Artificial quartzite plate and preparation method thereof

A technology of artificial quartz stone and plate, which is applied in the field of building material preparation, can solve the problems of physical and chemical performance decline, easy fading, easy breakage, etc., and achieve low manufacturing cost, good physical and chemical properties, and strong fracture resistance Effect

Inactive Publication Date: 2018-04-06
GUILIN AONISITE ENERGY SAVING & ENVIRONMENT PROTECTION TECH
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the artificial quartz stone produced by the prior art often has problems such as easy deformation, easy breakage, easy fading, and decline in physical and chemical properties, which limit its wider application and need to be solved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Artificial quartzite plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The artificial quartz stone plate of this embodiment is composed of the following raw materials: 20kg of 10-20 mesh quartz sand, 20kg of 20-40 mesh quartz sand, 10kg of 40-60 mesh quartz sand, 10kg of cullet, 4kg of unsaturated resin, fiber 15kg, styrene 1kg, medical stone powder 12kg, pigment 4kg, silane coupling agent 3kg and tert-butyl peroxy-2-ethylhexanoate 1kg.

[0024] The manufacturing method of the above-mentioned artificial quartz stone plate comprises the following process steps:

[0025] (1) Weigh the following raw materials: 20kg of 10-20 mesh quartz sand, 20kg of 20-40 mesh quartz sand, 10kg of 40-60 mesh quartz sand, 10kg of cullet, 4kg of unsaturated resin, 15kg of fiber, 1kg of styrene, 12kg of medical stone powder, 4kg of pigment, 3kg of silane coupling agent and 1kg of tert-butyl peroxy-2-ethylhexanoate, mix and stir evenly;

[0026] (2) Place the mixed raw materials in the mould;

[0027] (3) The mold is sent into the vacuum vibration forming press...

Embodiment 2

[0031] The artificial quartz stone plate of this embodiment is composed of the following raw materials: 30kg of 10-20 mesh quartz sand, 15kg of 20-40 mesh quartz sand, 15kg of 40-60 mesh quartz sand, 8kg of cullet, 8kg of phenolic resin, and 10kg of carbon fiber , 2 kg of styrene, 8 kg of medical stone powder, 7 kg of iron yellow powder, 2 kg of γ-(2,3-epoxypropoxy)propyltrimethoxysilane and 2 kg of tert-butyl peroxybenzoate.

[0032] The manufacturing method of the above-mentioned artificial quartz stone plate comprises the following process steps:

[0033] (1) Weigh the following raw materials: 30kg of 10-20 mesh quartz sand, 15kg of 20-40 mesh quartz sand, 15kg of 40-60 mesh quartz sand, 8kg of cullet, 8kg of phenolic resin, 10kg of carbon fiber, 2kg of styrene, wheat Rice stone powder 8kg, iron yellow powder 7kg, γ-(2,3-epoxypropoxy)propyltrimethoxysilane 2kg and tert-butyl peroxybenzoate 2kg, mix and stir evenly;

[0034] (2) Place the mixed raw materials in the mould; ...

Embodiment 3

[0039] The artificial quartz stone plate of this embodiment is composed of the following raw materials: 40kg of 10-20 mesh quartz sand, 10kg of 20-40 mesh quartz sand, 20kg of 40-60 mesh quartz sand, 5kg of cullet, 12kg of acrylic resin, basalt fiber 5kg, styrene 3kg, medical stone powder 4kg, iron red powder 10kg, N-(β-aminoethyl)-γ-aminopropyltriethoxysilane 1kg and benzoyl peroxide 3kg.

[0040] The manufacturing method of the above-mentioned artificial quartz stone plate comprises the following process steps:

[0041] (1) Weigh the following raw materials: 40kg of 10-20 mesh quartz sand, 10kg of 20-40 mesh quartz sand, 20kg of 40-60 mesh quartz sand, 5kg of cullet, 12kg of acrylic resin, 5kg of basalt fiber, 3kg of styrene, Medical stone powder 4kg, iron red powder 10kg, N-(β-aminoethyl)-γ-aminopropyltriethoxysilane 1kg and benzoyl peroxide 3kg, mix and stir evenly;

[0042] (2) Place the mixed raw materials in the mould;

[0043] (3) The mold is sent into the vacuum vib...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an artificial quartzite plate and a preparation method thereof, and belongs to the technical field of building material preparation. The artificial quartzite plate is composedof the following raw materials in parts by weight: 20-40 parts of 10-20-mesh quartz sand, 10-20 parts of 20-40-mesh quartz sand, 10-20 parts of 40-60-mesh quartz sand, 5-10 parts of cullet, 4-12 partsof unsaturated resin, 5-15 parts of fibers, 1-3 parts of styrene, 4-12 parts of maifan stone powder, 4-10 parts of a pigment, 1-3 parts of a silane coupling agent and 1-3 parts of a curing agent. Theinvention also discloses the preparation method of the above artificial quartzite plate. The artificial quartzite plate disclosed by the invention has stronger breaking and cracking strength, compressive strength and bending strength, the preparation method is simple and environmentally friendly, and the artificial quartzite plate has low costs and is suitable for industrialized production.

Description

technical field [0001] The invention belongs to the technical field of building material preparation, in particular to an artificial quartz stone plate and a manufacturing method thereof. Background technique [0002] Artificial quartz stone is a synthetic stone manufactured by artificial methods. It uses siliceous stone grains and stone powder as raw materials, and uses less binders and pigments. After aggregate → stirring → mixing → cloth → vacuum → vibration → compression and other processes Complete its thin plate forming, and then process it through heat curing→thickness setting→reverse thickness setting→grinding→slitting, etc. It has strong acid resistance, corrosion resistance, wear resistance, high temperature resistance, impact resistance, compression resistance and penetration resistance. , easy to clean and convenient for construction, it is an ideal substitute for natural stone. However, the artificial quartz stone produced by the prior art often has problems su...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B26/18C04B111/34C04B111/54C04B111/82
CPCC04B26/18C04B2111/00017C04B2111/343C04B2111/542C04B2111/82C04B2201/50C04B24/281C04B24/302C04B24/282C04B14/06C04B14/22C04B14/42C04B24/10C04B14/04C04B24/42C04B24/045C04B2103/54C04B14/386C04B14/46C04B14/4625C04B14/308
Inventor郑波何星基何星存
OwnerGUILIN AONISITE ENERGY SAVING & ENVIRONMENT PROTECTION TECH