A-grade fireproof non-combustible polystyrene particle heat insulation board preparation method

A technology of polystyrene particles and polystyrene foam, which is applied in the field of thermal insulation boards, can solve the problems of poor fire resistance, low safety factor, and easy combustion, and achieves the effects of high fire rating, high fire resistance, and not easy to melt and drip.

Inactive Publication Date: 2017-06-30
JIANGSU ALUMEIGE NEW MATERIALS
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main material of polystyrene insulation board is polystyrene. In principle, polystyrene is composed of hydrocarbon elements, and because there is no flame retardant substance on the ou...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0017] A method for preparing a class A fireproof non-combustible polystyrene particle insulation board, the preparation method comprising the following steps:

[0018] Step 1, weighing the following components by weight: 80-120 parts of polystyrene foam particles, 300-400 parts of water glass, 400-600 parts of mixture, and 300-500 parts of water;

[0019] Step 2, the above-mentioned water glass and water are fully stirred evenly to prepare a mixed solution A;

[0020] Step 3, adding the obtained mixed solution A to the mixture and fully stirring to obtain a mixed solution B, which is an inorganic glue;

[0021] Step 4, adding polystyrene foam particles to the obtained mixture solution B and fully stirring to obtain mixture C;

[0022] In step five, the mixture C obtained in step four is pressed and molded through a pressing mold to obtain a grade A fire-proof and non-combustible polystyrene particle insulation board.

[0023] The water is pure water or deionized water. The...

Embodiment 1

[0028] A method for preparing a class A fireproof non-combustible polystyrene particle insulation board, the preparation method comprising the following steps:

[0029] Step 1, weighing the following components by weight: 80-120 parts of polystyrene foam particles, 300-400 parts of water glass, 400-600 parts of mixture, and 300-500 parts of water;

[0030] Step 2, the above-mentioned water glass and water are fully stirred evenly to prepare a mixed solution A;

[0031] Step 3, adding the obtained mixed solution A to the mixture and fully stirring to obtain a mixed solution B, which is an inorganic glue;

[0032] Step 4, adding polystyrene foam particles to the obtained mixture solution B and fully stirring to obtain mixture C;

[0033] In step five, the mixture C obtained in step four is pressed and molded through a pressing mold to obtain a grade A fire-proof and non-combustible polystyrene particle insulation board.

[0034] The water is pure water or deionized water. The...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thermal conductivityaaaaaaaaaa
Densityaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an A-grade fireproof non-combustible polystyrene particle heat insulation board preparation method. The preparation method includes the steps: firstly, weighing components by weight: 80-120 parts of polystyrene foam particles, 300-400 parts of water glass, 400-600 parts of mixed materials and 300-500 parts of water; secondly, sufficiently and uniformly stirring the water glass and the water to prepare into mixed solution A; thirdly, adding the obtained mixed solution A into the mixed materials to sufficiently and uniformly stir to prepare into mixture solution B which is inorganic glue; fourthly, adding the polystyrene foam particles into the obtained mixture solution B to sufficiently and uniformly stir to obtain a mixture C; fifthly, pressing the mixture C obtained in the fourth step by the aid of a pressing die. The A-grade fireproof non-combustible polystyrene particle heat insulation board prepared by the method is high in fire resistance and is not easy to combust and has heat insulation effect.

Description

technical field [0001] The invention relates to the technical field of thermal insulation boards, in particular to a method for preparing a Class A fireproof and non-combustible polystyrene particle thermal insulation board. Background technique [0002] Insulation board is a board used as insulation for the exterior wall of a building. In the application of thermal insulation engineering, most of them use organic polymer foam thermal insulation materials, but organic thermal insulation materials have a fatal flaw, that is, they are flammable. For example, polystyrene insulation board is the most widely used in insulation boards. Polystyrene insulation boards are widely used in the field of domestic building insulation due to their low thermal conductivity, high insulation effect, low bulk density, and convenient processability. The main material of polystyrene insulation board is polystyrene. In principle, polystyrene is composed of hydrocarbon elements, and because ther...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/26C04B111/28
CPCC04B28/26C04B2111/28C04B2201/20C04B2201/32C04B16/08C04B7/02C04B18/08C04B18/141
Inventor 陈建明
Owner JIANGSU ALUMEIGE NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap