Glaze material capable of removing peculiar smell and preparation method thereof

A glaze and peculiar smell technology is applied in the field of odor-removing glaze and its preparation, which can solve the problems of high energy consumption, serious environmental pollution and many materials, and achieve the effects of removing peculiar smell, wide market prospect and high artistic value.

Inactive Publication Date: 2018-01-12
禹州市华盛钧窑有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ordinary daily-use porcelain products are of low grade and poor quality. At the same time, they consume a lot of energy, use a lot of materials, and cause serious environmental pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1: a kind of glaze material that can remove peculiar smell, it is prepared by the raw material of following parts by weight: feldspar 38 parts, quartz 23 parts, soft soil 12 parts, stainless steel powder 7 parts, ox bone ash 6 parts , 4 parts of talcum powder.

[0013] The preparation method of the deodorizing glaze comprises the following steps:

[0014] Step 1: (1) Coarsely crush the stone raw materials with a wheel mill; (2) Stack the soil materials in the open air and weather them through perennial wind, sun, rain, freezing, etc.; (3) Carry out 20 hours of feldspar Up to 25 hours of pre-burning treatment;

[0015] Step 2: Put the well-proportioned glaze into the ball mill, add water with a total weight of 30-45% of the mixed raw materials, start the wet mill for 10-25 hours, and take out the glaze slurry from the ball mill after reaching the specified fineness;

[0016] Step 3: Sieve the wet-milled slurry through a 200-300-mesh sieve into a glaze pool o...

Embodiment 2

[0017] Embodiment 2: a kind of glaze material that can remove peculiar smell, it is prepared by the raw material of following parts by weight: 30 parts of feldspar, 20 parts of quartz, 10 parts of soft soil, 5 parts of stainless steel powder, 5 parts of bovine bone ash , 2 parts of talcum powder.

[0018] The preparation method of the deodorizing glaze comprises the following steps:

[0019] Step 1: (1) Coarsely crush the stone raw materials with a wheel mill; (2) Stack the soil materials in the open air and weather them through perennial wind, sun, rain, freezing, etc.; (3) Carry out 20 hours of feldspar Up to 25 hours of pre-burning treatment;

[0020] Step 2: Put the well-proportioned glaze into the ball mill, add water with a total weight of 30-45% of the mixed raw materials, start the wet mill for 10-25 hours, and take out the glaze slurry from the ball mill after reaching the specified fineness;

[0021] Step 3: Sieve the wet-milled slurry through a 200-300-mesh sieve ...

Embodiment 3

[0022] Embodiment 3: a kind of glaze material that can remove peculiar smell, it is prepared by the raw material of following parts by weight: feldspar 40 parts, quartz 25 parts, soft soil 15 parts, stainless steel powder 10 parts, bovine bone ash 8 parts , 6 parts of talcum powder.

[0023] The preparation method of the deodorizing glaze comprises the following steps:

[0024] Step 1: (1) Coarsely crush the stone raw materials with a wheel mill; (2) Stack the soil materials in the open air and weather them through perennial wind, sun, rain, freezing, etc.; (3) Carry out 20 hours of feldspar Up to 25 hours of pre-burning treatment;

[0025] Step 2: Put the well-proportioned glaze into the ball mill, add water with a total weight of 30-45% of the mixed raw materials, start the wet mill for 10-25 hours, and take out the glaze slurry from the ball mill after reaching the specified fineness;

[0026] Step 3: Sieve the wet-milled slurry through a 200-300-mesh sieve into a glaze p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a glaze material capable of removing peculiar smell and a preparation method thereof. The glaze material is prepared from the following raw materials in parts by weight: 30-40parts of feldspar, 20-25 parts of quartz, 10-15 parts of weak soil, 5-10 parts of stainless steel powder, 5-8 parts of cow bone ash and 2-6 parts of talcum powder. By adding the stainless steel powder into the ingredients of the glaze material, stainless steel can assist on a glaze layer of Jun porcelain, and when the glaze layer is in contact with a hand of a user, released iron ions are bound with peculiar smell molecules, so that the peculiar smell can be removed, and a special art effect that the glaze layer of Jun porcelain presents a metal luster can be achieved; and the glaze materialhas relatively high art values and wide market prospects.

Description

technical field [0001] The invention relates to the field of Jun porcelain, in particular to a deodorizing glaze and a preparation method thereof. Background technique [0002] Jun porcelain originated in the Eastern Han Dynasty. It is one of the five famous kiln porcelains in the Song Dynasty. Famous for its unique kiln transformation art, it has the reputation of "gold is priceless and Jun porcelain is priceless" and "a family is rich, but it is not as good as a piece of Jun porcelain". With its simple shape, exquisite craftsmanship, complex glaze matching, the magical kiln transformation of "one color in the kiln, thousands of colors out of the kiln", lakes and mountains, clouds and mist, human beings, animals, flowers, birds, insects and fish, etc. Known as the first of China's "Five Famous Porcelains". [0003] The traditional technology uses coal to directly fire the kiln to produce ordinary daily-use porcelain. Ordinary daily-use porcelain products are of low grade...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/18
Inventor 任合超
Owner 禹州市华盛钧窑有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com