Elliptical machine light cover surface silica gel and preparation method thereof

An elliptical machine and bright light technology, applied in dyeing, textiles and papermaking, etc., can solve the problems of poor rubber strength, brittleness, slow defoaming, etc., and achieve rapid leveling, fast defoaming and leveling, and good physical properties Effect

Inactive Publication Date: 2017-09-05
广东省良展有机硅科技有限公司
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, ordinary hand-printed silica gel used for machine-printed cover adhesives has the problem of slow defoaming. Although some bright cover products defoam quickly, the strength of the rubber is poor and brittle.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Embodiment 1, a bright cover silica gel for an elliptical machine provided in this embodiment is composed of the following raw materials in parts by mass: 100 parts of vinyl polysiloxane, 10-15 parts of white carbon black, 0.15-0.2 parts Inhibitor, 0.3-0.5 parts of platinum catalyst, 11-12 parts of hydrogen-containing silicone oil and 0.2-0.5 parts of fluorocarbon-based silicone oil.

[0025] The vinyl polysiloxane is a polydiorganosiloxane containing two or more vinyl groups.

[0026] The vinyl polysiloxane is double-terminated vinyl polydimethylsiloxane, the viscosity is 3000mPa.s-5000mP.s, and the vinyl content is preferably 0.13%.

[0027] The inhibitor is two kinds of methyl butynol, ethynyl cyclohexanol, phenyl butynol and propyl butynol.

[0028] The inhibitor is a compound of propyl butynol and methyl butynol.

[0029] The white carbon black is surface-treated fumed white carbon black.

[0030] The platinum catalyst is H 2 PtCl 6 isopropanol solution, H 2 ...

Embodiment 2

[0040] Embodiment 2, a kind of bright cover silica gel for elliptical machine that this embodiment provides, its raw material is composed of: 100g vinyl polysiloxane (ViMe 2 Si(Me 2 SiO) n SiMeVi), 15g fumed silica, 0.3g platinum catalyst, 0.5g fluorocarbon-based silicone oil, 11g hydrogen-containing silicone oil, 0.1g propyl butynol and 0.05g methyl butynol.

[0041] Add 100 g of vinyl polysiloxane (ViMe 2 Si(Me 2 SiO) n SiMeVi), then add 15g of surface-treated fumed silica, knead at 160°C for 1H until the kneading is uniform, cool, then put it into a planetary mixer, then add 0.3g of platinum catalyst, 0.5g of fluorocarbon-based silicone oil, Mix for 30 minutes and apply vacuum to obtain the A component. Then put 11g of hydrogen-containing silicone oil, 0.1g of propyl butynol, and 0.05g of methyl butynol into a disperser, and disperse for 15 minutes to obtain component B. When in use, components A and B are mixed evenly, and then they can be used for glue screen printi...

Embodiment 3

[0042] Embodiment 3, a kind of glossy silica gel for an elliptical machine provided in this embodiment, its raw material composition is as follows:

[0043] 100g vinyl polysiloxane (ViMe 2 Si(Me 2 SiO) n SiMeVi), 10g fumed silica, 0.3g platinum catalyst, 0.2g fluorocarbon-based silicone oil, 12g hydrogen-containing silicone oil, 0.1g propyl butynol and 0.1g methyl butynol.

[0044] Add 100 g of vinyl polysiloxane (ViMe 2 Si(Me 2 SiO) n SiMeVi), then add 10g of surface-treated fumed silica, knead at 160°C for 1H until kneaded evenly, cool, then put it into a planetary mixer, add 0.3g of platinum catalyst, 0.2g of fluorocarbon-based silicone oil, Mix for 30 minutes and apply vacuum to obtain the A component. Then put 12g of hydrogen-containing silicone oil, 0.1g of propyl butynol, and 0.1g of methyl butynol into a disperser, and disperse for 15 minutes to obtain component B. When in use, components A and B are mixed evenly, and then they can be used for glue screen printi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses elliptical machine light cover surface silica gel and a preparation method thereof. The light cover surface silica gel comprises, by weight, 100 parts of vinyl polysiloxane, 10-15 parts of white carbon black, 0.15-0.2 part of inhibitors, 0.3-0.5 parts of platinum catalysts, 11-12 parts of hydrogen-containing silicone oil and 0.2-0.5 part of fluoroalkyl silicone oil. By the aid of a compound comprising base gel, the hydrogen-containing silicone oil, propargyl alcohol and methyl propargyl alcohol, the content of vinyl in the base gel is 0.13%, the content of hydrogen in the hydrogen-containing silicone oil is 0.2%, the surfaces of silica gel materials are dried in about 5S at the temperature of about 50 DEG C, operating time is longer than 4H, and the silica gel meets elliptical machine operating requirements. The invention further discloses a preparation method of the elliptical machine light cover surface silica gel. The viscosity of the cover surface silica gel prepared by the method is about ten thousands, defoaming and leveling are the silica gel are accelerated, the silica gel cannot be embrittled, is suitable for elliptical machine operation and good in physical performance and has long operation time, high vulcanization, defoaming and leveling speed.

Description

technical field [0001] The invention relates to the field of screen silica gel printing, in particular to a bright cover silica gel for an elliptical machine and a preparation method of the bright cover silica gel for an elliptical machine. Background technique [0002] Printed silicone is a special liquid silicone that can be firmly adhered to the surface of textiles by screen printing. [0003] In the prior art, the current printing silica gel is generally only suitable for the fingerprint environment, with low work efficiency, high labor cost and low stability of product performance. With the development of mechanization and intelligence, the printing industry urgently needs printing silica gel suitable for printing on elliptical machines. Adopting the method of machine printing, there are some technical problems in the printing silica gel currently on the market. For example, ordinary hand-printed silica gel used for machine-printed cover adhesives has the problem of s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06P1/52D06P1/651D06P1/673
CPCD06P1/5292D06P1/65118D06P1/67383
Inventor 王志良
Owner 广东省良展有机硅科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap