A highly reflective degradable mulch film

A highly reflective and biodegradable technology, applied in the field of highly reflective and degradable mulch, can solve the problem of high environmental requirements for double-sided battery modules, and achieve the effects of suitability for industrial production, high water vapor barrier performance, and high reflectivity

Active Publication Date: 2020-07-14
HANGZHOU FIRST APPLIED MATERIAL CO LTD
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the problem that double-sided battery components have relatively high environmental requirements, the present invention provides a highly reflective and degradable plastic film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A highly reflective degradable mulch film
  • A highly reflective degradable mulch film
  • A highly reflective degradable mulch film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] In the manufacturing process, calculated by mass percentage, 60% polyethylene terephthalate modified material, 20% polyadipate / butylene terephthalate (PBAT), 15% polylactic acid, α - Diethoxyacetophenone 5% was homogeneously mixed by a high-speed mixer.

[0022] The polyethylene terephthalate modified material, calculated by mass percentage, includes the following components: high-density polyethylene terephthalate 65%, maleic anhydride grafted polyethylene 20%, starch 13% %, poly-p-phenylene terephthalamide 2%.

[0023] The reflective coating, calculated by mass percentage, includes the following components: 70% of acrylic resin, 10% of titanium dioxide, 10% of barium sulfate, 5% of curing agent, and 5% of adhesive.

[0024] The polyethylene terephthalate modified material, polyadipate / butylene terephthalate (PBAT), polylactic acid, and α-diethoxyacetophenone are uniformly mixed according to the above mass percentages to obtain The mixture is added into a casting mac...

Embodiment 2

[0026] In the manufacturing process, 70% polyethylene terephthalate modified material, 15% polyadipate / butylene terephthalate (PBAT), 10% polylactic acid, α -Hydroxyalkylbenzophenone 5% was uniformly mixed by a high-speed mixer.

[0027] The polyethylene terephthalate modified material, calculated by mass percentage, includes the following components: 75% high-density polyethylene terephthalate, 13% maleic anhydride grafted polyethylene, 20% starch %, poly-p-phenylene terephthalamide 2%.

[0028] The reflective coating, calculated by mass percentage, includes the following components: 75% of acrylic resin, 10% of titanium dioxide, 5% of barium sulfate, 5% of curing agent, and 5% of adhesive.

[0029] The polyethylene terephthalate modified material, polyadipate / butylene terephthalate (PBAT), polylactic acid, and α-hydroxyalkyl phenone are uniformly mixed according to the above mass percentages, and the obtained mixture Add it into a tape casting machine to cast a film to obt...

Embodiment 3

[0031] In the manufacturing process, calculated by mass percentage, polyethylene terephthalate modified material 65%, polyadipate / butylene terephthalate (PBAT) 20%, polylactic acid 10%, α - Diethoxyacetophenone 5% was homogeneously mixed by a high-speed mixer.

[0032] The polyethylene terephthalate modified material, calculated by mass percentage, includes the following components: 70% of high-density polyethylene terephthalate, 15% of maleic anhydride grafted polyethylene, and 11% of starch %, poly-p-phenylene terephthalamide 4%.

[0033] The reflective coating, calculated by mass percentage, includes the following components: 70% of acrylic resin, 10% of titanium dioxide, 10% of barium sulfate, 5% of curing agent, and 5% of adhesive.

[0034] The polyethylene terephthalate modified material, polyadipate / butylene terephthalate (PBAT), polylactic acid, and α-diethoxyacetophenone are uniformly mixed according to the above mass percentages to obtain The mixture is added into ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-reflective degradable mulching film. The reflective film comprises an upper protective layer, an adhesive layer, a reflective coating, a prism base layer and a lower protective layer from top to bottom. The upper surface of the lower protective layer is coated with the reflective coating. The reflective film covers the ground surface under an assembly, and accordingly the aim of reflecting sunlight which directly irradiates the ground to the back side of the two-side assembly is achieved. Adaptability between the two-side assembly and different environments is greatly improved. Materials in use are biodegradable materials, the cost is low, the degradation age limit is about 25 years, and the materials are highly matched with the service life of the assembly and do not pollute the environment. The prepared high-reflective degradable mulching film has high light reflectivity and high water vapor isolation performance, and also has outstanding advantages in the aspects of temperature use range, mechanical properties, outdoor weather resistance and the like.

Description

technical field [0001] The invention relates to the technical field of solar energy, in particular to a highly reflective and degradable mulch film that improves the adaptability of double-sided battery components. Background technique [0002] With the continuous development of photovoltaic technology, the improvement of ordinary solar cells has reached a bottleneck, and it is difficult to greatly improve their power generation efficiency, so relevant personnel have shifted their direction to double-sided cells. [0003] The double-sided battery module can use the reflected light from the back and the diffuse light from the surrounding environment. Under the same footprint, the double-sided battery module can have higher power generation efficiency. However, the use of double-sided battery components has great limitations. Due to the extremely low reflectivity of ordinary ground, it is difficult to use double-sided batteries in general areas. The emergence of highly reflec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A01G13/02A01G13/00B32B7/12B32B27/06B32B27/20B32B27/36B32B33/00B32B37/02B32B37/12B32B37/15B32B38/00C09D133/00C09D5/33C09D7/61
CPCA01G13/0262B32B7/12B32B27/06B32B27/20B32B27/36B32B33/00B32B37/02B32B37/12B32B37/15B32B38/00B32B2255/10B32B2255/26B32B2307/416B32B2307/7244C09D7/61C09D133/00
Inventor 邵佳俊王丹凤桑燕周光大林建华
Owner HANGZHOU FIRST APPLIED MATERIAL CO LTD