-dibromobutane and 15g Dissolve N,N,N,N-tetramethyl-1,4-butanediamine in 50ml of ethanol, set the temperature at 80°C to reflux, stir for 12 hours, after the reaction is completed, add ether to the reaction product to produce A white solid precipitated, filtered and dried to obtain the required template.
Embodiment 2
[0021] Embodiment 2: Synthesis of ERS-7 zeolite by linear polyquaternium salt organic template
[0022] 8.12g H 2 O, 0.065g NaAlO 2 , 0.3g NaOH, 0.65g organic template (T, structure such as figure 1 ) and 3.32g of silica sol with a silicon dioxide content of 30% were placed in a beaker and stirred evenly, and then the gel was added to a polytetrafluoroethylene stainless steel reaction kettle, crystallized at 160°C for 5 days and then completely crystallized, and the product was filtered with suction. The product is obtained after drying. The proportioning of reaction raw material is as follows:
[0023] 35H 2 O:SiO 2 :0.017Al 2 o 3 :0.23Na 2 O:0.04T
[0024] Through X-ray diffraction analysis, its structure is ERS-7 zeolite molecular sieve belonging to ESV ( figure 1 ), and it can be seen from the scanning electron microscope that the particle size of the synthesized product is relatively uniform and the purity is high, such as figure 2 shown.
Embodiment 3
[0025] Example 3: High temperature synthesis of ERS-7 zeolite with linear polyquaternium organic template
[0026] 12.67g H 2 O, 0.028g Al 2 (SO 4 ) 3 18H 2 O, 0.13g NaOH, 0.65g organic template (T, structure such as figure 1 ) and 3.32g of silica sol with a silicon dioxide content of 30% were placed in a beaker and stirred evenly, and then the gel was added into a polytetrafluoroethylene stainless steel reaction kettle, crystallized at 200°C for 1 day to completely crystallize, and the product was suction filtered, The product is obtained after drying. The proportioning of reaction raw material is as follows:
[0027] 50H 2 O:SiO 2 :0.0025Al 2 o 3 :0.1Na 2 O:0.04T
PUM
![No PUM](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/noPUMSmall.5c5f49c7.png)
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap