Multifunctional high-strength composite fabric coating agent, coating, and preparation method and application of multifunctional high-strength composite fabric coating agent

A composite fabric, multi-functional technology, applied in the field of materials, can solve the problems of wear resistance, high strength, waterproof and moisture permeability, achieve good burst resistance, suitable for large-scale promotion and application, and enhance the effect of bonding force

Inactive Publication Date: 2017-10-17
JIANGNAN UNIV
View PDF4 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing fabric coatings cannot meet the higher performance requirements of high-end tents, toys, travel bags, express packages, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multifunctional high-strength composite fabric coating agent, coating, and preparation method and application of multifunctional high-strength composite fabric coating agent
  • Multifunctional high-strength composite fabric coating agent, coating, and preparation method and application of multifunctional high-strength composite fabric coating agent
  • Multifunctional high-strength composite fabric coating agent, coating, and preparation method and application of multifunctional high-strength composite fabric coating agent

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0047] In some embodiments, the preparation method includes: adding the enhancer, synergist, and solvent into the reactor at a mass ratio of 1:0.025-2.5:20-50 and reacting at 20-100°C for 1- After 10 hours, after the reaction product is cooled, the solid matter is separated (for example, by vacuum filtration, etc.) and dried at room temperature for 10-30 hours, and then milled and sieved to finally obtain a reinforcing agent with active groups on the surface.

[0048] In some embodiments, the synergist includes a silane coupling agent and / or a polymer compound. Since the reinforcing agent has undergone surface modification treatment, it has -OH, -NH 3 and other active functional groups, which enhance the binding force between the coating and the fabric, thereby greatly improving the strength of the coating compared with the prior art.

[0049] Preferably, the silane coupling agent includes 3-aminopropyltrimethoxysilane, γ-(2,3-glycidoxy)propyltriethoxysilane, γ-methacryloxypr...

Embodiment 1

[0067] (1) Add 9g nanometer tungsten carbide (particle size about 200nm), 22.5g 3-aminopropyltrimethoxysilane and 450g ethanol into the reaction kettle and react at 100°C for 10h. After the reaction product is cooled, filter it under reduced pressure The product was dried at room temperature for 30 h, then milled and sieved to obtain a surface with a large amount of -NH 3 nano tungsten carbide.

[0068] (2) Weigh 15 g of polyurethane resin and 30 g of xylene respectively in a 250 mL beaker, and stir for 40 min with a magnetic stirrer at 1500 rpm.

[0069] (3) add 9g surface to have a large amount of-NH in the dispersion liquid that step (2) makes 3 Nano-tungsten carbide, 7.5g isophorone, 6g sodium lauryl sulfate, 4.5g dodecyl alcohol ester, 6g pentaerythritol fatty acid ester, 4.5g nano-zinc oxide, then stirred with a magnetic stirrer at 2000rpm for 20min to obtain a stable The dispersion liquid, promptly obtains described multifunctional high-strength composite fabric coati...

Embodiment 2

[0073] (1) Add 2g of black gemstone (particle size about 50nm), 0.5g of polyacrylic acid and 90g of deionized water into the reactor and react at 60°C for 2 hours. After the reaction product is cooled, filter the product under reduced pressure and dry it at room temperature 14h, followed by grinding and sieving to finally obtain black gemstones with a large amount of -COOH on the surface;

[0074] (2) Weigh 20g of polyacrylic resin, 50g of n-butanol and 50g of xylene in a 250mL beaker respectively, and stir for 45min with a magnetic stirrer at 1500rpm;

[0075] (3) Add 2g of black gemstone with a large amount of -COOH on the surface, 0.3g of octyltriethoxysilane, 0.20g of polyacrylamide, 0.15g of ethylene glycol monopropylene to the dispersion liquid prepared in step (2). Ether, 3g of triethanolamine ammonium stearate, 1g of nano-copper oxide, and then stirred with a 2000rpm magnetic stirrer for 20min to obtain a stable dispersion, that is, to obtain the multifunctional high-s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a multifunctional high-strength composite fabric coating agent, a coating, and a preparation method and application of the multifunctional high-strength composite fabric coating agent. The multifunctional high-strength composite fabric coating agent comprises resin, a reinforcing agent of which the surface is provided with active groups, a difunctional dispersing agent, a levelling agent, a film forming agent, a softening agent, an antibacterial agent, a solvent and the like, wherein the reinforcing agent is subjected to surface modifying treatment and is provided with the active functional groups, such as -OH and -NH3. The fabric coating agent provided by the invention is convenient to apply, high in acting speed and stable in characteristics, and is basically suitable for the surfaces of fabrics made of any materials; moreover, the fabric which is treated by the fabric coating agent has very great tensile breaking force, excellent bursting performance and tearing performance, high waterproofing and moisture-penetration performance and antibacterial performance, and high adhesion force, can also be scraped and coated, rolled and coated, calendered or soaked repeatedly; and moreover, the preparation method of the coating agent is mature in process and low in production cost, and is suitable for large-scale popularization and application.

Description

technical field [0001] The invention specifically relates to a multifunctional high-strength composite fabric coating agent, a multifunctional high-strength composite fabric coating, a preparation method and application thereof, and belongs to the field of material technology. Background technique [0002] Fabric coating is a polymer compound that is uniformly coated on the surface of the fabric. It forms one or more layers of film on the surface of the fabric through adhesion, which can not only improve the appearance and style of the fabric, but also increase the function of the fabric, making the fabric have high strength, waterproof, water pressure resistance, breathable and moisture-permeable, flame-retardant and waterproof. Special functions such as pollution and shading reflection. [0003] Most of the fabrics currently on the market have low strength. The functional finishing of fabrics, that is, coating technology, can meet the main performance requirements of fab...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D133/00C09D161/06C09D179/04C09D5/14C09D7/12D06N3/00D06N3/04D06N3/12D06N3/14
CPCC09D133/00C09D161/06C09D175/04C09D179/04D06N3/0006D06N3/0036D06N3/0061D06N3/0063D06N3/042D06N3/12D06N3/14C09D5/14C08K3/14C08K3/34C08K3/38C08K5/103C08K2003/385C08K2201/011C08K2003/2227C08K2003/2248C08K2003/2296C08K9/06C08K9/04C08K9/08C08K13/06C08L2205/02D06N2209/1671D06N2209/103D06N2209/128D06N2201/045C08L33/26C08K3/22C08L33/00C08K3/28D06P1/44D06N2201/0245D06N2201/042D06N2201/06D06M11/74D06M11/82D06M11/58D06M11/44D06M15/263D06M15/564D06M2101/06D06M2101/32D06M2101/12D06M11/13D06M2101/28D06M16/00D06M13/513D06M11/42D06M11/46D06M11/70D06M11/78D06M15/41D06M15/55D06M15/59D06M23/10D06M2101/04
Inventor 张丹黄婵娟郑磊龙柱
Owner JIANGNAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com