A kind of preparation method of biomedical magnesium alloy wire

A biomedical and magnesium alloy technology, applied in the field of preparation of biomedical magnesium alloy wire, can solve the problems of multiple drawing passes, low deformation, and low plasticity of the wire, and achieve clear preparation principles, improved corrosion resistance, The effect of meeting the requirements of strength and plasticity

Active Publication Date: 2018-11-09
YANGZHOU UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to aim at the traditional magnesium alloy wire preparation method, the room temperature forming deformation is low, the drawing passes are many, the drawing process needs annealing to eliminate work hardening, and the plasticity of the wire is also low; Heating for a long time causes coarse grains, material mechanical properties and processing properties to decline, and it is difficult to completely dissolve the second phase in the matrix after long-term homogenization treatment, and it is difficult to obtain single-phase supersaturated solid solutions. Based on the preparation method of biomedical magnesium alloy wire, a single-phase supersaturated solid solution structure can be obtained, which can not only meet the requirements of strength and plasticity, but also make the material have better corrosion resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of biomedical magnesium alloy wire
  • A kind of preparation method of biomedical magnesium alloy wire
  • A kind of preparation method of biomedical magnesium alloy wire

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0020] A method for preparing a biomedical magnesium alloy wire, comprising the following steps:

[0021] (1) Metal magnesium and metal zinc are melted into liquid metal;

[0022] (2) Stirring and refining the liquid metal in step (1) to obtain refined liquid metal, mechanically stirring the molten metal for 3 to 5 minutes, then allowing the molten slag to float and then removing the slag;

[0023] (3) casting the refined liquid metal in step (2) into an alloy ingot;

[0024] (4) Perform homogenization heat treatment on the alloy ingot obtained in step (3) or directly perform equal-channel extrusion without heat treatment, the homogenization treatment temperature is 300-350 ° C, and the time is 2-6 hours; equal-channel angular extrusion The pressing temperature is between 200°C and 300°C, and the cumulative deformation is required to be over 400%;

[0025] (5) The material after medium channel extrusion in step (4) is processed into wire by multi-pass drawing. Before drawing...

Embodiment 1

[0029] like Figure 1~4 Shown, a kind of preparation method of biomedical magnesium alloy wire, Mg-6%wt.Zn alloy casts and there is bulk eutectic phase in the tissue after extrusion, such as figure 1 As shown, after the extruded sample was subjected to 200°C, 6-pass equal-channel extrusion treatment, the number of mesophases decreased, the size decreased, and a large number of fine precipitates were precipitated, such as figure 2 shown. After the extruded sample is drawn into a wire with a diameter of 0.3mm, there are a large number of mesophases distributed in bands in the microstructure, and the area between the mesophases distributed in bands appears due to uneven deformation. microcracks and holes, such as image 3 shown. However, the microstructure of the wire drawn after multi-channel equal channel extrusion has almost no second phase precipitation, the structure is uniform, and there are no cracks and holes, such as Figure 4 shown.

[0030] like Figure 5 As sho...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

A method for preparing biomedical magnesium alloy wire belongs to the technical field of metal materials. After melting magnesium and zinc, stirring and refining, casting them into alloy ingots, and then performing homogenization heat treatment on the alloy ingots, or without The heat treatment is directly carried out by equal-channel extrusion, and finally the magnesium-zinc alloy by equal-channel extrusion is processed into wire by multi-pass drawing. When the wire drawing is completed, the single-phase supersaturated solid solution structure is obtained, and its strength and elongation are higher than those obtained by direct drawing without equal channel extrusion, which not only meets the requirements of strength and plasticity, but also makes the material The corrosion resistance performance has been greatly improved.

Description

technical field [0001] The invention belongs to the technical field of metal materials, and relates to a preparation technology of a magnesium alloy, in particular to a preparation method of a magnesium alloy wire for biomedical use. Background technique [0002] Biomedical magnesium alloy wire, as a degradable material, has broad application prospects in the biomedical field. It can be used as a raw material for human implanted medical devices such as degradable anastomotic wire, degradable esophageal stent, and degradable bladder stent. According to the requirements of clinical use, biomedical magnesium alloy wire should have high room temperature strength and plasticity to meet the requirements of the support integrity of implanted materials in the human body, and at the same time, in order to prevent the implanted device from corroding too quickly in the human body It also requires biomedical magnesium alloy wire to have better biocorrosion corrosion resistance. Magnesi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C23/04C22C1/02C22F1/06
CPCC22C1/02C22C23/04C22F1/06
Inventor 严凯金朝阳程宏辉方双全费洪旗宋奎
Owner YANGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com