Efficient adhesion type high-titanium furnace protection stemming
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An adhesive type, high-titanium technology, applied in the field of blast mud for protecting furnaces, can solve the problems of high sidewall temperature, affecting the normal production of blast furnaces, and threats to normal operation of blast furnaces, so as to prevent erosion and prolong service life.
Inactive Publication Date: 2017-11-24
畲云锋
View PDF8 Cites 9 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
With the continuous strengthening of blast furnace smelting, domestic blast furnaces, especially in the late age of blast furnaces, have serious corrosion on the side walls of the hearth in the iron mouth area and the iron mouth area, and the side wall temperature is too high, which not only poses a threat to the normal operation of the blast furnace, but also affects the normal operation of the blast furnace. production, and seriously affect the realization of the goal of blast furnace longevity. In order to ensure the safe production of blast furnaces, protect the parts around the taphole and the hearth, and reduce the erosion of the taphole brick lining, it is necessary to propose a high-efficiency adhesive high-titanium furnace protection Cannon clay
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0021] A high-efficiency adhesion type high-titanium furnace clay, the raw materials of which are calculated by weight percentage include the following components: bauxite 10%, brown corundum 5%, titanium iron powder 12%, titanium dioxide 15%, ferrosilicon nitride 12% %, silicon carbide 8%, coke 11%, tar 10%, pyrophyllite 2%, pitch 4%, kyanite 3%, sericite 5%, resin 2%, flake graphite 1%.
Embodiment 2
[0023] A high-efficiency adhesion type high-titanium furnace clay, the raw materials of which are calculated by weight percentage include the following components: bauxite 9%, brown corundum 6%, titanium iron powder 12%, titanium dioxide 15%, ferrosilicon nitride 13% %, silicon carbide 9%, coke 11%, tar 9%, pyrophyllite 2%, pitch 3%, kyanite 2%, sericite 5%, resin 2%, flake graphite 2%.
Embodiment 3
[0025] A high-efficiency adhesion type high-titanium furnace clay, the raw materials of which are calculated by weight percentage include the following components: bauxite 9%, brown corundum 7%, titanium iron powder 15%, titanium dioxide 15%, ferrosilicon nitride 10% %, silicon carbide 7%, coke 10%, tar 7%, pyrophyllite 1.5%, pitch 3.5%, kyanite 3%, sericite 4%, resin 4%, flake graphite 4%.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle size
aaaaa
aaaaa
compressive strength
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses efficient adhesion type high-titanium furnace protection stemming, which is prepared from the following ingredients in percentage by weight: 8 to 12 percent of bauxite, 3 to 7 percent of brown fused alumina, 22 to 32 percent of titanium-containing materials, 10 to 14 percent of iron silicon nitride, 6 to 10 percent of silicon carbide, 10 to 15 percent of coke, 6 to 12 percent of tar, 0.5 to 3 percent of pyrophillite, 2 to 5 percent of asphalt, 1 to 5 percent of cyanite, 3 to 7 percent of sericite, 0.5 to 4 percent of resin and a certain amount of crystalline flake graphite. Compared with a conventional titanium-containing stemming, the efficient adhesion type high-titanium furnace protection stemming has the advantages that the titanium content is high; the titanium-containing materials, particularly titanium pigments have good reaction activity, and can sufficiently react with other substances for forming caulking substances; due to the ultrafine granularity, the stemming can easily float up to a furnace cylinder erosion region in a furnace cylinder; flake graphite is introduced; good floating performance, lubricating performance and plasticity are realized; the stemming can be combined with generated high-temperature-resistant caulking particles such a TiC, TiN and Ti(C,N); the particles are carried for better entering the erosion region to be effectively filled into the seams; the effective furnace protection effect is achieved.
Description
【Technical field】 [0001] The invention relates to the technical field of furnace-protecting blasthole clay, in particular to a high-efficiency adhesion type high-titanium furnace-protecting blasthole clay. 【Background technique】 [0002] Blast furnace ironmaking is an important link in iron and steel production. With the large-scale blast furnace, high smelting strength, and the discharge of large amounts of slag and iron, the requirements for the quality of blasting mud for blocking iron ports are getting higher and higher. When the blast furnace does not produce molten iron slag, the blast furnace mud is filled in the tap hole to maintain a sufficient depth; when the blast furnace taps iron, the center of the blast furnace mud in the tap hole is drilled out of the tunnel, and the molten iron slag is discharged out of the furnace through the tunnel. The gun mud is required to keep the hole diameter of the iron hole stable, the iron tapping is uniform, and the molten iron sl...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.