Green glazed jun porcelain and preparation method thereof
A green-glazed Jun porcelain and Jun porcelain technology, applied in the field of glaze, can solve the problem of high fuel cost of liquefied gas and achieve the effect of ensuring stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0026] A green-glazed Jun porcelain, the body of which is prepared from the following raw materials in parts by weight: 70-80 parts of white clay, 4-6 parts of black wool soil, 9-15 parts of burnt gemstones, and 6-10 parts of sandstone;
[0027] The glaze is prepared from the following raw materials in parts by weight: 47-53 parts of feldspar, 17-23 parts of quartz, 10-16 parts of limestone, 1.5-2.5 parts of antimonite, 2-4 parts of iron ore, 8- 10 parts, 2-4 parts of talc.
[0028] The preparation method of above-mentioned celadon Jun porcelain, comprises the following steps:
[0029] (1) Preparation of base slurry and glaze slurry;
[0030] ①Preparation of glaze slurry: First, calcinate the sand and coke gems at high temperature, crush the calcined sand and coke gems, mix them with white clay and black wool soil, add 27-30% water of the total weight of the green body raw materials, Ball mill for 12-15 hours, stale for 36-48 hours, pass through a 150-mesh sieve, and dehydra...
Embodiment 2
[0043] A green-glazed Jun porcelain, the body of which is prepared from the following raw materials in parts by weight: 75 parts of white clay, 5 parts of black wool soil, 12 parts of burnt gemstones, and 8 parts of sandstone;
[0044] The glaze is prepared from the following raw materials in parts by weight: 50 parts of feldspar, 20 parts of quartz, 13 parts of limestone, 2 parts of antimonite, 3 parts of iron ore, 9 parts of wood ash and 3 parts of talc.
[0045] The preparation method of above-mentioned celadon Jun porcelain, comprises the following steps:
[0046] (1) Preparation of base slurry and glaze slurry;
[0047] ①Preparation of base slurry: Firstly, high-temperature calcining of sandstone and coke gemstones, crushing the calcined sandstone and coke gemstones, mixing them with clay and black hairy soil, adding water with 28% of the total weight of the green body raw materials, and ball milling for 14 hours , stale for 40 hours, passed through a 150-mesh sieve, and...
Embodiment 3
[0059] A green-glazed Jun porcelain, the body of which is prepared from the following raw materials in parts by weight: 80 parts of white clay, 5 parts of black wool soil, 9 parts of burnt gemstones, and 10 parts of sandstone;
[0060] The glaze is prepared from the following raw materials in parts by weight: 52 parts of feldspar, 18 parts of quartz, 14 parts of limestone, 1.5 parts of antimonite, 3.5 parts of iron ore, 10 parts of wood ash and 2.5 parts of talc.
[0061] The preparation method of above-mentioned celadon Jun porcelain, comprises the following steps:
[0062] (1) Preparation of base slurry and glaze slurry;
[0063] ①Preparation of base slurry: Firstly, high-temperature calcining is carried out on sandstone and coke gemstones, and the calcined sandstone and coke gemstones are crushed and then mixed with white clay and black hairy soil, and water with 30% of the total weight of raw materials of the green body is added, and ball milled for 12 hours , stale for 4...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap