Method for preparing pickering emulsion by using modified nanocellulose

A nanocellulose and modification technology, which is applied in the field of preparing Pickering emulsion by using modified nanocellulose, can solve the problems of ineffective stable emulsion, etc. Effect

Active Publication Date: 2019-04-09
SHAANXI UNIV OF SCI & TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since the surface of CNC has a large number of hydroxyl groups and is extremely hydrophilic, it cannot effectively stabilize the emulsion when it is used as a Pickering emulsion stabilizer. Therefore, it needs to be surface modified to make it have a certain degree of hydrophobicity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing pickering emulsion by using modified nanocellulose

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Take the amphiphilic block copolymer modified nanocellulose (MCNC) and grind it into powder to obtain the amphiphilic block copolymer modified nanocellulose powder;

[0043] Weigh the amphiphilic block copolymer-modified nanocellulose powder and deionized water at a mass ratio of 1:1000; weigh the amphiphilic block copolymer-modified nanocellulose powder and deionized water. Mix with water to form a mixed solution; place the mixed solution in an ultrasonic cell pulverizer with a power of 20% to disperse for 5 minutes to obtain a light yellow modified nanocellulose dispersion;

[0044] Weigh the liquid paraffin and add it to the modified nanocellulose dispersion, wherein the volume ratio of the liquid paraffin to the modified nanocellulose dispersion is 1:9 to form a mixture; wherein, the pH range of the modified nanocellulose dispersion is 1; the obtained mixture is placed in an ultrasonic cell pulverizer with a power of 20% for mixing and emulsification to obtain a sta...

Embodiment 2

[0046] Take the amphiphilic block copolymer modified nanocellulose (MCNC) and grind it into powder to obtain the amphiphilic block copolymer modified nanocellulose powder;

[0047] Weigh the amphiphilic block copolymer-modified nanocellulose powder and deionized water at a mass ratio of 1:100; weigh the amphiphilic block copolymer-modified nanocellulose powder and deionized water. Mix with water to form a mixed solution; place the mixed solution in an ultrasonic cell pulverizer with a power of 30% to disperse for 10 minutes to obtain a light yellow modified nanocellulose dispersion;

[0048]Weigh n-heptane and add it to the modified nanocellulose dispersion, wherein the volume ratio of n-heptane to the modified nanocellulose dispersion is 1:7 to form a mixture; wherein, the pH of the modified nanocellulose dispersion The value range is 7; the obtained mixture is mixed and emulsified in an ultrasonic cell pulverizer with a power of 30%, to obtain a stable Pickering emulsion.

Embodiment 3

[0050] Get amphiphilic block copolymer modified nanocellulose (MCNC) and grind it into powder to obtain amphiphilic block copolymer modified nanocellulose powder;

[0051] Weigh the amphiphilic block copolymer modified nanocellulose powder and deionized water respectively according to the mass ratio of 1:25; the weighed amphiphilic block copolymer modified nanocellulose powder and deionized water Mix with water to form a mixed solution; place the mixed solution in an ultrasonic cell pulverizer with a power of 30% and disperse for 20 minutes to obtain a light yellow modified nanocellulose dispersion;

[0052] Weigh methyl methacrylate and add it to the modified nanocellulose dispersion, wherein the volume ratio of methyl methacrylate to the modified nanocellulose dispersion is 1:1 to form a mixture; wherein, the modified nanocellulose The pH range of the dispersion liquid was 9; the obtained mixture was mixed and emulsified in an ultrasonic cell pulverizer with a power of 40%, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing Pickering emulsion by utilizing modified nano-crystalline cellulose. The method comprises the following steps: 1) taking the nano-crystalline cellulose modified with an amphiphilic segmented copolymer and grinding into powder, thereby acquiring the amphiphilic segmented copolymer modified nano-crystalline cellulose powder; 2) dispersing the amphiphilic segmented copolymer modified nano-crystalline cellulose powder acquired in the step 1) into deionized water, thereby forming modified nano-crystalline cellulose dispersion liquid; and 3) weighting an oily solvent, adding into the modified nano-crystalline cellulose dispersion liquid acquired in the step 2), and mixing and emulsifying, thereby forming stable Pickering emulsion. The method for preparing the Pickering emulsion by utilizing the modified nano-crystalline cellulose has the characteristics of less CNC dosage and low application cost.

Description

technical field [0001] The invention belongs to the technical field of material preparation methods, and in particular relates to a method for preparing Pickering emulsion by using modified nanocellulose. Background technique [0002] Pickering emulsion refers to the emulsion stabilized by using solid particles instead of traditional surfactants. The properties of Pickering emulsion have a great relationship with the wettability of particle surface. Too hydrophilic or too hydrophobic cannot form Pickering emulsion. Compared with the traditional surfactant-stabilized emulsion, Pickering emulsion has its own advantages: 1) It can significantly reduce the amount of emulsifier and save costs; 2) The toxic effect on the human body is far less than that of the surfactant; 3) It is harmful to the environment Friendly; 4) It is not easily affected by external environmental factors, and the emulsion has strong stability. Therefore, it has important application prospects in the field...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J3/05C08L87/00C08L1/02
CPCC08J3/05C08J2301/02C08J2387/00C08L1/02C08L87/005C08L2201/54
Inventor 周建华李艳南马建中
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com