Anti-fatigue tire compound and its preparation method

An anti-fatigue, tire technology, applied in the field of tire rubber, can solve the problems of difficult dispersion effect, insufficient compatibility, etc., and achieve high anti-fatigue effect

Inactive Publication Date: 2017-12-01
SICHUAN YUANXING RUBBER
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to its molecular group, silica has insufficient compatibility with rubber, and it is difficult to obtain the required dispersion effect. Therefore, improving the fatigue resistance of tire rubber has always been the bottleneck of the existing technology.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] An anti-fatigue tire rubber compound, which is prepared from the following raw materials in parts by weight: diene rubber: 100 parts, white carbon black: 30-50 parts, carbon black: 0-10 parts, Active agent: 3-5 parts, anti-aging agent: 1-3 parts, binder: 2-4 parts, softener: 6-10 parts; the white carbon black is hydrated silica or Non-highly disperse silica or non-transparent silica. The diene rubber is a mixture of natural rubber, butadiene rubber and styrene-butadiene rubber.

[0022] The anti-fatigue tire compound of the present embodiment provides the following specific formula preferred examples:

[0023] The anti-fatigue tire compound is prepared according to the following raw materials in parts by weight: natural rubber: 40 parts, butadiene rubber: 30 parts, styrene-butadiene rubber: 30 parts, white carbon black: 40 parts, carbon black N220: 10 parts Parts, zinc oxide active agent: 2 parts, stearic acid active agent: 1 part; coupling agent: 5 parts, binder: 3 p...

Embodiment 2

[0032] An anti-fatigue tire rubber compound, which is prepared from the following raw materials in parts by weight: diene rubber: 100 parts, white carbon black: 30-50 parts, carbon black: 0-10 parts, Active agent: 3-5 parts, anti-aging agent: 1-3 parts, binder: 2-4 parts, softener: 6-10 parts, coupling agent: 3-5 parts, vulcanizing agent: 1-3 parts, Accelerator: 1 to 3 parts. The white carbon black is hydrated silica or non-highly dispersed white carbon black or non-transparent white carbon black prepared by a precipitation method. The diene rubber is a mixture of natural rubber, butadiene rubber and styrene-butadiene rubber.

[0033] The anti-fatigue tire compound of the present embodiment provides the following specific formula preferred examples:

[0034] The anti-fatigue tire compound is prepared according to the following raw materials in parts by weight: natural rubber: 40 parts, butadiene rubber: 30 parts, styrene-butadiene rubber: 30 parts, white carbon black: 40 par...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anti-fatigue tire compound and its preparation method. The anti-fatigue tire compound is prepared from, by weight, 100 parts of alkadiene rubber, 30-50 parts of white carbon black, 0-10 parts of carbon black, 3-5 parts of active agent, 1-3 parts of anti-aging agent, 2-4 parts of bonding agent, and 6-10 parts of softening agent. According to the anti-fatigue tire compound, the rubber compound or final compound has very high anti-fatigue without adding the non-environmental-friendly antifatigue during the preparation process of the tire compound; through being detected by a carbon black dispersion tester, the dispersion grade of the prepared tire rubber can stably reach 7 and above; the fatigue test or the yield after thermal aging of the tire compound can be free from crack for 1.2 million times.

Description

technical field [0001] The invention relates to the technical field of tire rubber materials, in particular to an anti-fatigue tire rubber material and a preparation method thereof. Background technique [0002] At present, in tire manufacturers, most of the anti-fatigue agents are added to the rubber compound to achieve the same performance index. The amount of anti-fatigue agent is relatively large, and most of them are controlled above 5PHR, but the fatigue test (after heat aging) Flexion) is also 300,000-700,000 times. Most of the anti-fatigue agents on the market are non-environmental protection products and may be banned in the future. With the further promotion and implementation of environmental protection awareness in the people's livelihood industry, all walks of life are speeding up the rectification, and the carbon black used in the tire industry has pollution effects due to its production process, and the production of white carbon black is relatively clean. M...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/00C08L9/06C08L61/12C08K13/02C08K3/36C08K3/04C08K3/22C08K5/09
CPCC08L7/00C08K2003/2296C08L2205/02C08L2205/035C08L9/00C08L9/06C08L61/12C08K13/02C08K3/36C08K3/04C08K3/22C08K5/09
Inventor 吕荣福
Owner SICHUAN YUANXING RUBBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap