Preparation method of thermal ageing resisting resin lens

A resin lens, anti-heat aging technology, applied in glasses/goggles, instruments, optics, etc., can solve problems such as corporate image decline, economic loss, etc., to prolong service life, enhance heat aging resistance, and not easy to yellow Effect

Active Publication Date: 2017-05-31
JIANGSU CONANT OPTICS +1
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When customers receive yellowed resin lenses, they will complain to the company and return the p

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0022] Example 1

[0023] A preparation method of a heat-aging resin lens, comprising the following steps: Step 1: Dissolving an antioxidant and a light stabilizer in a solvent, and after forming a transparent homogeneous solution, then adding it to a monomer, and at a temperature of 40° C. Dissolve the UV agent, then cool down to room temperature, add the initiator;

[0024] Step 2: Stir the raw materials for 2 hours at room temperature and the vacuum degree is -0.1MPa, filter through a 0.1μm filter element, add pigment blue and pigment red, continue stirring for 0.5 hours, and vacuumize 1 under the condition of vacuum degree -0.1MPa Hour;

[0025] Step 3: The static raw material is filtered again through 7μm filter paper, poured into the mold, and sealed in the mold with adhesive tape;

[0026] Step 4: Put the mold into the curing oven to heat up and cure once according to the corresponding curing curve;

[0027] Step 5: After the first curing, open the mold, take out the...

Example Embodiment

[0040] Example 2

[0041] A method for preparing a thermal aging resin lens, comprising the following steps: Step 1: Dissolving an antioxidant and a light stabilizer in a solvent; Dissolve the UV agent, then cool down to room temperature, add the initiator;

[0042] Step 2: Stir the raw materials for 4 hours at room temperature and a vacuum of -0.05MPa, filter with a 0.1 μm filter element, add pigment blue and pigment red, continue stirring for 2 hours, and vacuumize for 3 hours at a vacuum of -0.05MPa Hour;

[0043] Step 3: The static raw material is filtered again through 7μm filter paper, poured into the mold, and sealed in the mold with adhesive tape;

[0044] Step 4: Put the mold into the curing oven to heat up and cure once according to the corresponding curing curve;

[0045] Step 5: After the first curing, open the mold, take out the lens, and after cleaning, turn it into a lens of a certain size and diameter;

[0046] Step 6: Put the finished lens into the curing ...

Example Embodiment

[0058] Example 3

[0059] A method for preparing an anti-heat-aging resin lens, comprising the following steps: Step 1: Dissolving an antioxidant and a light stabilizer in a solvent, and after forming a transparent homogeneous solution, then adding it to a monomer, and cooling at 40-60° C. The UV agent is dissolved at the temperature, and then the initiator is added after cooling to room temperature;

[0060] Step 2: Stir the raw materials for 3 hours at room temperature and a vacuum degree of -0.07MPa, filter with a 0.1 μm filter element, add pigment blue and pigment red, continue stirring for 1.25 hours, and vacuumize for 2 hours at a vacuum degree of -0.107MPa Hour;

[0061] Step 3: The static raw material is filtered again through 7μm filter paper, poured into the mold, and sealed in the mold with adhesive tape;

[0062] Step 4: Put the mold into the curing oven to heat up and cure once according to the corresponding curing curve;

[0063] Step 5: After the first curing...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a thermal ageing resisting resin lens. The preparation method comprises the following steps: dissolving an antioxygen and a light stabilizer into a solvent; after forming a transparent homogeneous solution, adding the solution into a monomer and dissolving a UV (Ultraviolet) agent; cooling to room temperature and adding an initiator; stirring raw materials at room temperature and under a vacuum condition; after filtering, adding pigment blue and pigment red; continually stirring and vacuumizing under a vacuum condition; filtering the static raw materials again and pouring into a mold; sealing in the mold by utilizing an adhesive tape; putting the mold into a curing furnace, and heating according to a corresponding curing curve and curing for a first time; after finishing, opening the mold and taking out the lens; after washing, turning the lens with certain size and diameter; putting the turned lens into the curing furnace, and heating according to the corresponding curing curve and curing for a second time; after checking that the lens is qualified, packaging and storing. According to the preparation method disclosed by the invention, the thermal ageing resisting performance of the lens is enhanced and the lens does not easily become yellow; a condition that the color of the lens is abnormal is not easy to cause and the service life of the lens is prolonged; the requirement on the light transmission of the lens is met.

Description

technical field [0001] The invention relates to the technical field of resin lenses, in particular to a method for preparing a heat-aging-resistant resin lens. Background technique [0002] In today's society, eye problems are an increasingly serious social phenomenon, such as myopia, astigmatism, and hyperopia. Therefore, glasses have just become the basic tool for solving these problems, thereby become the requisite articles for use in people's daily life. And lens is as the most important component part of glasses, and the quality of its performance directly affects the use effect of glasses. Normally, the warehouse will guarantee a certain amount of inventory after the lens is produced, but if there is a problem with an order, it will cause a large amount of inventory retention. During the storage process, due to the effect of heat and oxygen, if coupled with the The initiator that has time to react, the resin lens will age and cause the color to turn yellow or fade. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F118/00C08F2/44G02C7/02
CPCC08F2/44C08F118/00G02C7/022
Inventor 王传宝严清波黄添鸟黄健
Owner JIANGSU CONANT OPTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap