A kind of efficient antibacterial masterbatch and preparation method thereof

An antibacterial masterbatch, high-efficiency technology, applied in the field of high-efficiency antibacterial masterbatch, can solve the problem of uneven dispersion, achieve the effect of good bonding, simple process and low cost

Active Publication Date: 2020-07-31
温岭市林氏鞋业有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

By coating the surface of the inorganic carrier, the current technical problem of uneven dispersion of inorganic antibacterial agents in the resin is solved, and the antibacterial effect is improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A highly efficient antibacterial masterbatch, its detailed preparation process steps are as follows:

[0025] (1) Pretreatment of porous bentonite powder, put the commercially available porous bentonite powder into a muffle furnace and roast at 400°C for 2h, the heating rate is set at 2°C / min, after cooling out of the furnace, it is crushed to obtain a particle size of 10-50μm Porous bentonite powder;

[0026] (2) Put the porous bentonite powder and water prepared in step (1) into a double-layer oil bath reactor with a mechanical stirring device, wherein the stirring speed of the reactor is 60r / min, and the stirring time is 2h. The bath temperature is 60°C, and the weight ratio of porous bentonite powder to water is 1:5;

[0027] (3) Add zinc nitrate to the reaction kettle of step (2), wherein the amount of zinc nitrate added is calculated as zinc, and the weight ratio to the porous bentonite powder is 1:10. After stirring for 10 minutes, slowly drop into the alkaline ...

Embodiment 2

[0031] A highly efficient antibacterial masterbatch, its detailed preparation process steps are as follows:

[0032](1) Pretreatment of porous bentonite powder. Put the commercially available porous bentonite powder into a muffle furnace and roast at 500°C for 2 hours. The heating rate was set at 5°C / min. Porous bentonite powder;

[0033] (2) Put the porous bentonite powder and water prepared in step (1) into a double-layer oil bath reactor with a mechanical stirring device, wherein the stirring speed of the reactor is 100r / min, and the stirring time is 3h. The bath temperature is 80°C, and the weight ratio of porous bentonite powder to water is 1:10;

[0034] (3) Add zinc nitrate to the reaction kettle of step (2), wherein the amount of zinc nitrate added is calculated as zinc, and the weight ratio to the porous bentonite powder is 1:20. After stirring for 20 minutes, slowly drop into the alkaline solution ammonia water, The amount of alkaline solution added is according to...

Embodiment 3

[0038] A highly efficient antibacterial masterbatch, its detailed preparation process steps are as follows:

[0039] (1) Pretreatment of porous bentonite powder, put the commercially available porous bentonite powder into a muffle furnace and roast at 600°C for 2h, the heating rate is set at 2°C / min, after cooling out of the furnace, it is crushed to obtain a particle size of 10-50μm Porous bentonite powder;

[0040] (2) Put the porous bentonite powder and water prepared in step (1) into a double-layer oil bath reactor with a mechanical stirring device, wherein the stirring speed of the reactor is 180r / min, the stirring time is 5h, and the oil The bath temperature is 100°C, and the weight ratio of porous bentonite powder to water is 1:20;

[0041] (3) Add zinc nitrate to the reaction kettle of step (2), wherein the amount of zinc nitrate added is calculated as zinc, and the weight ratio to the porous bentonite powder is 1:30. After stirring for 10-30 minutes, slowly drop into...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention aims at providing an efficient antibacterial masterbatch. The method is characterized in that porous bentonite powder is selected as an antibacterial agent carrier and is modified to carry negative charges through a quaternary ammonium base solution, and then the processed porous bentonite powder is soaked in a resin solution with opposite charge; the surface layer of the porous bentonite powder is covered by a resin film under the mutual effect of charge; a solvent is removed; the product is dried and crushed to obtain the efficient antibacterial masterbatch. According to the efficient antibacterial masterbatch and the preparation method, the surface of an inorganic carrier is covered by the film, so that the technical problem of non-uniform dispersing of an current inorganic antibacterial agent in resin can be solved, and the antibacterial effect is improved.

Description

technical field [0001] The invention belongs to the field of composite materials and functional polymer materials, and in particular relates to an efficient antibacterial masterbatch. Background technique [0002] Antibacterial materials are a new class of functional materials with antibacterial and bactericidal properties. It is often made by adding or compounding one or several specific antibacterial ingredients (antibacterial agents) to common materials, such as antibacterial plastics, antibacterial synthetic fibers, and antibacterial ceramics. After ordinary materials are endowed with antibacterial properties, various products made of them have hygienic and self-cleaning functions, which can play an important role in protecting human health and reducing diseases. Antibacterial plastics and antibacterial fibers, as the most striking branches of antibacterial materials, are used in a wide range of fields and have important research and application values. Among them, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08J3/22C08K9/12C08K9/04C08K7/26C08K3/34C08K3/22
CPCC08J3/223C08J2323/06C08K3/22C08K3/346C08K7/26C08K9/04C08K9/12C08K2003/2296C08K2201/011
Inventor 陈庆昝航
Owner 温岭市林氏鞋业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap