A kind of preparation method of soft magnetic composite powder core

A soft magnetic composite, powder core technology, applied in the manufacture of inductors/transformers/magnets, magnetic materials, magnetic objects, etc. High saturation magnetic induction, low eddy current loss, and the effect of improving molding density

Inactive Publication Date: 2018-06-15
HEBEI UNIV OF TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is: provide a kind of preparation method of soft magnetic composite powder core, is based on amorphous nanocrystalline Fe a Si b m c B d Cu e Powder is the main powder, and the auxiliary powder composed of at least one of water atomized Fe powder, gas atomized FeNi50 powder and gas atomized FeSi3.5 powder is evenly mixed according to the set mass ratio, and the mixed powder is mixed with passivation solution and The insulating agent forms a passivation insulating film on the surface, and then undergoes compression molding and annealing process to obtain a soft magnetic composite powder core with excellent comprehensive soft magnetic properties, which overcomes the low saturation magnetic induction of the soft magnetic powder core produced by the prior art , large coercive force, large loss and reduced effective permeability at high frequencies

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of soft magnetic composite powder core
  • A kind of preparation method of soft magnetic composite powder core
  • A kind of preparation method of soft magnetic composite powder core

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] The first step is to prepare amorphous and nanocrystalline Fe 74.5 Si 13.5 Nb 2.5 B 8.5 Cu 1 Main Powder:

[0044] Calculate the element composition formula Fe according to the atomic percentage 74.5 Si 13.5 Nb 2.5 B 8.5 Cu 1 The mass percent of the constituent elements in the element, weigh the required amount of component raw materials according to the calculated mass percent of the element: pure iron, pure silicon, ferro-niobium, ferro-boron and pure copper, wherein the mass fraction of niobium in ferroniobium 66.5%, and the mass fraction of boron in ferroboron is 17.4%, thus completing the preparation of raw materials, smelting the raw materials of the above components evenly and spraying out an amorphous thin strip with a thickness of 30 μm and a width of 10 mm in the atmospheric environment. Thin strip in vacuum -1 In the heat treatment furnace of Pa, the temperature is heated from room temperature to 480°C at a heating rate of 1°C / min, and then heated fr...

Embodiment 2

[0063] In this embodiment, the amorphous nanocrystalline Fe 74.5 Si 13.5 Nb 2.5 B 8.5 Cu 1 The mass fraction of the main powder is changed to 60%, the mass fraction of the gas-atomized FeNi50 powder is changed to 40%, and other processes are the same as in Example 1.

[0064] The soft magnetic properties and mechanical properties of the soft magnetic composite powder core prepared in this example are shown in Table 1.

Embodiment 3

[0066] The first step is to prepare amorphous and nanocrystalline Fe 70 Si 15.5 Nb 2 Mo 1.5 B 10 Cu 1 Main Powder:

[0067] Calculate the element composition formula Fe according to the atomic percentage 70 Si 15.5 Nb 2 Mo 1.5 B 10 Cu 1 The mass percentage of the constituent elements in the element, weigh the required amount of component raw materials according to the calculated mass percentage of the element: pure iron, pure silicon, ferro-niobium, ferro-molybdenum, ferro-boron and pure copper, wherein niobium in ferroniobium The mass fraction of boron in ferro-boron is 66.5%, the mass fraction of boron in ferro-molybdenum is 17.4%, and the mass fraction of molybdenum in ferro-molybdenum is 50%, thus completing the preparation of raw materials, smelting the raw materials of the above components evenly and spraying them out in the atmosphere An amorphous thin strip with a thickness of 40 μm and a width of 5 mm, the thin strip is vacuumed -1 In the heat treatment fur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The preparation method of a kind of soft magnetic composite powder core of the present invention relates to the magnet that distinguishes according to used magnetic material, is main powder with amorphous nano crystal FeaSibMcBdCue powder, and water atomization Fe powder, gas atomization FeNi50 powder and gas atomization FeSi3 .5 Auxiliary powders composed of at least one of the powders are uniformly mixed according to the set mass ratio, and the mixed powder is used to form a passivation insulating film on the surface of the mixed powder with a passivation liquid and an insulating agent, and then subjected to compression molding and annealing processes to produce A soft magnetic composite powder core with excellent comprehensive soft magnetic properties is obtained, which overcomes the defects of low saturation magnetic induction intensity, large coercive force, large loss and reduced effective permeability at high frequencies in the soft magnetic powder core prepared by the prior art .

Description

technical field [0001] The technical scheme of the invention relates to magnets classified according to the magnetic materials used, in particular to a method for preparing a soft magnetic composite powder core. Background technique [0002] With the rapid development of the electronics and electrical industry, new requirements have been put forward for the performance of electrical devices such as switching power supplies. So far, magnetic powder cores with stable effective permeability, low loss and high quality factor have been used at frequencies from 50Hz to 100kHz. Not perfect. Yoshizawa et al. (Y.Yoshizawa, S.Oguma, K.Yamauchi. New Fe-based soft magnetic alloys composed of ultrafine grain structure[J]. Journal of Applied Physics.1988,64:6044-6046.) of Hitachi in 1988 Invented Finemet, an amorphous and nanocrystalline material with excellent soft magnetic properties, with a saturation magnetic induction of 1.2T and an initial permeability of 10 4 ~10 5 And the advan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01F41/02H01F1/147C22C45/02B22F1/00
CPCB22F1/0003H01F1/14766H01F41/0246C22C45/02B22F1/145
Inventor 孙继兵杜帅龙李英殷福星张磊
Owner HEBEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com