Plant-growing pervious concrete system for sludge recycling disposal and preparation method thereof

A permeable concrete and resource-based technology, applied in botany equipment and methods, ceramic products, plant cultivation, etc., can solve the problems of no vegetative concrete, achieve good social and economic benefits, eliminate environmental and safety problems, The effect of high nutrients

Active Publication Date: 2017-08-08
SAFECLEEN TECH
View PDF7 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, so far, there have been no research reports on the use of sludge as a raw material for the p...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Plant-growing pervious concrete system for sludge recycling disposal and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A plant-grown permeable concrete system that realizes sludge resource disposal is prepared by the following method:

[0041] (1) Weigh 40kg gravel, 3kg zeolite, 2kg vermiculite, 20kg ceramsite, 5kg porous silica microspheres and mix evenly, add 0.5kg water to wet the surface of the mixed material, obtain material I, and the average particle diameter of material I is 20mm;

[0042] (2) Fully mix the ordinary Portland cement and 4.5kg fly ash of material I and 20kg grade 42.5 grades to obtain material II, and the particle diameters of the ordinary Portland cement and fly ash of the 42.5 grades are 75μm square hole sieve residue ≤ 5%;

[0043] (3) Add 5kg of water to the material II again, add water while stirring to obtain the material III;

[0044] (4) The material III is poured out, inserted and pounded into shape, and the matrix material I with a porosity of 30% is obtained after 3 days of curing, which can be used as the matrix material of the vegetation permeable c...

Embodiment 2

[0052] A plant-grown permeable concrete system that realizes sludge resource disposal is prepared by the following method:

[0053] (1) Take by weighing 20kg gravel, 5kg zeolite, 50kg ceramsite and mix evenly, add 0.5kg water to wet the surface of the mixed material, obtain material I, and the average particle diameter of material I is 30mm;

[0054] (2) Material I is fully mixed with 15kg grade 42.5 ordinary Portland cement and 8kg fly ash to obtain material II. The particle diameters of the 42.5 grade ordinary Portland cement and fly ash are 75 μm Square hole sieve residue ≤ 5%;

[0055] (3) Add 1.5kg of water to the material II again, add water while stirring to obtain the material III;

[0056] (4) Pour out the material III, insert and pound it into shape, and obtain a matrix material I with a porosity of 35% after 3 days of curing, which can be used as a matrix material for a plant-growing permeable concrete system;

[0057] (5) Screening the sludge from dredging to rem...

Embodiment 3

[0064] A plant-grown permeable concrete system that realizes sludge resource disposal is prepared by the following method:

[0065] (1) Take by weighing 30kg gravel, 3kg vermiculite, 30kg ceramsite, 2kg porous silica microspheres and mix uniformly, add 0.8kg water to wet the surface of the mixed material, obtain material I, and the average particle diameter of material I is 35mm; ;

[0066] (2) Material I is fully mixed with 18kg grade 42.5 ordinary Portland cement, 2kg desulfurized gypsum, 8kg coal gangue powder and 2kg acidic slag micropowder to obtain material II, the 42.5 grade ordinary Portland cement, The particle size of desulfurized gypsum, coal gangue powder and acid slag powder is 75 μm square hole sieve ≤ 5%;

[0067] (3) Add 4.2kg of water to the material II again, add water while stirring to obtain the material III;

[0068] (4) The material III is poured out, inserted and pounded into shape, and the matrix material I with a porosity of 36% is obtained after cur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Login to view more

Abstract

Belonging to the field of sludge recycling disposal, the invention in particular relates to a plant-growing pervious concrete system for sludge recycling disposal and a preparation method thereof. The method includes: fully mixing rubble, zeolite, vermiculite, ceramsite, porous silicon dioxide microspheres, a cementing material, an acidic admixture and water, and conducting insertion tamping molding to obtain a base material I; carrying out sieving and dehydration on sludge to obtain a slurry II; fully mixing the slurry II with a permeable conditioning agent and a fluidity conditioning agent, and filling the base material I with the obtained mixture so as to obtain a base material II; fully mixing the slurry with a curing agent and a modifier, and performing curing, thus obtaining a material IV; covering the surface of the base material II with a material IV, and sowing grass seeds thereon, thus obtaining the plant-growing pervious concrete system. The invention aims at sludge recycling disposal, and realizes sludge recycling disposal. The obtained plant-growing pervious concrete system can be widely applied to in rive bank slope protection projects, road edge protection projects, and sponge city construction projects.

Description

technical field [0001] The invention belongs to the fields of sludge resource disposal, ecological concrete, environmental protection materials and permeable materials, and in particular relates to a plant-grown permeable concrete system for realizing sludge resource disposal and a preparation method thereof. Background technique [0002] Silt is a floc structure formed by the deposition of clay minerals, animal and plant humus, fine sand and other fine particles under the action of slow flowing water. For the purposes of dredging and navigation, environmental protection and water quality improvement, large-scale dredging of rivers, lakes and rivers has been carried out in various places, resulting in a large amount of silt. Ordinary sludge has the characteristics of high water content, low strength, easy muddying, high humus content, and some heavy metals exceeding agricultural standards. These characteristics lead to the treatment and disposal of sludge, which has graduall...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B38/08C04B28/04C04B28/34C04B28/14C04B41/70A01G1/00
CPCA01G20/00C04B28/04C04B28/144C04B28/34C04B38/08C04B41/52C04B41/70C04B2111/00284C04B14/02C04B14/047C04B14/202C04B18/027C04B20/0036C04B14/062C04B22/002C04B18/08C04B41/5035C04B41/5037C04B41/4598C04B41/46C04B41/5014C04B41/5024C04B41/50C04B22/145C04B18/12C04B18/141C04B41/4803
Inventor 刘啸赵皇孙涛张峻清李立马彩凤徐民主陈益人
Owner SAFECLEEN TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap