Rapid curing process of battery plate

A curing process and fast curing technology, applied in the direction of lead-acid battery electrodes, etc., can solve the problems of insufficiency and long curing time, and achieve the effect of improving production efficiency, good capacity and cycle life

Active Publication Date: 2017-11-10
SHENZHEN CENT POWER TECH +1
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the above-mentioned problems of long curing time in the curing of the raw plate of the existing lead-acid battery and the inability to meet the high automation, complete set and systematic production mode, the embodiment of the present invention provides a rapid curing process for the battery

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] (1) According to the material of positive lead paste, it is composed of the following weight percentages: lead powder 30%; dilute sulfuric acid 18%; pure water 15%; short fiber 1.2%; On the grid; coated with a punched plate with a thickness of 2.5mm;

[0034] (2) the punched pole plate obtained above is evenly spread in the curing chamber in the form of a single piece and carried out by the following steps:

[0035] 1) The first stage of curing, the temperature is 60°C, the humidity is 98%, and the time is 1.0h;

[0036] 2) The second stage of curing, the temperature is 65°C, the humidity is 90%, and the time is 0.5h;

[0037] 3) The third stage of curing, the temperature is 72°C, the humidity is 90%, and the time is 1.0h;

[0038] 4) The fourth stage of curing, the temperature is 83°C, the humidity is 85%, and the time is 2.5h;

[0039] 5) The fifth stage of curing, the temperature is 70°C, the humidity is 85%, and the time is 0.5h;

[0040] 6) The first stage of d...

Embodiment 2

[0044] (1) According to the material of positive lead paste, it is composed of the following weight percentages: lead powder 80%; dilute sulfuric acid 20%; pure water 8%; short fiber 0.8%; On the grid; coated with a punched plate with a thickness of 2.5mm;

[0045] (2) the punched pole plate obtained above is evenly spread in the curing chamber in the form of a single piece and carried out by the following steps:

[0046] 1) The first stage of curing, the temperature is 65°C, the humidity is 100%, and the time is 0.5h;

[0047] 2) The second stage of curing, the temperature is 65°C, the humidity is 95%, and the time is 1.0h;

[0048] 3) The third stage of curing, the temperature is 75°C, the humidity is 85%, and the time is 1.0h;

[0049] 4) The fourth stage of curing, the temperature is 85°C, the humidity is 85%, and the time is 2.5h;

[0050] 5) The fifth stage of curing, the temperature is 75°C, the humidity is 85%, and the time is 0.5h;

[0051] 6) The first stage of d...

Embodiment 3

[0055] (1) According to the material of positive lead paste, it is composed of the following weight percentages: lead powder 80%; dilute sulfuric acid 10%; pure water 20%; short fiber 0.8%; On the grid; coated with a punched plate with a thickness of 2.5mm;

[0056] (2) the punched pole plate obtained above is evenly spread in the curing chamber in the form of a single piece and carried out by the following steps:

[0057] 1) The first stage of curing, the temperature is 65°C, the humidity is 95%, and the time is 0.5h;

[0058] 2) The second stage of curing, the temperature is 60°C, the humidity is 95%, and the time is 1.0h;

[0059] 3) The third stage of curing, the temperature is 70°C, the humidity is 90%, and the time is 0.5h;

[0060] 4) The fourth stage of curing, the temperature is 80°C, the humidity is 80%, and the time is 1.0h;

[0061] 5) The fifth stage of curing, the temperature is 75°C, the humidity is 85%, and the time is 1.0h;

[0062] 6) The first stage of d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a rapid curing process of a battery plate. The rapid curing process comprises the following steps: stage 1: the temperature is 60 to 65 DEG C, the humidity is 95% to 100%, and the time is 0.5h to 1.0h; stage 2: the temperature is 60 to 65 DEG C, the humidity is 90% to 95%, and the time is 0.5h to 1.0h; stage 3: temperature is 70 to 75 DEG C, the humidity is 85% to 90%, and the time is 0.5h to 1.0h; stage 4: the temperature is 80 to 85 DEG C, the humidity is 80% to 85%, and the time is 1.0h to 2.5h; stage 5: the temperature is 70 to 75 DEG C, the humidity is 85% to 90%, and the time is 0.5h to 1.0h; and a drying stage: the temperature is 80 to 85 DEG C, the humidity is 0%, and the time is 1.0h to 4.0h. The scheme of the invention greatly improves the production efficiency of plate curing and drying, realizes the continuous production of lead-acid battery plates and assembly, and the manufactured lead-acid batteries have good capacity and cycle life.

Description

technical field [0001] The invention relates to the technical field of storage batteries, in particular to a rapid curing process for storage batteries. Background technique [0002] With the intensification of the world energy crisis and the rise of a low-carbon economy, the production model of China's battery industry is undergoing tremendous transformation and upgrading. The new production technology will gradually replace the old production technology. At present, high-tech complete sets of wire mesh production lines, continuous casting and rolling production lines, and automatic material conveying systems have gradually emerged, and advanced high-automation, complete sets, and systematic production models are emerging. [0003] In the manufacturing process of lead-acid batteries, the curing of green plates is a key process, and it is also one of the processes with the longest production cycle. At present, the common curing process time is usually between 60h and 90h; t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/21
CPCH01M4/21Y02E60/10
Inventor 廖兆军胡金丰张华农
Owner SHENZHEN CENT POWER TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products