Permeable pointing agent composition and preparation method thereof

A composition and jointing agent technology, which is applied in the field of water permeable jointing agent composition and its preparation, can solve the problems of poor water permeability, affecting the appearance, affecting the stability of structures, etc., and achieve good water permeability and ensure the effect of appearance

Inactive Publication Date: 2018-03-16
浙江德赛堡建筑材料科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing pointing materials have poor water permeability and cannot effectively drain the moisture in the masonry cultural relics buildings in humid areas, causing the wall or rock mass to be in a wet state for a long time, affecting the stability of the structure. At the same time, the existence of a large amount of water gives Vegetation provides good growth conditions, resulting in many bryophytes appearing on the surface of the building, which affects the appearance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A water-permeable pointing agent composition, which is composed of the following components by weight percentage: 60% of aggregate, 39% of natural hydraulic lime, and 1% of auxiliary agent.

[0024] The aggregate is limestone; the particle size of the aggregate is between 0.25-1.00mm.

[0025] The natural hydraulic lime is the natural hydraulic lime specified in the European standard EN459-1 2010; the natural hydraulic lime is NHL2 produced by German HESSLER KALKWERKEGMBN company.

[0026] The auxiliary agent includes cellulose ether and wood fiber, and the weight percent content of cellulose ether and wood fiber in the water-permeable grouting agent composition is respectively: 0.5% of cellulose ether, 0.5% of wood fiber; The ether is cellulose ether M4025 from Hercules Temple Company; the wood fiber is wood fiber ARBOCEL FD40 from JRS Company of Germany.

[0027] In this embodiment, the preparation method of the permeable pointing agent composition, the steps are as ...

Embodiment 2

[0034] A water-permeable pointing agent composition, which is composed of the following components by weight percentage: 79% of aggregate, 20% of natural hydraulic lime, and 1% of auxiliary agent.

[0035] The aggregate is quartz sand; the particle size of the aggregate is between 0.25-1.00mm.

[0036] The natural hydraulic lime is the natural hydraulic lime specified in the European standard EN459-1 2010; the natural hydraulic lime is NHL5 produced by the French company St Astier.

[0037] The auxiliary agent includes cellulose ether and wood fiber, and the weight percent content of cellulose ether and wood fiber in the water-permeable grouting agent composition is respectively: 0.5% of cellulose ether, 0.5% of wood fiber; The ether is cellulose ether M4025 from Hercules Temple Company; the wood fiber is wood fiber ARBOCEL FD40 from JRS Company of Germany.

[0038] In this embodiment, the preparation method of the permeable pointing agent composition, the steps are as follow...

Embodiment 3

[0045] A water-permeable pointing agent composition, which is composed of the following components by weight percentage: 70% of aggregate, 28.5% of natural hydraulic lime, and 1.5% of auxiliary agent.

[0046] The aggregate is formed by mixing limestone and quartz sand at a weight ratio of 1:1; the particle size of the aggregate is between 0.25-1.00 mm.

[0047] The natural hydraulic lime is the natural hydraulic lime specified in the European standard EN459-1 2010; the natural hydraulic lime is NHL5 produced by the French company St Astier.

[0048] The auxiliary agent includes cellulose ether and wood fiber, and the weight percent content of cellulose ether and wood fiber in the water-permeable grouting agent composition is respectively: 0.6% of cellulose ether, 0.9% of wood fiber; The ether is cellulose ether M4025 from Hercules Temple Company; the wood fiber is wood fiber ARBOCEL FD40 from JRS Company of Germany.

[0049] In this embodiment, the preparation method of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
heightaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a permeable pointing agent composition which consists of the following components in percentage by weight: 60-79 percent of aggregate, 20-39 percent of natural water hard limeand 1-2 percent of an auxiliary. The invention further discloses a preparation method of the permeable pointing agent composition. The permeable pointing agent composition prepared through the preparation method disclosed by the invention has good water permeability and can effectively drain moisture in brick and stone heritage buildings in a wet area and avoid the influence on the stability of astructural body as a wall body or a rock mass is in a damp state for a long time; moreover, as the surfaces of the buildings are no longer damp, the appearance of many bryophytes on the surfaces of the buildings is also avoided, therefore, the attractive appearances of the surfaces of the buildings are ensured.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a water-permeable pointing agent composition and a preparation method thereof. Background technique [0002] Pointing materials are also called caulking agents and grouting agents, which are mainly used for caulking between tiles, tiles, marble, granite and other bricks. The existing pointing materials have poor water permeability and cannot effectively drain the moisture in the masonry cultural relics buildings in humid areas, causing the wall or rock mass to be in a wet state for a long time, affecting the stability of the structure. At the same time, the existence of a large amount of water gives Vegetation provides good growth conditions, resulting in many bryophytes appearing on the surface of the building, which affects the appearance. Contents of the invention [0003] The object of the present invention is to provide a water-permeable pointing agent composit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/12
CPCC04B28/12C04B2111/00284C04B2111/00672C04B2201/50C04B14/28C04B16/02C04B24/383C04B14/06
Inventor 张德兵
Owner 浙江德赛堡建筑材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com