Preparation method for pigment coated with prussian blue or prussian blue analogue
A technology similar to Prussian blue and Prussian blue, applied in the field of pigment preparation, which can solve the problems of decreased gloss, difficulty in filtration, and free iron blue
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0047] In the reactor, add 60g of glass flakes with an average particle size of 500μm and a thickness of 3μm, add 800mL of water to make a slurry, add 4g of ammonium chloride, heat up to 78°C, and stir for 3h; use hydrochloric acid to adjust the pH of the system to 2.5, Add 20mL of 0.25M potassium ferrocyanide aqueous solution at a rate of 10mL / h at a temperature of 78°C, and at the same time add 6.7mL of 1M ferric chloride aqueous solution at a rate of 3.33mL / h. During this process, use hydrochloric acid or sodium hydroxide to maintain the pH 2.5-2.6, stirred for 0.1h after the addition was completed; then suction filtered, almost free, and obtained Prussian blue-coated glass flakes.
[0048] Coating amount is Fe 4 [Fe(CN] 6 ] The theoretical amount calculated is 1.43g, the calculated coating amount is 1.40g, the coating rate is 2.3% of the base material weight, and the coating amount is 97% of the theoretical amount, indicating that the free situation has been excellently c...
Embodiment 2
[0050] In the reactor, add 60g of synthetic mica substrate chameleon with an average particle size of 40 μm, add 500g of water and 100g of ethanol to prepare a slurry according to the solid-to-liquid weight ratio of 1 / 10, add 2g of ammonium chloride and 2g of urea, and heat up to 85 Stir at ℃ for 2 hours; adjust the pH of the system to 2.7 with sulfuric acid, add 60mL of 0.5M ammonium ferrocyanide solution at 10mL / h at a temperature of 60°C, and add 60mL of 0.66M ferric chloride aqueous solution at 10mL / h at the same time. Hydrochloric acid or sodium hydroxide maintains the pH of the system at 2.7-2.8, and stirs for 0.5h after the addition is complete; filters and washes to obtain a chameleon-coated iron blue pigment, almost free of dissociation. Coating amount is Fe 4 [Fe(CN] 6 ] 3 The calculated theoretical amount is 8.58g, the calculated coating amount is 8.26g, the coating rate is 13.8% of the substrate weight, and the coating amount is 96% of the theoretical amount, whi...
Embodiment 3
[0052] In the reactor, add 60g of green interference pearlescent pigment of synthetic mica coated titanium dioxide with an average particle size of 100 μm, add 1200g of water according to the solid-to-liquid weight ratio of 1 / 20 to prepare a slurry, add 2g of ammonium sulfate and 2g of ammonium bromide, Raise the temperature to 85°C and stir for 3 hours; use sulfuric acid to adjust the pH of the system to 2.5, add 15mL of 0.25M ammonium ferrocyanide solution at 5ml / h at 85°C, and simultaneously add 15mL of ferric chloride 0.167M and Titanium chloride 0.125M mixture aqueous solution, use sodium hydroxide or hydrochloric acid to maintain the pH value of the system at 2.5-2.6 during the process, stir for 0.5h after the addition is complete; filter and wash, the free amount is small, and after drying, obtain a green interference Color, green accumulation of color powder. Its theoretical coating amount is Fe 4 Ti 3 [Fe(CN) 6 ] 6 It is 1.02g, and the calculated coating amount is...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap