Novel bonding process for glass fiber plate and silica gel plate

A technology of glass fiber board and silica gel board, which is applied in the new technology field of combining glass fiber board and silica gel board, which can solve the problems of poor bonding force and glue opening, and achieve the effect of improving bonding strength, eliminating the process of viscose glue, and improving stability

Inactive Publication Date: 2018-01-16
SHENZHEN STRONG TECH
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] e. Bonded with glue, the bonding force is poor, and the glue is opened during the product processing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] The technical solution of this patent will be further described in detail below in conjunction with specific embodiments.

[0027] A new process for combining glass fiber boards and silica gel boards, comprising the following process steps:

[0028] (1) Prepare materials: prepare glass fiber board and liquid silicon raw materials, products with anti-static requirements, use anti-static glass fiber board and make anti-static liquid silicone raw materials for product raw materials;

[0029] (2) Make the cavity: make a cavity made of glass fiber board, and the cavity is made into a clad structure;

[0030] (3) Brush treatment agent: treat the inner side of the fiberglass board with treatment agent;

[0031] (4) Preliminary solidification of the surface: use liquid silica gel as the raw material;

[0032] (5) One-time vulcanization: perform one-time vulcanization treatment on the cured silica gel plate;

[0033] (6) Secondary vulcanization: perform secondary vulcanizatio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a novel bonding process for a glass fiber plate and a silica gel plate. The novel bonding process comprises the following steps: (1) material preparation; (2) cavity preparation; (3) brushing of a treating agent; (4) surface preliminary curing; (5) primary vulcanization; (6) secondary vulcanization; and (7) preparation of a finished product. The novel bonding process provided by the invention can obviously improve the bonding strength of glass fibers and silica gel in the product and obviously enhance the stability of the volume resistance antistatic capability of the product; the procedure of adhesive application is omitted, so the production and manufacturing cycle of the product is shortened; and the product needs no special mold, and only enclosure of a cavity is needed during material production, so the material cost of the product is not increased.

Description

technical field [0001] The invention relates to the occasion of combining glass fiber boards with various thicknesses and silica gel boards, in particular to a new technology for combining glass fiber boards and silica gel boards. Background technique [0002] At present, the glass fiber board and the silica gel board generally use glue to bond the two joint surfaces of the product. The existing technology has the following technical defects: [0003] a. There are few glues on the market that can bond silica gel and glass fiber products at the same time, even if they can be glued, it is easy to open the glue; [0004] b. For occasions with anti-static requirements, use anti-static glue to make the bonding even weaker; [0005] c. For occasions with anti-static requirements, use non-anti-static glue + conductive substances (silver paste, metal and other conductive media); [0006] d. It takes a long time to bond and cure with glue, and the product production cycle is long; ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B29C39/10B29C39/22B29C39/26B29C35/00
Inventor 刘泉
Owner SHENZHEN STRONG TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap