Nitrile rubber oleophobic strippable high-molecular antirust membrane

A technology of nitrile rubber and polymer, which is applied in the direction of anti-corrosion coatings and coatings, and can solve the problems of restricting the application field of anti-rust film

Inactive Publication Date: 2017-05-31
江海涛
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In Guo Jun's article "The Development of PVA Water-Soluble Polymer Peelable Antirust Film", he added antirust agent and other additives to polyvinyl alcohol, heated it in a water bath until it was completely dissolved, and then used the coating fluid to dissolve it completely. The extension method uniformly coats it on the metal surface, heats and dries it in a drying oven to form a film, and uses the neutral salt spray test, water solubility test and electron microscope test to characterize the performance of the polyvinyl alcohol antirust packaging film. The results show that the PVA antirust film not only has good antirust performance, but also has good peelability and water solubility, which meets the characteristics of green packaging and has good application prospects. However, the article uses polyvinyl alcohol and polyvinyl alcohol The combination of ethylene glycol is used as the carrier film-forming agent of the anti-rust film. Both polyvinyl alcohol and polyethylene glycol have good water solubility, and the prepared anti-rust film is not easy to dissolve in cold water at 40°C, but it is not easy to dissolve in cold water at a constant temperature. In the hot water heated to above 40°C in the water bath, it can be observed that the polyvinyl alcohol film will gradually soften first, then the film will become thinner, and finally dissolve completely, indicating that the antirust film is water-soluble and belongs to high-temperature water-soluble The film can be recycled, and it can be transported at room temperature or below 40°C to play a good anti-rust effect, which greatly limits the application field of the anti-rust film. It must be modified to improve its corrosion resistance, oil resistance, High temperature resistance and water resistance, etc., expand the application field, so that it can meet the anti-rust and anti-corrosion requirements under various conditions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] A nitrile rubber oleophobic peelable polymer antirust film, prepared from the following raw materials in parts by weight (kg): aluminum isopropoxide 6.8, silane coupling agent KH550 0.2, tetraethyl orthosilicate 12 , Sucrose fatty acid ester 1.7, polyethylene glycol 2, isooctyl trimethoxysilane 3.7, polyvinyl alcohol 15, borax 1.8, methacryloxypropyl trimethoxysilane 1, nitrile rubber emulsion 2.4, Epoxidized natural rubber latex 0.3, graphene oxide 0.6, oleic acid amide 2, tetrasodium edetate 1, triethanolamine 3, borate 3, sodium lauryl sulfate 1, hydroxyl synthetic alcohol polyoxyethylene ether Appropriate amount, appropriate amount of methanol, appropriate amount of nitric acid, appropriate amount of hydrochloric acid, appropriate amount of absolute ethanol, and appropriate amount of deionized water.

[0016] Described a kind of nitrile rubber oleophobic type peelable macromolecule antirust film is prepared by the following specific steps:

[0017] (1) Mix aluminum...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a nitrile rubber oleophobic strippable high-molecular antirust membrane. The antirust membrane is prepared from the following raw materials: aluminum isopropoxide, silane coupler KH550, tetraethyl orthosilicate, sucrose fatty acid ester, polyethylene glycol, iso-octyltrimethoxysilane, polyvinyl alcohol, borax, trimethoxysilyl propyl methacrylate, nitrile rubber emulsion, epoxidized natural rubber latex, graphene oxide, oleamide, tetrasodium ethylene diamine tetraacetic acid, triethanolamine, borate, lauryl sodium sulfate, a proper amount of hydroxyl synthesized alcohol polyoxyethylene ether, a proper amount of methyl alcohol, a proper amount of nitric acid, a proper amount of hydrochloric acid, a proper amount of absolute ethyl alcohol and a proper amount of deionized water. The antirust agent prepared by the method can form a film on the surface of a workpiece, has the advantages of water proofing, oil proofing, cracking prevention, good heat resistance and good aging resistance to achieve excellent antirust anticorrosive effects, is convenient for later stripping, and is worthy of popularization.

Description

technical field [0001] The invention relates to the technical field of metal surface treatment agents, in particular to a nitrile rubber oleophobic peelable polymer antirust film. Background technique [0002] According to statistics, every year in the world, steel products with a total weight equivalent to 10-20% of the annual metal content cannot be used due to corrosion, rust and other reasons. Therefore, people have adopted various anti-rust methods to avoid rust. Cut your losses. There are various kinds of antirust agents, among which sodium nitrite has been favored and widely used because of its excellent antirust performance and low price. , a lot of research and development work has been carried out at home and abroad, and a variety of alkyl, alkoxy, halo, naphthoic acids and their derivatives, nitrobenzoic acids, and borates, borates and molybdenum have been prepared. A new type of water-soluble rust inhibitor that replaces sodium nitrite with materials such as ac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D129/04C09D5/20C09D5/08C09D7/12
CPCC09D129/04C08L2201/08C08L2205/035C09D5/08C09D5/20C09D7/61C09D7/62C09D7/65
Inventor 江海涛
Owner 江海涛
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products