480MPa-grade galvanized strip steel and production method thereof
A production method and 480mpa technology, applied in hot dip plating, coating, metal material coating process, etc., can solve the problems of extremely high requirements for rapid cooling capacity, high cost of precious alloys, and no applicability, so as to improve The effect of solid solution strengthening, reducing the difficulty of production control, and reducing the probability of inclusion defects
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example
[0016] Example 1-13: The final chemical composition of the 480MPa grade galvanized steel strip and the process conditions of the production method are as follows.
[0017] (1) The galvanized steel strip is prepared by converter smelting, LF refining, continuous casting, hot rolling, cold rolling, continuous annealing, and galvanizing processes. The chemical composition of the castings after the continuous casting process is shown in Table 1:
[0018] Table 1: Chemical composition of castings
[0019]
[0020] (2) Hot rolling process:
[0021] During the hot rolling process, the solid solution and precipitation of the second phase particles, the deformation and recrystallization of austenite, and the transformation of ferrite occur. Therefore, hot rolling is an important part of quality control; through heating temperature, final rolling temperature and coiling The joint setting of temperature and the control of the front cooling after finishing rolling can lead to the precipitation of...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap