Jun porcelain and preparation method thereof

A production method, the technology of Jun porcelain, applied to clay products, other household utensils, household utensils, etc., can solve the problems of uneven glazing and difficult quality control, so as to achieve vivid and colorful glazed surface, stable and controllable glazing quality, Pure glaze effect

Active Publication Date: 2018-03-30
XUCHANG UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the traditional production method of Jun porcelain, 70% of the products will be scrapped during the firing process, and the treasures among them are even rarer, and most of the glazing methods need to be completed manually, the quality is not easy to control, and the glazing is uneven

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A method for making Jun porcelain, comprising:

[0029] Step 1. Bake the qualified plain tires that have been cleaned of dust at 35-40°C for 3 hours;

[0030] Step 2. Immediately immerse the baked plain tire in the glaze slurry for glazing;

[0031] Step 3, put the glazed plain tire into the kiln for glaze firing, wherein, the glaze firing includes:

[0032] Pre-firing: Put the plain tire into the kiln, keep the kiln door open 2-3cm, then ignite and fire, so that the temperature in the furnace will rise from room temperature to 590-600°C evenly within 2 hours, and then close the kiln door tightly ;

[0033] Firing in an oxidizing atmosphere: the temperature in the furnace is evenly raised from 590-600°C to 1000-1050°C within 4 hours, and fresh air is supplied to the kiln to ensure sufficient oxygen in the kiln;

[0034] Firing in reducing atmosphere: Make the temperature in the furnace rise uniformly from 1000-1050°C to 1400-1500°C within 8 hours, and stop supplying ...

Embodiment 2

[0043] A method for making Jun porcelain, comprising:

[0044] Step 1. Bake the qualified plain tire at 35-40°C for 3.5 hours after dust removal;

[0045] Step 2. Immediately immerse the baked plain tire in the glaze slurry for glazing;

[0046] Step 3, put the glazed plain tire into the kiln for glaze firing, wherein, the glaze firing includes:

[0047] Pre-firing: Put the plain tire into the kiln, keep the kiln door open 2-3cm, then ignite and fire, so that the temperature in the furnace will rise from room temperature to 590-600°C evenly within 2 hours, and then close the kiln door tightly ;

[0048] Firing in an oxidizing atmosphere: the temperature in the furnace is raised uniformly from 590-600°C to 1000-1050°C within 4 hours, and fresh air is supplied to the kiln to ensure sufficient oxygen in the kiln;

[0049] Firing in a reducing atmosphere: Increase the temperature in the furnace from 1000-1050°C to 1400-1500°C evenly within 8 hours, and stop supplying fresh air to...

Embodiment 3

[0058] A method for making Jun porcelain, comprising:

[0059] Step 1. Bake the qualified plain tires that have been cleaned of dust at 35-40°C for 4 hours;

[0060] Step 2. Immediately immerse the baked plain tire in the glaze slurry for glazing;

[0061] Step 3, put the glazed plain tire into the kiln for glaze firing, wherein, the glaze firing includes:

[0062] Pre-firing: Put the plain tire into the kiln, keep the kiln door open 2-3cm, then ignite and fire, so that the temperature in the furnace will rise from room temperature to 590-600°C evenly within 2 hours, and then close the kiln door tightly ;

[0063] Firing in an oxidizing atmosphere: the temperature in the furnace is evenly raised from 590-600°C to 1000-1050°C within 4 hours, and fresh air is supplied to the kiln to ensure sufficient oxygen in the kiln;

[0064] Firing in reducing atmosphere: Make the temperature in the furnace rise uniformly from 1000-1050°C to 1400-1500°C within 8 hours, and stop supplying ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a manufacturing method for jun porcelain. The method comprises the following steps: step 1, putting a qualified blank body subjected to ash removal treatment into a baking ovenat a temperature of 35-40 DEG C for baking for 3-4 hours; step 2, carrying out glazing; step 3, carrying out glaze firing, wherein the glaze firing comprises pre-firing, firing in an oxidizing atmosphere, and firing in a reducing atmosphere. The temperature in the furnace is increased at a constant speed from 1000-1050 DEGC to 1400-1500 DEG C; then fresh air is stopped from being conveyed into akiln; and nitrogen is conveyed into the kiln, wherein in 0-3 hours, the conveying amount of the nitrogen is 0.002-0.003 m<3> / s, in 3-7 hours, the conveying amount of the nitrogen is 0.0005-0.001 m<3> / s, and in 7-9 hours, the conveying amount of the nitrogen is 0.003-0.004 m<3> / s. The invention also discloses jun porcelain manufactured by the manufacturing method for jun porcelain. The preparationmethod provided by the invention has the advantage of low rejection rate, high precious product rate, simple operation and the like.

Description

technical field [0001] The invention relates to the field of porcelain production. More specifically, the present invention relates to a Jun porcelain and its manufacturing method. Background technique [0002] Jun Porcelain is the first of my country's "Five Famous Porcelains". It is famous all over the world for its unique kiln transformation art. In the traditional production method of Jun porcelain, 70% of the products will be scrapped during the firing process, and the treasures among them are even rarer, and most of the glazing methods need to be completed manually, the quality is not easy to control, and the glazing is uneven. Contents of the invention [0003] It is an object of the present invention to solve at least the above-mentioned problems and to provide at least the advantages which will be described later. [0004] Another object of the present invention is to provide a Jun porcelain production method with low rejection rate, high treasure rate and simpl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/24C03C8/00C04B33/34C04B41/86
CPCC03C8/00C04B33/24C04B33/34C04B41/5022C04B41/86C04B2235/658C04B2235/6583
Inventor 王菲张晓珂史澎涛黄杨龚理
Owner XUCHANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap