High-temperature-resistant rubber sealing element

A technology of rubber seals and fluorine rubber, which is applied in other chemical processes, chemical instruments and methods, etc., can solve the problems of poor temperature resistance, achieve good high temperature resistance and mechanical stability, and promote the use value

Inactive Publication Date: 2017-12-01
宁国市宁和密封件厂
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Electric vehicle brake caliper parts also need to use rubber seals, and when the brake caliper parts are in use, the internal components will squeeze and rub against the rubber seals, which will cause the rubber

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0018] Example 1

[0019] A high-temperature-resistant rubber seal, composed of the following parts by weight:

[0020] 60 parts of nitrile rubber, 40 parts of fluorine rubber, 55 parts of modified ceramic powder, 8 parts of manganese powder, 6 parts of glass fiber, 2 parts of dispersant, 1 part of antioxidant, 4 parts of vulcanizing agent.

[0021] Further, the preparation method of the modified ceramic powder includes the following steps:

[0022] (1) Put the ceramic powder into a 6% nitric acid solution and soak for 30 minutes, take it out and rinse it with clean water for use;

[0023] (2) Put the ceramic micropowder treated in step (1) into the modification solution and soak for 1 hour, during which time it is heated to maintain the temperature of the modification solution at 80℃, and ultrasonic waves with a frequency of 70kHz are applied for treatment. After rinsing with clean water, put it in a drying box and dry to a constant weight; the components in the modified solution and ...

Example Embodiment

[0027] Example 2

[0028] A high-temperature-resistant rubber seal, composed of the following parts by weight:

[0029] 63 parts of nitrile rubber, 42 parts of fluorine rubber, 58 parts of modified ceramic powder, 10 parts of manganese powder, 8 parts of glass fiber, 3 parts of dispersant, 1.5 parts of antioxidant, 5 parts of vulcanizing agent.

[0030] Further, the preparation method of the modified ceramic powder includes the following steps:

[0031] (1) Put the ceramic powder into a nitric acid solution with a mass fraction of 8% for 33 minutes, take it out and rinse it with clean water for use;

[0032] (2) Put the ceramic powder treated in step (1) into the modification solution and soak for 1.5 hours, during which time it is heated to keep the temperature of the modification solution at 83°C, and ultrasonic waves with a frequency of 72kHz are applied for treatment, and then taken out after completion After rinsing it with clean water, put it in a drying box and dry to a constant...

Example Embodiment

[0036] Example 3

[0037] A high-temperature-resistant rubber seal, composed of the following parts by weight:

[0038] 65 parts of nitrile rubber, 45 parts of fluorine rubber, 60 parts of modified ceramic powder, 12 parts of manganese powder, 9 parts of glass fiber, 4 parts of dispersant, 2 parts of antioxidant, 6 parts of vulcanizing agent.

[0039] Further, the preparation method of the modified ceramic powder includes the following steps:

[0040] (1) Put the ceramic micropowder into a 9% nitric acid solution and soak for 35 minutes, take it out and rinse it with clean water for use;

[0041] (2) Put the ceramic powder treated in step (1) into the modification solution and soak for 2 hours, during which time it is heated to maintain the temperature of the modification solution at 85°C, and ultrasonic waves with a frequency of 75kHz are applied for treatment. After rinsing with clean water, put it in a drying box and dry to constant weight; the components in the modified solution an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high temperature-resistant rubber seal, which is composed of the following materials: nitrile rubber, fluorine rubber, modified ceramic micropowder, manganese powder, glass fiber, dispersant, antioxidant and vulcanizing agent. The present invention carries out special matching treatment on the rubber seal, and under the joint action of each component, the final rubber seal has good high temperature resistance and mechanical stability, and has good popularization and use value.

Description

technical field [0001] The invention belongs to the technical field of processing and manufacturing rubber seals, and in particular relates to a high temperature-resistant rubber seal. Background technique [0002] Rubber seals are a general basic component in sealing devices Rubber seals are a type of rubber products widely used in sealing technology. Because of its small elastic modulus, high elongation, and air resistance, it is widely used for installation on various mechanical equipment. Electric vehicle brake caliper parts also need to use rubber seals, and when the brake caliper parts are in use, the internal components will squeeze and rub against the rubber seals, which will cause the rubber seals to generate a lot of heat, so rubber seals are required The parts have good temperature resistance to ensure the quality of their use, but most of the existing rubber seals have poor temperature resistance. Contents of the invention [0003] The object of the present i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L9/02C08L27/12C08K13/06C08K9/10C08K9/12C08K3/00C08K7/14C08K3/08C08K5/134C09K3/10
CPCC08L9/02C08K2003/0856C08K2201/003C08K2201/004C08L2201/08C09K3/10C09K2003/1078
Inventor 张文尧
Owner 宁国市宁和密封件厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products