Zisha boiled water without frying pot

A technology of boiling water and purple sand, which is applied to water boiling utensils, other household utensils, clay products, etc., can solve the problems of poor sudden change, easy to explode and crack, and limited use range, and achieve good sudden change and excellent explosion resistance. The effect of action

Active Publication Date: 2020-11-27
宜兴市凤凰陶瓷厂
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, Yiju Zisha teapots produced by Zisha ceramics have poor sudden change, are not resistant to high temperature, are easy to explode and crack, and are limited in scope of use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The Zisha pot for boiling water without frying according to the present invention comprises the following components by weight percentage,

[0038] (1) Zisha mud 49.8%;

[0039] (2) White clay 12.6%;

[0040] (3) Talc 1.8%;

[0041] (4) Burnt Gems 11%;

[0042] (5) Barium titanate 2.5%;

[0043] (6) Iron ore 4%;

[0044] (7) Volcanic rock 9%;

[0045] (8) Spodumene 9%;

[0046] Its preparation method comprises the following steps,

[0047] (1) Mix talc, coke gem, barium titanate, iron ore, volcanic rock and spodumene evenly, calcined at 1100°C and grind into 60 mesh powder;

[0048] (2) Add 75-mesh purple sand mud and white mud, put it into a mixer and stir evenly, then add water with 35% of the total of the above mud, stir evenly again, and stale for 3 days;

[0049] (3) Put the stale mud into a vacuum machine to make a lump of mud and then age it for 13 days, so that the water content in the mud is 22%;

[0050] (4) Put the mud into the vacuum machine again t...

Embodiment 2

[0057] The Zisha pot for boiling water without frying according to the present invention comprises the following components by weight percentage,

[0058] (1) Zisha mud 50%;

[0059] (2) white clay 13%;

[0060] (3) Talc 2%;

[0061] (4) Burnt Gems 10%;

[0062] (5) Barium titanate 3%;

[0063] (6) Iron ore 4%;

[0064] (7) Volcanic rock 8%;

[0065] (8) Spodumene 10%;

[0066] Its preparation method comprises the following steps,

[0067] (1) Mix talc, coke gemstone, barium titanate, iron ore, volcanic rock and spodumene evenly, calcined at 1150°C and grind into 60-mesh powder;

[0068] (2) Add 75-mesh purple sand mud and white mud, put it into a mixer and stir evenly, then add water with 36% of the total of the above mud, stir evenly again, and stale for 3 days;

[0069] (3) Put the stale mud into a vacuum machine to make a lump of mud and then age it for 12 days, so that the water content in the mud is 25%;

[0070] (4) Put the mud into the vacuum machine again to ...

Embodiment 3

[0077] The Zisha pot for boiling water without frying according to the present invention comprises the following components by weight percentage,

[0078] (1) Zisha mud 51%;

[0079] (2) white mud 14%;

[0080] (3) Talc 2.6%;

[0081] (4) Burnt Gems 11%;

[0082] (5) Barium titanate 3.5%;

[0083] (6) Iron ore 3.2%;

[0084] (7) Volcanic rock 8.5%;

[0085] (8) Spodumene 8.5%;

[0086]Its preparation method comprises the following steps,

[0087] (1) Mix talc, coke gemstone, barium titanate, iron ore, volcanic rock and spodumene evenly, calcined at 1190°C and grind into 60-mesh powder;

[0088] (2) Add 75-mesh purple sand mud and white mud, put it into a mixer and stir evenly, then add water with 39% of the total of the above mud, stir evenly again, and stale for 3 days;

[0089] (3) Put the stale mud into a vacuum machine to make a lump of mud and then age it for 14 days, so that the water content in the mud is 28%;

[0090] (4) Put the mud into the vacuum machine ag...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a dark-red enameled pot for boiling water without cracking. The pot comprises arenaceous clay, white mud, talc, flint clay, barium titanate, iron ore, a volcanic rock and spodumene. A manufacturing method comprises the steps of mixing the talc, the flint clay, the barium titanate, the iron ore, the volcanic rock and the spodumene evenly, burning and grinding the mixture into 60mesh powder; adding the arenaceous clay and the white mud, stirring evenly, adding water, stirring evenly again and staling; putting the staled mud into a vacuum machine for smelting into lumps of clay and then staling; putting the lumps of clay into the vacuum machine again for pugging; making a blank and naturally drying; carrying out once firing, wherein the firing temperature is 1120-1180 DEG C, carrying out naturally cooling, drawing and checking the blank; carrying out opening trimming of a finished product; and carrying out second firing, slowly raising the temperature to 600 DEG C and then quickly raising the temperature to 1180-1190 DEG C at the speed of 80 DEG C / h and carrying out heat-insulated firing and natural cooling and molding. The dark-red enameled pot is good in sudden change, the pH value of boiled water is about 8.5 and the water is a small molecule group.

Description

technical field [0001] The invention relates to a kettle and a preparation method thereof, in particular to a purple sand kettle and a preparation method thereof. Background technique [0002] Yixing purple clay pottery has a history of several thousand years. It is a unique ceramic utensil in China that combines appreciation and practicality. It has a unique position in the history of Chinese ceramic development and is a wonderful flower in Chinese pottery culture. At present, the purple sand teapots produced by Yiju Zisha ceramics have poor sudden change, are not resistant to high temperatures, are explosive and easy to crack, and their range of use is limited. Contents of the invention [0003] Purpose of the invention: the purpose of the present invention is to overcome the deficiencies in the prior art, to provide a kind of purple clay pot with good sudden change, the pH value of the fired water is about 8.5 and small molecular groups without frying. [0004] Technic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13C04B33/32A47J27/21A47J36/04
CPCA47J27/21A47J36/04C04B33/13C04B33/32C04B2235/3203C04B2235/3215C04B2235/3236C04B2235/3472C04B2235/656C04B2235/6562C04B2235/6567C04B2235/661
Inventor 江小东江华
Owner 宜兴市凤凰陶瓷厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap