Halloysite nanotube-added abrasion-resistant type strippable macromolecular antirust film

A technology of halloysite nanotubes and polymers, which is applied in the direction of anti-corrosion coatings, coatings, polyether coatings, etc., and can solve problems such as limiting the application of anti-rust films

Inactive Publication Date: 2017-04-26
江海涛
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In Guo Jun's article "The Development of PVA Water-Soluble Polymer Peelable Antirust Film", he added antirust agent and other additives to polyvinyl alcohol, heated it in a water bath until it was completely dissolved, and then used the coating fluid to dissolve it completely. The extension method uniformly coats it on the metal surface, heats and dries it in a drying oven to form a film, and uses the neutral salt spray test, water solubility test and electron microscope test to characterize the performance of the polyvinyl alcohol antirust packaging film. The results show that the PVA antirust film not only has good antirust performance, but also has good peelability and water solubility, which meets the characteristics of green packaging and has good application prospects. However, the article uses polyvinyl alcohol and polyvinyl alcohol The combination of ethylene glycol is used as the carrier film-forming agent of the anti-rust film. Both polyvinyl alcohol and polyethylene glycol have good water solubility, and the prepared anti-rust film is not easy to dissolve in cold water at 40°C, but it is not easy to dissolve in cold water at a constant temperature. In the hot water heated to above 40°C in the water bath, it can be observed that the polyvinyl alcohol film will gradually soften first, then the film will become thinner, and finally dissolve completely, indicating that the antirust film is water-soluble and belongs to high-temperature water-soluble The film can be recycled, and it can be transported at room temperature or below 40°C to play a good anti-rust effect, which greatly limits the application field of the anti-rust film. It must be modified to improve its corrosion resistance, oil resistance, High temperature resistance and water resistance, etc., expand the application field, so that it can meet the anti-rust and anti-corrosion requirements under various conditions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] A wear-resistant and peelable polymer antirust film added with halloysite nanotubes, prepared from the following raw materials in parts by weight (kg): aluminum isopropoxide 6.8, silane coupling agent KH570 0.2, orthosilicate tetra Ethyl Ester 12, Span 80 1.5, Polyethylene Glycol 2, Isobutyl Triethoxysilane 3.8, Polyvinyl Alcohol 15, Emulsifier OP10 0.8, Glycerin 0.4, Tween 80 0.6, Lauryl Sulfate Sodium 1, triethanolamine 2, benzotriazole 3, sodium benzoate 3, halloysite 2.2, borax 1.8, appropriate amount of Pingpingjia, appropriate amount of nitric acid, appropriate amount of hydrochloric acid, appropriate amount of absolute ethanol, and appropriate amount of deionized water.

[0016] The wear-resistant peelable polymer antirust film added with halloysite nanotubes is prepared by the following specific steps:

[0017] (1) Mix aluminum isopropoxide and deionized water at a molar ratio of 1:100, reflux and stir in a water bath environment at 85°C for 1 hour, then add nit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a halloysite nanotube-added abrasion-resistant type strippable macromolecular antirust film. The halloysite nanotube-added abrasion-resistant type strippable macromolecular antirust film is prepared from the following raw materials of aluminum isopropoxide, silane coupling agent KH570, tetraethyl orthosilicate, Span 80, polyethylene glycol, i-butyltriethoxanesilane, polyvinyl alcohol, emulsifier OP10, glycerin, Tween 80, lauryl sodium sulfate, triethanolamine, benzotriazole, sodium benzoate, halloysite, borax, a proper amount of peregal, a proper amount of nitric acid, a proper amount of hydrochloric acid, a proper amount of absolute ethyl alcohol, and a proper amount of deionized water. The halloysite nanotube-added abrasion-resistant type strippable macromolecular antirust film has the advantages that a thin film can be formed on the surface of a workpiece, the waterproof and oilproof effects are realized, the easiness in cracking is avoided, the heat-resistant and aging-resistant properties are good, the antirust and anti-corrosive functions are good, the later stripping is convenient, and the antirust film is suitable for being popularized.

Description

technical field [0001] The invention relates to the technical field of metal surface treatment agents, in particular to a wear-resistant and peelable polymer antirust film added with halloysite nanotubes. Background technique [0002] According to statistics, every year in the world, steel products with a total weight equivalent to 10-20% of the annual metal content cannot be used due to corrosion, rust and other reasons. Therefore, people have adopted various anti-rust methods to avoid rust. Cut your losses. There are various kinds of antirust agents, among which sodium nitrite has been favored and widely used because of its excellent antirust performance and low price. , a lot of research and development work has been carried out at home and abroad, and a variety of alkyl, alkoxy, halo, naphthoic acids and their derivatives, nitrobenzoic acids, and borates, borates and molybdenum have been prepared. A new type of water-soluble rust inhibitor that replaces sodium nitrite ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D129/04C09D171/02C09D7/12C09D5/08
CPCC09D129/04C08L2201/08C09D5/08C09D7/61C09D7/62C09D7/63C09D7/70
Inventor 江海涛
Owner 江海涛
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products