Production technology for continuously producing light ceramic base material solar tiles

A technology for solar tile and production process, applied in the field of solar tile, can solve the problems of inconvenient production and installation, high cost of glass substrate, heavy weight, etc., and achieve the effects of low production and installation cost, weight reduction, and weight reduction

Inactive Publication Date: 2018-01-05
万锦标
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, solar power generation films are generally installed in glass interlayers for utilization, but glass substrates are not only costly, but also heavy, making production and installation extremely inconvenient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] A kind of production technology of the present invention continuously produces light-weight ceramic substrate solar tile, implements according to the following steps:

[0013] The first step is to press the configured raw materials into a mud body and then biscuit;

[0014] In the second step, the first glaze is applied after bisque firing, and then glaze firing is carried out;

[0015] The fourth step is to polish the glazed products;

[0016] The fifth step is to install a solar power generation film on the upper side of the product that has completed the fourth step, and install special transparent glass to press and fix it, and then pack it into the warehouse.

[0017] The first glazing includes bottom glaze and top glaze.

[0018] The raw materials include main ingredients, feldspar, quartz and composite active ingredients, wherein the main ingredients are 25-35 parts including shale, clay and kaolin, the feldspar is 45-55 parts, and the quartz is 15-25 parts , ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a production technology for continuously producing light ceramic base material solar tiles. The production technology for continuously producing the light ceramic base materialsolar tiles overcomes the defects of the prior art, a solar power generation film is matched with a light ceramic base material, the weight is greatly reduced, and the production cost and the installation cost are quite low. The production technology for continuously producing the light ceramic base material solar tiles is executed according to the following steps that raw materials which are wellprepared is pressed into a mud greed body for biscuiting, and primary glazing is then conducted after biscuiting; then glaze firing is conducted, a product obtained after glaze firing is completed ispolished, the solar power generation film is installed on the upper side face of the product, a special transparent glass is installed, pressed and fixed, and then the product is packed and put in storage. The production technology for continuously producing the light ceramic base material solar tiles can be widely applied to the field of solar tiles.

Description

technical field [0001] The invention discloses a production process for continuously producing light-weight ceramic substrate solar tiles, which belongs to the technical field of solar tiles. Background technique [0002] At present, solar power generation films are generally installed in glass interlayers for utilization, but glass substrates are not only expensive, but also heavy, making production and installation extremely inconvenient. Contents of the invention [0003] The present invention overcomes the deficiencies in the prior art, and provides a production process for continuously producing solar tiles with light ceramic base material. The combination of solar power generation film and light ceramic base material not only greatly reduces the weight, but also improves the efficiency of production and installation. The cost is extremely low. [0004] In order to solve the above technical problems, the technical solution adopted in the present invention is: a produ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): E04D1/00E04D1/04E04D1/16E04D13/18H02S20/25C04B35/18C04B38/00C04B35/622
CPCY02B10/10Y02E10/50
Inventor 万锦标
Owner 万锦标