Transformer case material and preparation method thereof

A shell material and transformer technology, applied in the direction of transformer/inductor shell, etc., can solve the problems of poor electromagnetic radiation shielding, poor corrosion resistance, low mechanical strength, etc., and achieve good low temperature resistance, good wear resistance, and aging resistance Good results

Inactive Publication Date: 2017-11-10
HEFEI ANLI ELECTRIC POWER ENG CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problems of poor corrosion resistance, poor electromagnetic radiation shielding and low mechanical strength in the existing transformer casing, the purpose of the present invention is to provide a transformer casing material and a preparation method thereof, and the prepared transformer casing material has corrosion resistance Good, good electromagnetic radiation shielding and high mechanical strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A transformer casing material, comprising the following raw materials in parts by weight: 1.5 parts of dolomite, 1.5 parts of bentonite, 2.5 parts of molybdenum disulfide, 3.5 parts of aluminum tripolyphosphate, 5.5 parts of boron nitride, 5.5 parts of lead sulfate, and nano silicon carbide 9 parts, magnesium oxide 16.5 parts, stainless steel 22.5 parts, aluminum hydroxide 27.5 parts, expanded graphite 6 parts, silicon nitride 6 parts, quartz glass 3 parts, diatomite 4 parts and ceramic matrix composite material 6 parts.

[0038] Expanded graphite is added to the raw material. Expanded graphite is a loose and porous worm-like substance obtained from natural graphite flakes through intercalation, water washing, drying, and high-temperature expansion. Expanded graphite has good flexibility, good plasticity, high temperature resistance, and fire resistance. , Good low temperature resistance, good corrosion resistance, good radiation resistance and good aging resistance.

...

Embodiment 2

[0055] A transformer casing material, comprising the following raw materials in parts by weight: 1 part of dolomite, 1 part of bentonite, 2 parts of molybdenum disulfide, 3 parts of aluminum tripolyphosphate, 5 parts of boron nitride, 5 parts of lead sulfate, and nanometer silicon carbide 8 parts, magnesium oxide 15 parts, stainless steel 20 parts, aluminum hydroxide 25 parts, expanded graphite 5 parts, silicon nitride 3 parts, quartz glass 2 parts, diatomaceous earth 2 parts and ceramic matrix composite material 4 parts.

[0056] Expanded graphite is added to the raw material. Expanded graphite is a loose and porous worm-like substance obtained from natural graphite flakes through intercalation, water washing, drying, and high-temperature expansion. Expanded graphite has good flexibility, good plasticity, high temperature resistance, and fire resistance. , Good low temperature resistance, good corrosion resistance, good radiation resistance and good aging resistance.

[0057]...

Embodiment 3

[0073] A transformer shell material, comprising the following raw materials in parts by weight: 2 parts of dolomite, 2 parts of bentonite, 3 parts of molybdenum disulfide, 4 parts of aluminum tripolyphosphate, 6 parts of boron nitride, 6 parts of lead sulfate, and nano silicon carbide 10 parts, 18 parts of magnesium oxide, 25 parts of stainless steel, 30 parts of aluminum hydroxide, 7 parts of expanded graphite, 9 parts of silicon nitride, 4 parts of quartz glass, 6 parts of diatomaceous earth and 8 parts of ceramic matrix composite material.

[0074] Expanded graphite is added to the raw material. Expanded graphite is a loose and porous worm-like substance obtained from natural graphite flakes through intercalation, water washing, drying, and high-temperature expansion. Expanded graphite has good flexibility, good plasticity, high temperature resistance, and fire resistance. , Good low temperature resistance, good corrosion resistance, good radiation resistance and good aging ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention provides a transformer casing material and a preparation method thereof, and relates to the field of power materials. The transformer casing material includes the following raw materials in parts by weight: dolomite, bentonite, molybdenum disulfide, aluminum tripolyphosphate, boron nitride, lead sulfate, nano Silicon carbide, magnesium oxide, stainless steel, aluminum hydroxide, expanded graphite, silicon nitride, quartz glass, diatomite and ceramic matrix composite material; the preparation method comprises the following steps: (1) weighing raw materials; (2) ball milling; ( 3) Stirring and molding into a mold. The invention solves the problems of poor corrosion resistance, poor electromagnetic radiation shielding performance and low mechanical strength existing in the existing transformer casing.

Description

technical field [0001] The invention belongs to the field of power materials, and in particular relates to a transformer shell material and a preparation method thereof. Background technique [0002] The transformer shell is mainly used for the safety protection of the operation transformer site. Avoid accidents caused by foreign objects such as small animals and rainwater entering the transformer, avoid damage to the transformer caused by corrosion, and the transformer can protect personal safety. In the existing technology, there are few researches on the transformer shell, but the safety hazards caused by the transformer shell are more and more. In order to ensure the safety of people's production and life, we need to study a kind of transformer with good corrosion resistance, good electromagnetic radiation shielding, Transformer housing with high mechanical strength. Contents of the invention [0003] In order to solve the problems of poor corrosion resistance, poor ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C29/00C22C49/00C22C1/05C22C47/14C22F1/00H01F27/02C22C101/20
CPCC22C29/00C22C1/051C22C47/14C22C49/00C22F1/00H01F27/02
Inventor 殷世尧
Owner HEFEI ANLI ELECTRIC POWER ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com