Self-luminous pavement material and preparation method

A technology of self-luminous materials and pavement materials, applied in the field of materials used in road engineering, can solve the problems of limited application scope, application limitations, long time span at night, etc. long span effect

Inactive Publication Date: 2017-11-10
SHANGHAI PUDONG ROAD & BRIDGE GRP CO LTD +1
View PDF9 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although there are many researches and achievements on self-illuminating pavement materials, the application of these technologies has limitations:
[0005] Because stone aggregates must be mixed in, the scope of application of these materials is limited, so that the corresponding technology can only be applied to new road pavements or pavements without elevation restrictions. For pavements that have been built and have elevation restrictions, these technologies cannot be used
[0006] (2), the self-illumination effect is limited
[0007] The time span of continuous self-illumination after light storage is between 1h-8h, which cannot meet the needs of areas with poor ambient light conditions and long time spans at night

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The mass fraction of the self-luminous material is 25%; the mass fraction of the epoxy resin is 45%; the mass fraction of the curing agent is 15%; and the mass fraction of the diluent is 15%.

[0031] Among them, the self-luminous material is one of the aluminate light storage type or sulfide light storage type self-luminous material system, the size is 50 mesh, and the afterglow time is 12 hours.

[0032] The epoxy content of the epoxy resin is 220±5g / eq, the hydrolyzable chlorine content is 0.21%, the inorganic chlorine content is 0.008%, the volatile matter content is 0.27%, the Gardner color is 2, and it is colorless and transparent. The softening point is 25°C.

[0033] The curing agent is an acid anhydride curing agent, colorless, transparent, and odorless, with a volatile content of 0.33%, a halogen content of 4ppm, a Gardner color of 2, and a melting point of -28°C.

[0034] The diluent is a halogen-free, odorless, colorless transparent liquid with a halogen co...

Embodiment 2

[0036] The mass fraction of the self-luminous material is 30%; the mass fraction of the epoxy resin is 40%; the mass fraction of the curing agent is 15%; and the mass fraction of the diluent is 15%.

[0037] Among them, the self-luminous material is one of the aluminate light-storage type or sulfide light-storage type self-luminous material system, the size is 30 mesh, and the afterglow time is 10h.

[0038] The epoxy content of epoxy resin is 200±5g / eq, the content of hydrolyzable chlorine is 0.25%, the content of inorganic chlorine is 0.010%, the content of volatile matter is 0.5%, the color of Gardner method is 1, and it is colorless and transparent. The softening point is 10°C.

[0039] The curing agent is an acid anhydride curing agent, colorless, transparent and odorless, with a volatile content of 0.5%, a halogen content of 3ppm, a Gardner color of 1, and a melting point of -20°C.

[0040] The diluent is a halogen-free, odorless, colorless transparent liquid with a hal...

Embodiment 3

[0042] The mass fraction of the self-luminous material is 30%; the mass fraction of the epoxy resin is 45%; the mass fraction of the curing agent is 10%; and the mass fraction of the diluent is 15%.

[0043] Among them, the self-luminous material is one of the aluminate light storage type or sulfide light storage type self-luminous material system, the size is 100 mesh, and the afterglow time is 20h.

[0044] The epoxy content of the epoxy resin is 245±5g / eq, the hydrolyzable chlorine content is 0.1%, the inorganic chlorine content is 0.005%, the volatile matter content is 0.2%, the Gardner color is 0.5, and it is colorless and transparent. The softening point is 20°C.

[0045] The curing agent is an acid anhydride curing agent, colorless, transparent, and odorless, with a volatile content of 0.25%, a halogen content of 3.5ppm, a Gardner color of 1.5, and a melting point of -30°C.

[0046] The diluent is a halogen-free, odorless, colorless transparent liquid with a halogen co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
sizeaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a self-luminous pavement material and a preparation method. The self-luminous pavement material is prepared from, in percentage by mass, 25%-30% of a light-storing type self-luminous material, 40%-45% of epoxy resin, 10%-15% of a curing agent and 10%-15% of a diluent. The self-luminous pavement material can be directly applied to pavements, is attractive and can give out light continuously for a long time on the basis that the road performance is realized and the application range is further broadened.

Description

technical field [0001] The invention relates to the technical field of materials used in road engineering, in particular to a self-luminous pavement material and a preparation method. Background technique [0002] Safety, environmental protection, and energy saving are several directions for the development of road material technology. Self-luminous pavement material technology has many advantages such as safety warning, energy saving and power saving. It is a hot direction in the research and application of road material technology at present and in the future, such as The patent "Preparation Method of Luminescent Material" ZL200810224746.5 discloses that the pre-coated aggregate, binder, luminescent material and reflective material are mixed and stirred evenly, and the material that can be used for road luminescence is prepared. Another example is the application The patent "A Self-luminous Anti-slip Pavement Material and Its Preparation Method" CN201510424539.4 discloses ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/00C08K3/24
CPCC08K3/24C08L63/00
Inventor 闫国杰施曙东邓国民许严袁月邱轶马利志石剑张伟平徐韵淳王腾飞夏庆宇周维维李文超
Owner SHANGHAI PUDONG ROAD & BRIDGE GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com