Carbon fiber reinforced concrete for rockery and preparation method of carbon fiber reinforced concrete

A technology of reinforced concrete and carbon fiber, which is applied in applications, household utensils, ceramic products, etc., to achieve the effect of reasonable formula, high strength and significant harmful gas

Inactive Publication Date: 2018-05-29
山东昇昀国际贸易有限公司
View PDF16 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the deficiencies of the above-mentioned prior art, starting from the design point of view of the artificial manufacture of rockery, combined with the reduction of smog phenomenon, to provide a scientific and reasonable raw material composition, appropriate proportion, strong and durable, and also has significant degradation air Carbon Fiber Reinforced Concrete Used in Rockery for Environmental Protection of Harmful Gases

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbon fiber reinforced concrete for rockery and preparation method of carbon fiber reinforced concrete

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Prepare a kind of carbon fiber reinforced concrete for rockery, the steps are as follows:

[0036] 1) Weigh 20 parts of fly ash, 8 parts of chopped carbon fiber with a length of 5 mm, 19 parts of silicon oxide, 13 parts of calcium oxide, 12 parts of magnesium oxide, and 60 parts of water according to the required parts by weight. 10 parts of 5mm coal slag, 40 parts of Nichrome slag, 4 parts of graphene oxide, 10 parts of titanium dioxide, 9 parts of adhesive polyvinyl chloride, 2 parts of urea, 0.8 parts of foaming agent sodium dodecylbenzene sulfonate 1.1 parts of foam stabilizer ammonium oxide, 12 parts of sand;

[0037] 2) The graphene oxide, titanium dioxide and water weighed in step 1) are ultrasonically mixed to obtain a graphene oxide mixed solution;

[0038] 3) Add the fly ash, carbon fiber, silicon oxide, calcium oxide, magnesium oxide, coal slag, nichrome slag, sand and step 2) prepared graphene oxide mixed solution into the mixer to stir at a stirring speed ...

Embodiment 2

[0044] Prepare a kind of carbon fiber reinforced concrete for rockery, the steps are as follows:

[0045] 1) Weigh 50 parts of fly ash, 15 parts of chopped carbon fiber with a length of 10 mm, 26 parts of silicon oxide, 18 parts of calcium oxide, 15 parts of magnesium oxide, and 100 parts of water according to the required parts by weight. 30 parts of 5mm coal slag, 60 parts of nickel-chromium iron alloy slag, 10 parts of graphene oxide, 30 parts of titanium dioxide, 15 parts of adhesive polyvinyl chloride, 3 parts of urea, and 1.2 parts of foaming agent sodium dodecylbenzene sulfonate , 1.8 parts of foam stabilizer ammonium oxide, 16 parts of sand;

[0046] 2) The graphene oxide, titanium dioxide and water weighed in step 1) are ultrasonically mixed to obtain a graphene oxide mixed solution;

[0047] 3) Add the fly ash, carbon fiber, silicon oxide, calcium oxide, magnesium oxide, coal slag, nichrome slag, sand and step 2) prepared graphene oxide mixed solution into the mixer...

Embodiment 3

[0053] Prepare a kind of carbon fiber reinforced concrete for rockery, the steps are as follows:

[0054] 1) Weigh 30 parts of fly ash, 10 parts of chopped carbon fiber with a length of 6 mm, 20 parts of silicon oxide, 13 parts of calcium oxide, 13 parts of magnesium oxide, 70 parts of water, and particles with a particle size of less than 5 mm after crushing according to the required parts by weight. 15 parts of coal slag, 45 parts of Nichrome slag, 6 parts of graphene oxide, 15 parts of titanium dioxide, 10 parts of adhesive polyvinyl chloride, 2 parts of urea, 0.9 parts of foaming agent sodium dodecylbenzene sulfonate, stabilizer Foaming agent ammonium oxide 1.3 parts, sand 13 parts;

[0055] 2) The graphene oxide, titanium dioxide and water weighed in step 1) are ultrasonically mixed to obtain a graphene oxide mixed solution;

[0056] 3) Add the fly ash, carbon fiber, silicon oxide, calcium oxide, magnesium oxide, coal slag, nichrome slag, sand and step 2) prepared graphe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to carbon fiber reinforced concrete for rockery and a preparation method of the carbon fiber reinforced concrete. According to the invention, the technical problems of poor toughness, and no possibilities of adsorbing and degrading air pollutants of an artificial rockery in the prior art are solved. The invention provides the carbon fiber reinforced concrete for the rockery;the carbon fiber reinforced concrete is prepared from the following raw materials in parts by weight: 20 to 50 parts of fly ash, 8 to 15 parts of carbon fiber, 19 to 26 parts of silicon oxide, 13 to 18 parts of calcium oxide, 12 to 15 parts of magnesium oxide, 60 to 100 parts of water, 10 to 30 parts of coal slag, 40 to 60 parts of nickel-chromium iron alloy residues, 4 to 10 parts of graphene oxide, 10 to 30 parts of titanium dioxide, 9 to 15 parts of adhesive, 2 to 3 parts of urea, 0.8 to 1.2 parts of foaming agent, 1.1 to 1.8 parts of foam stabilizer and 12 to 16 parts of sand. The invention also provides the preparation method of the carbon fiber reinforced concrete for the rockery. The carbon fiber reinforced concrete disclosed by the invention can be widely applied to the field of production of rockeries.

Description

technical field [0001] The invention relates to the field of rockery manufacturing, in particular to a carbon fiber reinforced concrete used for rockery and a preparation method thereof. Background technique [0002] Rockery is widely used in modern gardens. It is a general term for artificially recreated landscapes. It is for the purpose of landscaping and sightseeing. It uses soil, stone, etc. as materials, and takes natural landscapes as the blueprint. It is artistically refined and exaggerated to form a real mountain It feels like a rocky structure with thousands of gestures. [0003] At present, in modern gardens, natural rocks are generally used as materials for independent or subsidiary landscaping arrangements, which mainly show the individual beauty or partial combination of rocks and do not have a complete mountain-shaped landscape effect. However, mining rocks will cause serious damage to the mountain environment, especially for vegetation, the living environment...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/10C04B28/10C04B14/38C04B14/30
CPCC04B28/10C04B2111/00017C04B2111/00827C04B2111/00956C04B18/08C04B14/386C04B14/06C04B14/304C04B18/144C04B14/024C04B18/10C04B14/305C04B24/2682C04B24/126C04B24/20C04B22/00C04B38/10
Inventor 李正坤李文涛
Owner 山东昇昀国际贸易有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap