Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

a static plate

A technology for static discs and aluminum alloy materials, applied in the field of alloy materials, can solve the problems of unsustainable use and short replacement cycle of static discs, and achieve the effects of easy operation, short replacement cycle, and improved quality and compactness.

Active Publication Date: 2019-12-06
JIANHUA CONSTR MATERIALS (JIANGSU) CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] During the application process, the static disc needs to be subjected to great friction and extrusion force, resulting in a short replacement cycle of the static disc, short-term use, and insufficient strength.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • a static plate
  • a static plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033]Melt the aluminum alloy material with the following mass percentage composition at 750°C, add 0.01% detonating agent and 1.0% reinforcing agent of the aluminum alloy mass at the same time of melting, and stir it repeatedly with an iron rake for 25 minutes to completely melt it to obtain molten aluminum; The composition and mass percentage of the alloy material: Si: 6%, Fe: 0.1%, Mg: 0.5%, Zr: 0.01%, Ti: 0.01%, B: 0.03%, La: 0.02%, the balance is aluminum and not Avoided impurities; then the resulting aluminum liquid is refined, and the refining temperature is 780°C. After refining, cool to 690°C and preheat the mold to 150°C at the same time, pour the cooling liquid into the mold and cast to form the final product static plate.

Embodiment 2

[0035] Melt the aluminum alloy material with the following mass percentage composition at 753°C, add 0.011% detonating agent and 1.1% reinforcing agent of the aluminum alloy mass at the same time of melting, and stir repeatedly with an iron rake for 26 minutes to completely melt to obtain aluminum liquid; The composition and mass percentage of the alloy material: Si: 6.2%, Fe: 0.105%, Mg: 0.52%, Zr: 0.011%, Ti: 0.024%, B: 0.031%, La: 0.023%, the balance is aluminum and not Avoided impurities; then the resulting aluminum liquid is refined, and the refining temperature is 784°C. Cool to 692°C after refining, and preheat the mold to 158°C at the same time, pour the cooling liquid into the mold and cast to form the final product static plate.

Embodiment 3

[0037] The aluminum alloy material composed of the following mass percentages was melted at 756°C, and 0.012% detonating agent and 1.2% reinforcing agent were added to the mass of the aluminum alloy while melting, and stirred repeatedly with an iron rake for 27 minutes to completely melt to obtain molten aluminum; The composition and mass percentage of the alloy material: Si: 6.4%, Fe: 0.11%, Mg: 0.54%, Zr: 0.012%, Ti: 0.038%, B: 0.032%, La: 0.026%, the balance is aluminum and not Avoid impurities; then the resulting aluminum liquid is refined, and the refining temperature is 788°C. Cool to 694°C after refining, and preheat the mold to 166°C at the same time, pour the cooling liquid into the mold and cast to form the final product static plate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a stationary disc, in particular to a stationary disc for a scroll type compressor, and belongs to the technical field of alloy materials. The stationary disc is made of an aluminum alloy material, and the aluminum alloy material comprises, by mass, 6-8% of Si, 0.10-0.15% of Fe, 0.5-0.7% of Mg, 0.01-0.02% of Zr, 0.01-0.15% of Ti, 0.03-0.04% of B, 0.02-0.05% of La, and thebalance aluminum and unavoidable impurities. The aluminum alloy material used in the stationary disc is reasonably configured, and meanwhile, a specific preparation method is adopted, so that the obtained stationary disc has higher strength and higher corrosion resistance.

Description

technical field [0001] The invention relates to a static disc, in particular to a static disc for a scroll compressor, and belongs to the technical field of alloy materials. [0002] technical background [0003] Scroll compressor is an energy-saving compressor in today's world. It is also known as "ultra-quiet compressor" because of its stable operation, small vibration and quiet working environment. The scroll compressor has a novel and precise structure, small size, low noise, light weight, small vibration, low energy consumption, long life, continuous and stable gas transmission, reliable operation, clean gas source, etc., and is known as the "New Revolution". Compressor” and “No Service Compressor”. Scroll compressors are ideal power sources for pneumatic machinery, and are widely used in industries such as industry, agriculture, transportation, medical equipment, food decoration and prevention, and other occasions that require compressed air. [0004] The scroll compr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/02C22C1/06C22C1/02F04C18/02F04C29/00
Inventor 华吉华胜
Owner JIANHUA CONSTR MATERIALS (JIANGSU) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com